Method of preparing a battery paste containing fibrous polyfluoroethylene for use in the plates of a lead-acid storage battery
Assignee: YERMCO Inc
•
Filing: 1978-01-27
•
Granted: 1982-02-16
•
Expires: 1998-01-27
Abstract
Abstract A method of preparing a battery paste for a lead-acid storage battery comprising: (a) mixing a water dispersion of polyfluoroethylene with lead material, (b) adding an aqueous solution of sulfuric acid to the lead material-dispersion mix and mixing to form a paste having fibrillation developed therein, (c) controlling the amount of fibrillation developed in the paste, and (d) controlling the paste density for use in a battery plate. The method provides an improved paste which permits substantial reduction in plate weights and density and loss of active material in the grid structure due to plate shedding over a conventional lead-acid paste. The saving in active material ranges from 10 to 30% over a conventional lead-acid paste without reduction in battery performance.
Inventors
- 👤 Joseph C. Duddy
- 👤 Francis P. Malaspina
- 👤 William J. Martini
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 22:23
CPC Classifications
H; H01; H01M; H01M4/00; H01M4/02; H01M4/62; H01M4/621; H01M4/36; H01M4/48; H01M4/56; Y; Y02; Y02E; Y02E60/00; Y02E60/10
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
106 words
A method of preparing a battery paste for use in the plates of a lead acid storage battery which comprises the steps of: (a) mixing a water dispersion of polyfluoroethylene with lead material, (b) adding an aqueous solution of sulfuric acid to the lead material-dispersion mix and mixing to form a paste having fibrillation developed therein, (c) controlling the amount of fibrillation developed in the paste by controlling the temperature developed during step (b) within a range from about 20° C. to about 100° C. and the amount of shear imparted to the paste, and (d) controlling the paste density for use in a battery plate.
Claim 2
Independent Claim
106 words
A method of preparing a battery paste for use in the plates of a lead acid storage battery which comprises the steps of: (a) mixing a water dispersion of polyfluoroethylene with lead material, (b) adding an aqueous solution of sulfuric acid to the lead material-dispersion mix and mixing to form a paste having fibrillation developed therein, (c) controlling the amount of fibrillation developed in the paste by controlling the temperature developed during step (b) within a range from about 20° C. to about 100° C. and the amount of shear imparted to the paste, and (d) controlling the paste density for use in a battery plate.
Claim 3
Dependent Claim
21 words
The method of preparing a battery paste according to claim 1 wherein the paste temperature is controlled externally of the paste.
Claim 4
Dependent Claim
31 words
The method of preparing a battery paste according to claim 1 wherein the paste temperature is controlled by controlling the quantity of acid and its rate of addition to the paste.
Claim 5
Dependent Claim
43 words
The method of preparing a battery paste according to claim 1 wherein the amount of shear imparted to the paste is controlled by varying the time of at least one of steps (a) and (b) in relation to the viscosity of the mix.
Claim 6
Dependent Claim
27 words
The method of preparing a battery paste according to claim 1 wherein the temperature is controlled within a range from about 43° C. to about 70° C.
Claim 7
Dependent Claim
78 words
The method of preparing a battery paste according to claim 1 wherein the polyfluoroethylene is polytetrafluoroethylene within the range of from about 1/8% to about 5% by weight of the weight of the leady active material and the water ranges from about 80 cc to about 160 cc per pound of leady active material, and the acid has a specific gravity of 1.400 and ranges from about 30 cc to about 75 cc per pound of lead material.
Claim 8
Dependent Claim
29 words
The method of preparing a battery paste according to claim 1 wherein the total time of mixing in step (a) ranges from about 5 minutes to about 20 minutes.
Claim 9
Dependent Claim
29 words
The method of preparing a battery paste according to claim 1 wherein the total time of mixing in step (b) ranges from about 6 minutes to about 25 minutes.
Claim 10
Dependent Claim
32 words
The method of preparing a battery paste according to claim 1 wherein the addition of the aqueous solution of sulfuric acid during step (b) takes place during approximately 4 to 15 minutes.
Claim 11
Dependent Claim
50 words
A battery paste for use in plates of a lead acid storage battery comprising a mixture of leady active material, fibrous polyfluoroethylene and water, wherein the polyfluoroethylene is within the range of about 1/8% to about 5% by weight of the initial leady active material utilized to make the paste.
Claim 12
Dependent Claim
50 words
A battery paste for use in plates of a lead acid storage battery comprising a mixture of leady active material, fibrous polyfluoroethylene and water, wherein the polyfluoroethylene is within the range of about 1/8% to about 5% by weight of the initial leady active material utilized to make the paste.
Claim 13
Dependent Claim
23 words
A battery plate for a lead acid storage battery, said plate having a paste thereon produced according to the method of claim 1.
References Cited (Backward Citations)
US3419900A
Cited
US3099586A
Cited
US3228796A
Cited
US3184339A
Cited
US3429750A
Cited
US3451856A
Cited
US3385736A
Cited
US3466193A
Cited
US3467612A
Cited
US3630781A
Cited
US3666563A
Cited
US3898099A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-02-15 | 1985-08-17 | 1986-02-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-02-15 | 1989-08-17 | 1990-02-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-02-15 | 1993-08-17 | 1994-02-16 | $7700.00 | Window Closed / Lapsed |