Aqueous dispersion of olefin resins and continuous process for preparing thereof
Assignee: Mitsubishi Chemical Corp
•
Filing: 1980-06-19
•
Granted: 1982-03-16
•
Expires: 2000-06-19
Abstract
Abstract Aqueous dispersions of olefin resins having a low film-forming temperature can be continuously produced by homogeneously mixing a mixture composed of olefin resin, partially saponified polyvinyl alcohol and water by means of an extruder having a multi-screw, and extruding the resulting dispersion. If partially saponified polyvinyl alcohol in which residual acetic acid groups are blocked is used, the film-forming temperature thereof is effectively lowered.
Inventors
- 👤 Katsuhiro Abe
- 👤 Mitsuo Tsuruoka
- 👤 Shigeki Kiriyama
- 👤 Kazunobu Nakamori
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 18:30
CPC Classifications
C; C08; C08J; C08J3/00; C08J3/02; C08J3/03; C08J3/05; B; B29; B29B; B29B7/00; B29B7/30; B29B7/34; B29B7/38; B29B7/46; B29B7/48; B29B7/482; B29B7/483; B29B7/488; B29B7/489; B29B7/58; B29B7/72; B29B7/726; B29B7/80; B29B7/82; B29B7/826; B29C; B29C48/00; B29C48/03; B29C48/25; B29C48/36; B29C48/50; B29C48/76; C09; C09D; C09D123/00; C09D123/02; C08J2323/00; C08J2323/02
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
107 words
A process for continuously preparing a homogeneous aqueous dispersion of olefin resin which comprises continuously feeding said olefin resin into a hopper of a multi-screw extruder having at least two screws in the compression zone thereof, continuously feeding an aqueous solution of partially saponified polyvinyl alcohol having from about 65 to 95 mol% of the maximum saponification value under pressure to at least one feed inlet provided in at least one of a compression zone and a metering zone of said extruder which are separate from said hopper, wherein said olefin resin is heated and mixed in said extruder and said aqueous solution is subsequently mixed therewith.
Claim 2
Dependent Claim
107 words
A process for continuously preparing a homogeneous aqueous dispersion of olefin resin which comprises continuously feeding said olefin resin into a hopper of a multi-screw extruder having at least two screws in the compression zone thereof, continuously feeding an aqueous solution of partially saponified polyvinyl alcohol having from about 65 to 95 mol% of the maximum saponification value under pressure to at least one feed inlet provided in at least one of a compression zone and a metering zone of said extruder which are separate from said hopper, wherein said olefin resin is heated and mixed in said extruder and said aqueous solution is subsequently mixed therewith.
Claim 3
Dependent Claim
15 words
A process according to claim 1, wherein said multiscrew extruder is a twin screw extruder.
Claim 4
Dependent Claim
39 words
A process according to claim 1, wherein the aqueous solution of partially saponified polyvinyl alcohol is fed to a highly kneading part of the compression zone at a pressure of at least 20 kg/cm 2 of the resin pressure.
Claim 5
Dependent Claim
49 words
A process according to claim 1, 2 or 3, wherein the partially saponified polyvinyl alcohol has from 70 to 90 mol% of the maximum saponification value, and the melting point (Tm, in °C.) of said partially saponified polyvinyl alcohol satisfies the formula 0.50x+179≧Tm≧1.18x+73 when the saponification value is x%.
Claim 6
Dependent Claim
167 words
An aqueous dispersion of olefin resin comprising (A) ethylene-vinyl acetate copolymer resin particles having an average particle size of 5 microns or less, (B) partially saponified polyvinyl alcohol and (C) water, wherein component (B) is mixed in an amount of from 2 to 35 parts by weight and component (C) is mixed in an amount of from 30 to 1000 parts by weight, based on 100 parts by weight of the resin particles of component (A), and wherein resin A satisfies the following requirements (a), (b) and (c): (a) the melt flow ratio of the resin of the component (A) measured by ASTM D-1238 is 30 g/10 minutes, or more, (b) the vinyl acetate content in the resin of the component (A) from 15 to 40% by weight, and (c) the saponification value, x%, of the partially saponified polyvinyl alcohol of the component (B) is from 70 to 90 mol% and the melting point (Tm, in °C.) of said partially saponified polyvinyl alcohol satisfies the formula 0.50x+179≧Tm≧1.18x+73.
Claim 7
Dependent Claim
167 words
An aqueous dispersion of olefin resin comprising (A) ethylene-vinyl acetate copolymer resin particles having an average particle size of 5 microns or less, (B) partially saponified polyvinyl alcohol and (C) water, wherein component (B) is mixed in an amount of from 2 to 35 parts by weight and component (C) is mixed in an amount of from 30 to 1000 parts by weight, based on 100 parts by weight of the resin particles of component (A), and wherein resin A satisfies the following requirements (a), (b) and (c): (a) the melt flow ratio of the resin of the component (A) measured by ASTM D-1238 is 30 g/10 minutes, or more, (b) the vinyl acetate content in the resin of the component (A) from 15 to 40% by weight, and (c) the saponification value, x%, of the partially saponified polyvinyl alcohol of the component (B) is from 70 to 90 mol% and the melting point (Tm, in °C.) of said partially saponified polyvinyl alcohol satisfies the formula 0.50x+179≧Tm≧1.18x+73.
Claim 8
Dependent Claim
74 words
A process for continuously preparing an aqueous dispersion of olefin resin as in claim 1, 2, or 3, wherein the olefin resin is selected from the group consisting of low-density polyethylene, middle-density polyethylene, high-density polyethylene, ethylene-vinyl acetate copolymer, ethylene-acrylic acid copolymer, metal salts of ethylene-acrylic acid copolymer, ethylene-methacrylic acid copolymer, ethylene-arcylic acid ester copolymer, ethylene-methacrylic acid ester copolymer, ethylene-propylene copolymer, atactic polypropylene, isotactic polypropylene, propylene-1-butene copolymer, ethylene-propylene-dicyclopentadiene copolymer, ethylene-propylene-ethylideneorbornane, and mixtures of said copolymers.
Claim 9
Dependent Claim
40 words
A process for continuously preparing an aqueous dispersion of olefinic resin as in claim 1, 2, or 3, wherein the aqueous solution of partially saponified polyvinyl alcohol is fed under pressure to a feed inlet provided in the compression zone.
Claim 10
Dependent Claim
33 words
A process according to claim 1, 2, or 3, wherein the olefin resin is an ethylenic resin having a melt flow ratio of 30 g/10 minutes or more measured according to ASTM D-1238-70.
Claim 11
Dependent Claim
32 words
An aqueous dispersion of olefin resin as in claim 5, wherein the ratio of the amount of olefin resin to the amount of partially saponified polyvinyl alcohol is from 97/3 to 70/30.
Claim 12
Dependent Claim
32 words
An aqueous dispersion of olefin resin as in claim 9, wherein the ratio of the amount of olefin resin to the amount of partially saponified polyvinyl alcohol is from 95/5 to 80/20.
Claim 13
Dependent Claim
26 words
An aqueous dispersion of olefin resin as in claim 5, wherein the component (B) is mixed in an amount from 5 to 15 parts by weight.
Claim 14
Dependent Claim
26 words
An aqueous dispersion of olefin resin as in claim 5, wherein the component (C) is mixed in an amount from 70 to 500 parts by weight.
Claim 15
Dependent Claim
43 words
An aqueous dispersion of olefin resin as in claim 5, 9, 10, 11, Or 12, wherein at least 10% by weight of the resin particles have an average particle size of 1μ or less, based on the total weight of a resin particle.
Claim 16
Dependent Claim
38 words
An aqueous dispersion of olefin resin as in claim 13, wherein at least 50% by weight of the resin particles have an average particle size of 1μ or less, based on the total weight of a resin particle.
Claim 17
Dependent Claim
39 words
The process of claim 1 wherein said extruder has an L/D ratio of 15 or more where L is the effective length of a screw of the extruder and D is the effective inner diameter of the extruder barrel.
Claim 18
Dependent Claim
81 words
The process of claim 1 wherein said partially saponified polyvinyl alcohol is present in an amount of from 2 to 35 parts by weight per 100 parts by weight of said olefin resin, and further wherein said olefin resin is an ethylene vinyl acetate copolymer having a melt/flow ratio measured by ASTM D-1238 of 30 g/10 mins. or more and wherein the vinyl acetate content of the ethylene vinyl acetate copolymer is from 15 to 40 percent by weight, balance ethylene.
Claim 19
Dependent Claim
15 words
The process of claim 1 wherein said extruder is a co-rotating, intermeshing twin screw extruder.
Claim 20
Dependent Claim
16 words
The process of claim 1 wherein said extruder is is a counter-rotating, intermeshing twin screw extruder.
Claim 21
Dependent Claim
15 words
The process of claim 1 wherein said extruder is a counter-rotating, non-intermeshing twin screw extruder.
Claim 22
Dependent Claim
41 words
The process of claim 1 wherein substantially no organic solvent is present in said aqueous solution or said olefin resin, whereby no organic solvent removal step is necessary in said continuous processing to form said homogeneous aqueous dispersion of olefin resin.
References Cited (Backward Citations)
US3300460A
Cited
US3356629A
Cited
US3708388A
Cited
US3925289A
Cited
US4001160A
Cited
US4126729A
Cited
US4043961A
Cited
US4201802A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-03-15 | 1985-09-14 | 1986-03-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-03-15 | 1989-09-14 | 1990-03-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-03-15 | 1993-09-14 | 1994-03-16 | $7700.00 | Window Closed / Lapsed |