Synthetic papers and method of making the same
Assignee: Mitsubishi Chemical Corp
•
Filing: 1978-08-14
•
Granted: 1982-03-09
•
Expires: 1998-08-14
Abstract
Abstract A laminated structure forming a synthetic paper made of a base or backing film layer made of a thermoplastic resin in a biaxially oriented state. A paper-like film layer is laminated to the base film layer and comprises a thermoplastic resin having 0.5 to 65% by weight of particles of a fine, inorganic filler dispersed in the resin thereof substantially uniformly. The paper-like film layer is in an uniaxially oriented state and has microvoids dispersed therein formed by stretching the laminated films in a heated state. The microvoids comprise microvoids open to a surface of the paper-like film layer free of the base film layer and include microvoids, open and closed, distributed in the paper-like film layer defining therein a cellular, fibrous structure. The two films are formed from thermoplastic resinous compositions in which the components of each composition are well admixed and particles of a fine filler are uniformly distributed in the thermoplastic resin of the paper-like film layer to obtain, as much as possible, microvoids distributed therein uniformly. After the base film layer is formed, it is stretched in a heated state in a machine for longitudinal direction to orient the film uniaxially. The paper-like layer is laminated under pressure on one surface of the base film layer while in a melted state and the resulting laminated structure is stretched transversely to at least 2.5 times the original transverse dimension of the portion of film being stretched between grippers of a stretching machine. This orients the base film layer biaxially and the paper-like film layer uniaxially. The stretching must be sufficient for the stretching and particles of filler to develop microvoids in the paper-like film layer rendering it a cellular and fibrous structure.
Inventors
- 👤 Masanori Takashi
- 👤 Mitsuo Yoshiyasu
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 22:38
CPC Classifications
B; B29; B29C; B29C43/00; B29C43/22; B29C43/30; B29C43/305; B32; B32B; B32B27/00; B32B27/06; B32B27/08; B32B27/12; B32B27/18; B32B27/20; B32B3/00; B32B3/26; B32B2307/00; B32B2307/40; B32B2307/41; Y; Y10; Y10S; Y10S428/00; Y10S428/91; Y10T; Y10T428/00; Y10T428/24; Y10T428/24355; Y10T428/24372; Y10T428/24413; Y10T428/24421; Y10T428/2443; Y10T428/24802; Y10T428/24934; Y10T428/249921; Y10T428/249953; Y10T428/249962; Y10T428/249964; Y10T428/249978; Y10T428/24998; Y10T428/249981; Y10T428/31
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
254 words
A synthetic opaque paper comprising; a base film layer comprising a thermoplastic resin, said base film layer being in a biaxially oriented state; said base layer comprising a film of a thermoplastic resin having less than 20% by weight of a fine inorganic filler dispersed in said resin; said base layer having microvoids dispersed therein; a paper-like film layer laminated to said base film layer and made of a thermoplastic resin having more than 25% and up to 65% by weight of particles of a fine, inorganic filler substantially uniformly dispersed in the resin thereof; said paper-like film layer being in an uniaxially oriented state and stretched in a range ranging from 2.5 up to 16 times the original transverse dimension thereof and having microvoids dispersed therein, wherein a microvoid proportion in said paper-like layer is from about 10% to about 65%; the microvoids comprising elongated open surface microvoids on a surface of said paper-like film layer and interior microvoids; said surface microvoids constituting open surface ruptures densely distributed throughout said surface, said surface ruptures having a major width in a direction transverse to the direction of transverse stretching of said paper-like layer determined principally by the size of the particulated filler contained in said surface ruptures and the length of said surface ruptures in a direction parallel to the direction of transverse stretching of paper-like layer being a function of the extent of stretching; and the interior microvoids being distributed in said paper-like layer and uniaxially elongated to define a cellular, fibrous structure.
Claim 2
Dependent Claim
254 words
A synthetic opaque paper comprising; a base film layer comprising a thermoplastic resin, said base film layer being in a biaxially oriented state; said base layer comprising a film of a thermoplastic resin having less than 20% by weight of a fine inorganic filler dispersed in said resin; said base layer having microvoids dispersed therein; a paper-like film layer laminated to said base film layer and made of a thermoplastic resin having more than 25% and up to 65% by weight of particles of a fine, inorganic filler substantially uniformly dispersed in the resin thereof; said paper-like film layer being in an uniaxially oriented state and stretched in a range ranging from 2.5 up to 16 times the original transverse dimension thereof and having microvoids dispersed therein, wherein a microvoid proportion in said paper-like layer is from about 10% to about 65%; the microvoids comprising elongated open surface microvoids on a surface of said paper-like film layer and interior microvoids; said surface microvoids constituting open surface ruptures densely distributed throughout said surface, said surface ruptures having a major width in a direction transverse to the direction of transverse stretching of said paper-like layer determined principally by the size of the particulated filler contained in said surface ruptures and the length of said surface ruptures in a direction parallel to the direction of transverse stretching of paper-like layer being a function of the extent of stretching; and the interior microvoids being distributed in said paper-like layer and uniaxially elongated to define a cellular, fibrous structure.
Claim 3
Dependent Claim
21 words
A synthetic opaque paper according to claim 1, in which said surface has a surface smoothness lower than 1120 Bekk seconds.
Claim 4
Dependent Claim
42 words
A synthetic opaque paper according to claim 1, in which said paper-like film layer in an uniaxially oriented state is permanently set in said uniaxially oriented state is a stretched state ranging from 7 up to 16 times the original transverse dimension.
Claim 5
Dependent Claim
49 words
A synthetic opaque paper according to claim 1, in which said inorganic filler comprises fine particles of a member selected from the group consisting of clay, talc, asbestos, gypsum, barium sulfate, calcium carbonate, magnesium carbonate, kieselguhr, titanium oxide, zinc oxide, magnesium oxide, diatomaceous earth, silica, silicates and silicon oxide.
Claim 6
Dependent Claim
76 words
A synthetic opaque paper according to claim 1, in which said resin of either said paper-like film layer and said base film layer comprises a member selected from the group consisting of polyolefin resins constituting homopolymers and copolymers of ethylene, propylene and butene-1, polyamide resins, polyester resin comprising polyethylene terephthalte, polyvinyl resins consisting of homopolymers and copolymers of vinyl chloride polyvinylidene resins such as homopolymers and copolymers of vinylidene chloride, and homopolymers and copolymers of styrene.
Claim 7
Dependent Claim
30 words
A synthetic opaque paper according to claim 5, in which the base film layer and the paper-like film layer each comprise a same resin selected from said group of resins.
Claim 8
Dependent Claim
28 words
A synthetic opaque paper according to claim 5, in which the base film layer and the paper-like film layer comprise different resins selected from said group of resins.
Claim 9
Dependent Claim
28 words
A synthetic opaque paper according to claim 1, in which said resin in said base film layer and said resin in said paper-like film layer each comprises polypropylene.
Claim 10
Dependent Claim
17 words
An article of manufacture made of synthetic opaque paper according to claim 1, and having indicia thereon.
Claim 11
Dependent Claim
265 words
A sythetic opaque paper comprising; a base film layer comprising a thermoplastic resin, said base film layer being in a biaxially oriented state; said base layer comprising a film of a thermoplastic resin having less than 20 percent by weight of a fine inorganic filler dispersed in said resin and having microvoids dispersed therein; two paper-like film layers laminated to said base film layer on opposite sides thereof; each paper-like film layer being made of a thermoplastic resin having more than 25% and up to 65% by weight of particles of a fine, inorganic filler substantially uniformly dispersed in the resin thereof; each said paper-like film layer being in an uniaxially oriented state and stretched in a range ranging from 2.5 up to 16 times the original transverse dimension thereof and having microvoids dispersed therein, wherein a microvoid proportion in each said paper-like layer is formed about 10% to about 65%; the microvoids comprising elongated, open surface microvoids on a surface of each said paper-like film layer and interior microvoids said surface microvoids constituting open surface ruptures densely distributed throughout said surface, said surface ruptures having a major width in a direction transverse to the direction of transverse stretching of said paper-like layer determined principally by the size of the particulated filler contained in said surface ruptures and the length of said surface ruptures in a direction parallel to the direction of transverse stretching of paper-like layer being a function of the extent of stretching; and the interior microvoids being distributed in each said paper-like layer and uniaxially elongated to define a cellular, fibrous structure.
Claim 12
Dependent Claim
265 words
A sythetic opaque paper comprising; a base film layer comprising a thermoplastic resin, said base film layer being in a biaxially oriented state; said base layer comprising a film of a thermoplastic resin having less than 20 percent by weight of a fine inorganic filler dispersed in said resin and having microvoids dispersed therein; two paper-like film layers laminated to said base film layer on opposite sides thereof; each paper-like film layer being made of a thermoplastic resin having more than 25% and up to 65% by weight of particles of a fine, inorganic filler substantially uniformly dispersed in the resin thereof; each said paper-like film layer being in an uniaxially oriented state and stretched in a range ranging from 2.5 up to 16 times the original transverse dimension thereof and having microvoids dispersed therein, wherein a microvoid proportion in each said paper-like layer is formed about 10% to about 65%; the microvoids comprising elongated, open surface microvoids on a surface of each said paper-like film layer and interior microvoids said surface microvoids constituting open surface ruptures densely distributed throughout said surface, said surface ruptures having a major width in a direction transverse to the direction of transverse stretching of said paper-like layer determined principally by the size of the particulated filler contained in said surface ruptures and the length of said surface ruptures in a direction parallel to the direction of transverse stretching of paper-like layer being a function of the extent of stretching; and the interior microvoids being distributed in each said paper-like layer and uniaxially elongated to define a cellular, fibrous structure.
Claim 13
Dependent Claim
33 words
A synthetic opaque paper according to claim 10, in which total percent thickness of said paper-like layers in the laminated structure is greater than 40% of the whole thickness of said synthetic paper.
References Cited (Backward Citations)
CA766728A
Cited
US3154461A
Cited
US3515626A
Cited
US3790435A
Cited
US3783088A
Cited
US3738904A
Cited
US4113908A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-03-08 | 1985-09-07 | 1986-03-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-03-08 | 1989-09-07 | 1990-03-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-03-08 | 1993-09-07 | 1994-03-09 | $7700.00 | Window Closed / Lapsed |