Process for increasing laser crystal fluorescence yield by controlled atmosphere processing
Assignee: The AT&T MVPD Group LLC
•
Filing: 1979-03-05
•
Granted: 1982-02-16
•
Expires: 1999-03-05
Abstract
Abstract The specification discloses a process for modifying the environment of active atoms in a selected material by removing impurities from the environment. The material is heated at an elevated temperature in an atmosphere conducive to the formation of atomic oxygen so that the atomic oxygen can react with the atoms and molecules in the environment to remove the impurities in and thus alter selected properties of the material. In a preferred embodiment of the present invention, the lasing efficiency of a neodymium-doped yttrium aluminum garnet crystal is increased by heating the crystal at an elevated temperature in an atmosphere conducive to the formation of atomic oxygen so that the atomic oxygen can react with and remove impurities from the crystal to diminish the color center concentration therein and thus increase the fluorescence yield and lasing efficiency of the crystal.
Inventors
- 👤 Ricardo C. Pastor
- 👤 Donald P. Devor
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 13:13
CPC Classifications
H; H01; H01S; H01S3/00; H01S3/14; H01S3/16; C; C30; C30B; C30B29/00; C30B29/10; C30B29/16; C30B29/22; C30B29/24; C30B29/28; C30B33/00; H01S3/1601; H01S3/1603; H01S3/1611; H01S3/163; H01S3/1631; H01S3/1638; H01S3/164; H01S3/1643; H01S3/1671; H01S3/1673
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
95 words
A process for modifying the environment of active atoms in a selected material by removing selected impurities from said environment, said impurities being selected from the group consisting of water and water-derived impurities and being substitutionally or interstitially incorporated in said material, which comprises heating said material at a predetermined elevated temperature in an atmosphere conducive to the formation of atomic oxygen for a period of time sufficient to enable said atomic oxygen to react with the atoms and molecules in said environment to thereby remove said impurities and alter selected properties of said material.
Claim 2
Dependent Claim
95 words
A process for modifying the environment of active atoms in a selected material by removing selected impurities from said environment, said impurities being selected from the group consisting of water and water-derived impurities and being substitutionally or interstitially incorporated in said material, which comprises heating said material at a predetermined elevated temperature in an atmosphere conducive to the formation of atomic oxygen for a period of time sufficient to enable said atomic oxygen to react with the atoms and molecules in said environment to thereby remove said impurities and alter selected properties of said material.
Claim 3
Dependent Claim
16 words
The process as set forth in claim 1 wherein said selected material is an insulating material.
Claim 4
Dependent Claim
45 words
The process as set forth in claim 1 wherein said heating is performed at 1500° C. or higher in a vapor mixture of oxygen and iodine having mole concentrations in the ratio of 10:1 and which is conducive to the formation of said atomic oxygen.
Claim 5
Dependent Claim
41 words
The process as set forth in claim 1 wherein said heating is performed at 1500° C. or higher in a vapor mixture of predetermined amounts of iodine, oxygen, and deuterium oxide, which is conducive to the formation of said atomic oxygen.
Claim 6
Dependent Claim
39 words
The process as set forth in claim 1 wherein said heating is performed at 1500° C. or higher in a vapor mixture of predetermined amounts of iodine and water, which is conducive to the formation of said atomic oxygen.
Claim 7
Dependent Claim
34 words
The process as set forth in claim 1 wherein said heating is performed at 1500° C. or higher in a vapor of nitrous oxide, which is conducive to the formation of said atomic oxygen.
Claim 8
Dependent Claim
34 words
The process as set forth in claim 1 wherein said heating is performed at 1500° C. or higher in an atmosphere of molecular oxygen, which is conducive to the formation of said atomic oxygen.
Claim 9
Dependent Claim
85 words
A process for increasing the lasing efficiency of a selected oxide laser material by removing selected impurities therein, said impurities being selected from the group consisting of water and water-derived impurities and being substitutionally or interstitially incorporated in said material, which comprises heating said material at a predetermined elevated temperature in an atmosphere conducive to the formation of atomic oxygen for a period of time sufficient to enable said atomic oxygen to react with and remove said impurities and to thereby increase said lasing efficiency.
Claim 10
Dependent Claim
85 words
A process for increasing the lasing efficiency of a selected oxide laser material by removing selected impurities therein, said impurities being selected from the group consisting of water and water-derived impurities and being substitutionally or interstitially incorporated in said material, which comprises heating said material at a predetermined elevated temperature in an atmosphere conducive to the formation of atomic oxygen for a period of time sufficient to enable said atomic oxygen to react with and remove said impurities and to thereby increase said lasing efficiency.
Claim 11
Dependent Claim
112 words
A process for increasing the lasing efficiency of a Nd-doped laser host crystal selected from the group consisting of Y 3 Al 5 O 12 (YAG), YAlO 3 (YALO), Gd 3 Ga 5 O 12 (GGG), YVO 4 , and Y 2 O 3 , by diminishing the color center concentration therein, which comprises heating said crystal at a predetermined elevated temperature in an atmosphere conducive to the formation of atomic oxygen for a period of time sufficient to enable said atomic oxygen to react with and remove selected impurities from said crystal to diminish said color center concentration herein and thereby increase the fluorescence yield and lasing efficiency of said crystal.
Claim 12
Dependent Claim
112 words
A process for increasing the lasing efficiency of a Nd-doped laser host crystal selected from the group consisting of Y 3 Al 5 O 12 (YAG), YAlO 3 (YALO), Gd 3 Ga 5 O 12 (GGG), YVO 4 , and Y 2 O 3 , by diminishing the color center concentration therein, which comprises heating said crystal at a predetermined elevated temperature in an atmosphere conducive to the formation of atomic oxygen for a period of time sufficient to enable said atomic oxygen to react with and remove selected impurities from said crystal to diminish said color center concentration herein and thereby increase the fluorescence yield and lasing efficiency of said crystal.
Claim 13
Dependent Claim
79 words
A process for increasing the lasing efficiency of Nd-doped yttrium aluminum garnet (YAG) crystals which comprises heating said crystals at 1500° C. or higher in a vapor mixture of chosen amounts of oxygen and iodine, which is conducive to the formation of atomic oxygen, for a period of time sufficient to enable said atomic oxygen to react with and remove water-derived impurities from said crystals and thereby increase the 1.06 micrometer fluorescence yield and lasing efficiency of said crystals.
Claim 14
Dependent Claim
79 words
A process for increasing the lasing efficiency of Nd-doped yttrium aluminum garnet (YAG) crystals which comprises heating said crystals at 1500° C. or higher in a vapor mixture of chosen amounts of oxygen and iodine, which is conducive to the formation of atomic oxygen, for a period of time sufficient to enable said atomic oxygen to react with and remove water-derived impurities from said crystals and thereby increase the 1.06 micrometer fluorescence yield and lasing efficiency of said crystals.
Claim 15
Dependent Claim
96 words
A process for increasing the lasing efficiency of a Nd-doped laser host crystal selected from the group consisting of Y 3 Al 5 O 12 (YAG), YAlO 3 (YALO), Gd 3 Ga 5 O 12 (GGG), YVO 4 , and Y 2 O 3 which comprises heating said crystal to a predetermined elevated temperature while exposing said crystal to atomic oxygen for a period of time sufficient to enable said atomic oxygen to react with and remove water-derived impurities from said crystal and thereby increase the 1.06 micrometer fluorescence yield and lasing efficiency of said crystal.
Claim 16
Dependent Claim
96 words
A process for increasing the lasing efficiency of a Nd-doped laser host crystal selected from the group consisting of Y 3 Al 5 O 12 (YAG), YAlO 3 (YALO), Gd 3 Ga 5 O 12 (GGG), YVO 4 , and Y 2 O 3 which comprises heating said crystal to a predetermined elevated temperature while exposing said crystal to atomic oxygen for a period of time sufficient to enable said atomic oxygen to react with and remove water-derived impurities from said crystal and thereby increase the 1.06 micrometer fluorescence yield and lasing efficiency of said crystal.
Claim 17
Dependent Claim
93 words
A Nd-doped laser host crystal selected from the group consisting of Y 3 Al 5 O 12 , YAlO 3 , Gd 3 Ga 5 O 12 , YVO 4 , and Y 2 O 3 having optimized lasing efficiency, formed by heating said crystal at a predetermined elevated temperature in an atmosphere conducive to the formation of atomic oxygen for a period of time sufficient to enable said atomic oxygen to react with and remove selected impurities from said crystal and thereby increase the fluorescence yield and lasing efficiency of said crystal.
Claim 18
Dependent Claim
93 words
A Nd-doped laser host crystal selected from the group consisting of Y 3 Al 5 O 12 , YAlO 3 , Gd 3 Ga 5 O 12 , YVO 4 , and Y 2 O 3 having optimized lasing efficiency, formed by heating said crystal at a predetermined elevated temperature in an atmosphere conducive to the formation of atomic oxygen for a period of time sufficient to enable said atomic oxygen to react with and remove selected impurities from said crystal and thereby increase the fluorescence yield and lasing efficiency of said crystal.
Claim 19
Dependent Claim
93 words
A Nd-doped laser host crystal selected from the group consisting of Y 3 Al 5 O 12 , YAlO 3 , Gd 3 Ga 5 O 12 , YVO 4 , and Y 2 O 3 , having optimized lasing efficiency, formed by heating said crystal to a predetermined elevated temperature while exposing said crystal to atomic oxygen for a period of time sufficient to enable said atomic oxygen to react with and remove water-derived impurities from said crystal and thereby increase the 1.06 micrometer fluorescence yield and lasing efficiency of said crystal.
Claim 20
Dependent Claim
93 words
A Nd-doped laser host crystal selected from the group consisting of Y 3 Al 5 O 12 , YAlO 3 , Gd 3 Ga 5 O 12 , YVO 4 , and Y 2 O 3 , having optimized lasing efficiency, formed by heating said crystal to a predetermined elevated temperature while exposing said crystal to atomic oxygen for a period of time sufficient to enable said atomic oxygen to react with and remove water-derived impurities from said crystal and thereby increase the 1.06 micrometer fluorescence yield and lasing efficiency of said crystal.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-02-15 | 1985-08-17 | 1986-02-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-02-15 | 1989-08-17 | 1990-02-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-02-15 | 1993-08-17 | 1994-02-16 | $7700.00 | Window Closed / Lapsed |