Synthetic paper
Assignee: Eneos Corp
•
Filing: 1975-12-09
•
Granted: 1978-09-12
•
Expires: 1995-12-09
Abstract
Abstract Synthetic paper comprising a film base material formed from a thermoplastic resin and a filler composed of a large number of fibrous filaments and a pigment and uniformly scattered over the base material, the dispersed filaments and pigment having void spaces therearound, so that the resultant synthetic paper as a whole presents a whitish opague texture similar to Japanese paper, with a large amount of white threadlike patterns all over the base material.
Inventors
- 👤 Toshihiko Shinomura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 20:55
CPC Classifications
B; B44; B44D; B44D3/00; B44D3/18; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24058; Y10T428/24124; Y10T428/24744; Y10T428/249921; Y10T428/249924; Y10T428/24994; Y10T428/249942; Y10T428/249947; Y10T428/249953; Y10T428/249978; Y10T428/249979; Y10T428/249986; Y10T428/25; Y10T428/258
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
188 words
Synthetic paper comprising a film base material formed from a thermoplastic resin selected from the group consisting of polyethylene, polypropylene, polystyrene, polyvinyl chloride, copolymers using ethylene, propylene, styrene or vinyl chloride as a base material, and mixtures thereof, a number of threadlike fibrous filaments selected from the class consisting of organic natural and synthetic fibers and having a diameter in the range of from about 1μ to 50μ and a length in the range of from about 1mm to 5cm, said fibrous filaments each having a void space therearound and being present in an amount of about 2 to 80 parts by weight per 100 parts by weight of said base material, and a substantially spherical particulate pigment having a diameter in the range of from about 100A to 50μ, the particles of pigment each having a void space therearound and being present in an amount of about 5 to 40 parts by weight per 100 parts by weight of said base material, therein at least some of the void spaces formed around said pigment connect with at least some of the void spaces around said fibrous filaments.
Claim 2
Dependent Claim
188 words
Synthetic paper comprising a film base material formed from a thermoplastic resin selected from the group consisting of polyethylene, polypropylene, polystyrene, polyvinyl chloride, copolymers using ethylene, propylene, styrene or vinyl chloride as a base material, and mixtures thereof, a number of threadlike fibrous filaments selected from the class consisting of organic natural and synthetic fibers and having a diameter in the range of from about 1μ to 50μ and a length in the range of from about 1mm to 5cm, said fibrous filaments each having a void space therearound and being present in an amount of about 2 to 80 parts by weight per 100 parts by weight of said base material, and a substantially spherical particulate pigment having a diameter in the range of from about 100A to 50μ, the particles of pigment each having a void space therearound and being present in an amount of about 5 to 40 parts by weight per 100 parts by weight of said base material, therein at least some of the void spaces formed around said pigment connect with at least some of the void spaces around said fibrous filaments.
Claim 3
Dependent Claim
35 words
Synthetic paper according to claim 1, wherein said thermoplastic resin is a mixture of 20-90 parts by weight of polypropylene and 80-10 parts by weight of polyethylene with a total of 100 parts by weight.
Claim 4
Dependent Claim
27 words
Synthetic paper according to claim 1, wherein said fibrous filaments are dispersed in the direction parallel to the plane of the surface of said film base material.
Claim 5
Dependent Claim
18 words
Synthetic paper according to claim 3, wherein said fibrous filaments are dispersed in cross relation with one another.
Claim 6
Dependent Claim
34 words
Synthetic paper according to claim 1, wherein said fibrous filaments are selected from the group consisting of polyester fiber, polyamide fiber, polyacrylonitrile fiber, polyvinylalcohol fiber, pulp fiber, cotton fiber, silk fiber, and rayon fiber.
Claim 7
Dependent Claim
38 words
Synthetic paper according to claim 1, wherein the void space around said fibrous filament has a width in the range of from about 100A to 50μ and a length in the range of from about 1mm to 6cm.
Claim 8
Dependent Claim
30 words
Synthetic paper according to claim 1, wherein said pigment is selected from the group consisting of calcium carbonate, magnesium carbonate, titanium dioxide, calcium sulfate, calcium sulfite, clay, and zinc white.
Claim 9
Dependent Claim
27 words
Synthetic paper according to claim 1, wherein said pigment is surrounded by a substantially ovate void space having a width in the range of from about 50A-50μ.
Claim 10
Dependent Claim
29 words
Synthetic paper according to claim 1 wherein at least 5% of the number of void spaces surrounding said pigment are communicating with the void spaces surrounding said fibrous filaments.
References Cited (Backward Citations)
US3551538A
Cited
US3616161A
Cited
US3790435A
Cited
US3741860A
Cited
US3765999A
Cited
US3783088A
Cited
US3741841A
Cited
US3758661A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-09-11 | 1982-03-13 | 1982-09-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-09-11 | 1986-03-13 | 1986-09-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-09-11 | 1990-03-13 | 1990-09-12 | $7700.00 | Window Closed / Lapsed |