Purification of gas mixtures

Claim 2

A process for the purification of a hydrogen-containing raw synthesis gas mixture which comprises 10% to 45% by volume of hydrogen on a dry basis, together with carbon oxides, at least 50 ppm hydrogen cyanide and impurities including at least one gas selected from a nitrogen oxide and oxygen and at least one sulphur-containing gas, and which is substantially free of hydrocarbons other than methane, said process comprising passing the gas mixture over a sulphur-resistant hydrogenation catalyst at a temperature of from 120° to 250° C. and at a pressure of from 0.5 to 250 bar to remove at least one gas selected from nitrogen oxides and oxygen therefrom while retaining a hydrogen cyanide content of at least 50 ppm.

Claim 3

A process according to claim 1, wherein the catalyst is a cobalt molybdate catalyst, and wherein the gas mixture is passed over it at a temperature of from 140° to 200° C. and a pressure of up to 5 bar.

Claim 4

A process according to claim 2, wherein the gas mixture has a content, by volume, of about 58% of carbon monoxide, about 12% of carbon dioxide, and about 27% of hydrogen, the remainder being hydrogen cyanide and impurities comprising hydrogen sulphide, carbonoxysulphide, methane, nitrogen oxides and oxygen.

Claim 5

A process as in claim 1 comprising the further steps of removing sulphur-containing gas from the resultant gas mixture; reacting the gas mixture with steam to convert carbon monoxide to hydrogen; removing further impurities therefrom to yield a gas having a hydrogen content of over 95% by volume; and reacting this gas with nitrogen in the presence of an ammonia synthesis catalyst.

Claim 6

A process as in claim 4 comprising the further step of adding nitrogen to the gas having a hydrogen content of over 95% by volume, reacting the resulting mixture in the presence of an ammonia synthesis catalyst and recovering ammonia from the reacted gas.

Claim 7

In a process for producing purified hydrogen by the steps of (a) oxygen-gasification of coal to produce a raw gas containing carbon monoxide, under 45% by volume of hydrogen and impurities including sulphur compounds, at least 50 ppm of hydrogen cyanide and at least one impurity selected from oxygen and nitrogen oxides, but substantially free of unsaturated hydrocarbons; (b) removal of sulphur compounds by washing with cold methanol; (c) catalytic shift conversion of carbon monoxide with steam to produce carbon dioxide and additional hydrogen; (d) removal of carbon dioxide by washing with cold methanol; and (e) removal of residual impurities by washing with liquid nitrogen; the improvement resulting in a decreased tendency to form deposits in step (b), (d) or (e) which comprises removing at least one impurity selected from oxygen and nitrogen oxides from the raw gas by passing that gas at a temperature in the range 120° to 250° C. and a pressure in the range 0.5 to 250 bar before step (b) over a sulphur-resistant hydrogenation catalyst and controlling the conditions so that at least 50 ppm of hydrogen is retained in the gas so treated.

Claim 8

In a process for producing purified hydrogen by the steps of (a) oxygen-gasification of coal to produce a raw gas containing carbon monoxide, under 45% by volume of hydrogen and impurities including sulphur compounds, at least 50 ppm of hydrogen cyanide and at least one impurity selected from oxygen and nitrogen oxides, but substantially free of unsaturated hydrocarbons; (b) removal of sulphur compounds by washing with cold methanol; (c) catalytic shift conversion of carbon monoxide with steam to produce carbon dioxide and additional hydrogen; (d) removal of carbon dioxide by washing with cold methanol; and (e) removal of residual impurities by washing with liquid nitrogen; the improvement resulting in a decreased tendency to form deposits in step (b), (d) or (e) which comprises removing at least one impurity selected from oxygen and nitrogen oxides from the raw gas by passing that gas at a temperature in the range 120° to 250° C. and a pressure in the range 0.5 to 250 bar before step (b) over a sulphur-resistant hydrogenation catalyst and controlling the conditions so that at least 50 ppm of hydrogen is retained in the gas so treated.

Claim 9

A process according to claim 1 in which the catalyst comprises, in oxide and/or sulphide form, at least one transition metal selected from the metals of Groups VI and VIII of the Periodic Table, and an inorganic refractory oxide carrier.

Claim 10

A process as in claim 7 in which the catalyst is cobalt molybdate or nickel molybdate on an alumina carrier.

Claim 11

A process according to claim 1 in which the hydrogen content of the starting gas is in the range 25-35% by volume.

Claim 12

A process according to claim 1 in which the temperature is in the range 140°-155° C.

Claim 13

A process according to claim in which the starting gas is the product of gasifying coal with oxygen at a temperature in the range 1600°-2500° C. and a pressure in the range 0.8 to 1.1 bar.