Polythiol effect, curable monoalkenyl aromatic-diene and ene composition
Assignee: P T Sub Inc
•
Filing: 1977-08-23
•
Granted: 1979-12-18
•
Expires: 1997-08-23
Abstract
Abstract Curable composition containing (1) at least 20% by weight monoalkenyl aromatic-diene copolymer resin; (2) at least 2% by resin weight of at least one monomer substantially compatible with said resin and having at least one cross-linkable C-C-double bond; (3) 0.1 to 35% by resin weight of polythiol containing at least two-SH groups per molecule; and, (4) a curing agent. The disclosure is directed primarily at printing plate production and the composition contains 0.01 to 10% by resin weight of photoinitiator and the monomer is an addition photopolymerizable polyethylenically unsaturated acrylic or methacrylic acid ester containing two or more acrylate or methacrylate groups per molecule or mixtures thereof. In an alternate form low molecular weight liquid rubber polymer may be included in the compositon. Other materials such as stabilizers may also be present.
Inventors
- 👤 Paul R. Hein
- 👤 Robert A. Irvin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 20:59
CPC Classifications
G; G03; G03F; G03F7/00; G03F7/004; G03F7/027; G03F7/0275; C; C08; C08F; C08F291/00; C08F291/18
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
97 words
The method of forming a printing plate which comprises exposing to actinic radiation projected through an image-bearing transparency selected portions of a radiation curable composition comprising (1) at least about 20% by weight of said composition of monoalkenyl aromatic-diene copolymer resin; (2) at least about 2% by resin weight of at least one monomer substantially compatible with said resin and having at least one photo-cross-linkable C--C-double bond; (3) about 0.1 to about 35% by resin weight of polythiol containing at least two-SH groups per molecule and (4) about 0.01 to about 10% by resin weight of photoinitiator.
Claim 2
Independent Claim
97 words
The method of forming a printing plate which comprises exposing to actinic radiation projected through an image-bearing transparency selected portions of a radiation curable composition comprising (1) at least about 20% by weight of said composition of monoalkenyl aromatic-diene copolymer resin; (2) at least about 2% by resin weight of at least one monomer substantially compatible with said resin and having at least one photo-cross-linkable C--C-double bond; (3) about 0.1 to about 35% by resin weight of polythiol containing at least two-SH groups per molecule and (4) about 0.01 to about 10% by resin weight of photoinitiator.
Claim 3
Dependent Claim
139 words
The method of claim 1 wherein said resin (1) is present in an amount of at least 40% by composition weight and is a block copolymer having the general formula A-B-A with blocks A being monoalkenyl aromatic blocks with may be the same or different and which have an average molecular weight of from 2,000 to 100,000 and a glass transition temperature above 25° C. and having the general formula: ##STR4## wherein X represents hydrogen or an alkyl radical containing 1 or 2 carbon atoms, Y represents hydrogen or an alkyl radical containing from 1 to 4 carbon atoms, and n represents an integer from 1 to 5 and with block B being derived from conjugated diene hydrocarbon having the general formula: ##STR5## wherein each R individually represents hydrogen or an alkyl radical containing 1 to 2 carbon atoms.
Claim 4
Dependent Claim
46 words
The method of claim 2 wherein said monomer (2) is an addition photopolymerizable polyethylenically unsaturated acrylic or methacrylic acid ester containing two or more acrylate or methacrylate groups per molecule or mixtures thereof and is present in an amount of at least 10% by resin weight.
Claim 5
Dependent Claim
39 words
The method of claim 2 wherein said polythiol (3) is chosen from the group consisting of pentaerythritol tetrakis (β-mercaptopropionate) and trimethylolpropane tris (β-mercaptopropionate) and mixtures thereof and is present in an amount of 0.5 to 10% by resin weight.
Claim 6
Dependent Claim
50 words
The method of claim 2 wherein from about 0.1 to about 50% by resin weight of a liquid polymer that is a homopolymer of butadiene or a copolymer of at least 30% by weight butadiene with the remainder being either styrene or acrylonitrile is included in said radiation curable composition.
Claim 7
Dependent Claim
72 words
The method of claim 3 wherein said monomer (2) is present in an amount of 15-30% by resin weight, said photoinitiator (4) is chosen from the group consisting of benzophenone and 2,2 dimethoxy 2-phenyl acetophenone and mixtures thereof and is present in an amount of 0.2 to 5%, and said radiation curable composition is applied to a substrate of polyester film in a coating thickness of about 2 to about 200 mils.
Claim 8
Dependent Claim
63 words
The method of claim 1 wherein said resin (1) is present in an amount of at least 40% by composition weight and is a two block copolymer of 30-95% by weight diene-hydrocarbon with 4 to 5 C-atoms and 5 to 70% by weight of a monomer of formula ##STR6## whereby R=H or CH 3 , R'=phenyl or C 1 -C 4 alkyl-substituted phenyl.
Claim 9
Dependent Claim
111 words
The method of claim 7 wherein said monomer (2) is an addition photopolymerizable polyethylenically unsaturated acrylic or methacrylic acid ester containing two or more acrylate or methacrylate groups per molecule or mixtures thereof and is present in an amount of at least 10% by resin weight, said polythiol (3) is chosen from the group consisting of pentaerythritol tetrakis (β-mercaptopropionate) and trimethylolpropane tris (β-mercaptopropionate) and mixtures thereof and is present in an amount of 0.5 to 10%, said photoinitiator (4) is chosen from the group consisting of benzophenone and 2,2-dimethoxy 2-phenyl acetophenone, and said radiation curable composition is applied to a substrate of polyester film in a coating thickness of 2-200 mils.
Claim 10
Independent Claim
91 words
The method of forming a coating on a substrate comprising applying to the surface a layer of a composition comprising (1) at least about 20% by weight of said composition of monoalkenyl aromatic-diene copolymer resin; (2) at least about 2% by resin weight of at least one monomer substantially compatible with said resin and having at least one radiation-cross-linkable C--C-double bond; and (3) about 0.1 to 35% by resin weight of polythiol containing at least two-SH groups per molecule; and thereafter exposing the layer to actinic radiation and curing said composition.
Claim 11
Independent Claim
91 words
The method of forming a coating on a substrate comprising applying to the surface a layer of a composition comprising (1) at least about 20% by weight of said composition of monoalkenyl aromatic-diene copolymer resin; (2) at least about 2% by resin weight of at least one monomer substantially compatible with said resin and having at least one radiation-cross-linkable C--C-double bond; and (3) about 0.1 to 35% by resin weight of polythiol containing at least two-SH groups per molecule; and thereafter exposing the layer to actinic radiation and curing said composition.
Claim 12
Dependent Claim
139 words
The method of claim 9 wherein said resin (1) is present in an amount of at least 40% by composition weight and is a block copolymer having the general formula A-B-A with blocks A being monoalkenyl aromatic blocks which may be the same or different and which have an average molecular weight of from 2,000 to 100,000 and a glass transition temperature above 25° C. and having the general formula: ##STR7## wherein X represents hydrogen or an alkyl radical containing 1 or 2 carbon atoms, Y represents hydrogen or an alkyl radical containing from 1 to 4 carbon atoms, and n represents an integer from 1 to 5; and with block B being derived from conjugated diene hydrocarbon having the general formula: ##STR8## wherein each R individually represent hydrogen or an alkyl radical containing 1 or 2 carbon atoms.
Claim 13
Dependent Claim
80 words
The method of claim 10 wherein said monomer (2) is an addition photopolymerizable polyethylenically unsaturated acrylic or methacrylic acid ester containing two or more acrylate or methacrylate groups per molecule or mixtures thereof and is present in an amount of at least 10% by resin weight and said polythiol (3) is chosen from the group consisting of pentaerythritol tetrakis (β-mercaptopropionate) and trimethylolpropane tris (β-mercaptopropionate) and mixtures thereof and is present in an amount of 0.5 to 10% by resin weight.
Claim 14
Dependent Claim
20 words
The method of claim 10 wherein said composition includes from about 0.01 to about 10% by resin weight of photoinitiator.
Claim 15
Dependent Claim
65 words
The method of claim 9 wherein said resin (1) is present in an amount of at least 40% by composition weight and is a two block copolymer of 30-95% by weight diene-hydrocarbon with 4 to 5 C-atoms and 5 to 70% by weight of a monomer having the general formula ##STR9## whereby R=H or CH 3 and R'=phenyl or C 1 -C 4 alkyl-substituted phenyl.
Claim 16
Dependent Claim
20 words
The method of claim 13 wherein said composition includes from about 0.01 to about 10% by resin weight of photoinitiator.
References Cited (Backward Citations)
CA885388A
Cited
US3149182A
Cited
US3084115A
Cited
US3029223A
Cited
US3051695A
Cited
US3144422A
Cited
US3240844A
Cited
US3338810A
Cited
US3661744A
Cited
US3615450A
Cited
US3627529A
Cited
US4008341A
Cited
US3640923A
Cited
US3950281A
Cited
US3666461A
Cited
GB1312492A
Cited
US3716466A
Cited
US3674486A
Cited
CA926183A
Cited
CA930094A
Cited
GB1350260A
Cited
CA924047A
Cited
GB1379229A
Cited
GB1366769A
Cited
GB1395822A
Cited
US3843502A
Cited
GB1420351A
Cited
US3864229A
Cited
US3783152A
Cited
US3843572A
Cited
US3832421A
Cited
DE2456439A1
Cited
DE2610206A1
Cited
US4045231A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1982-12-17 | 1983-06-18 | 1983-12-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1986-12-17 | 1987-06-18 | 1987-12-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1990-12-17 | 1991-06-18 | 1991-12-18 | $7700.00 | Window Closed / Lapsed |