Method of strengthening glass containers and articles so made
Assignee: OI Glass Inc
•
Filing: 1980-10-06
•
Granted: 1982-02-16
•
Expires: 2000-10-06
Abstract
Abstract This invention relates to a method of strengthening glass articles and, more specifically, hollow glass containers such as jars for containing foodstuffs. The invention is directed to a method wherein the hollow glass container is surrounded at its heel and bearing surfaces with a thin continuous frangible coating of a polymeric resin such as an epoxy resin. The resin is cured into a frangible thermoset condition to resist thermal shock breakage; however, any breakage of the container at its coated area will result in disruption of the surrounding coating evidencing such breakage. The coating is extremely thin and continuous, and readily applied, and may be used in combination with a foamed thermoplastic tubular sleeve snugly conforming to the body portion of the container. The conforming sleeve serves as a label and to provide an insulating jacket for handling the container when its contents are heated, such as in a microwave oven. The thin coating serves to increase the thermal shock strength of the container and to prevent its thermal shock breakage, but to evidence same when and if such event should occur.
Inventors
- 👤 Ronald W. Bradley
- 👤 David G. Carl
- 👤 Bernard L. Keating
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 09:21
CPC Classifications
B; B32; B32B; B32B17/00; B32B17/06; B32B17/10; B32B5/00; B32B5/18; B65; B65D; B65D23/00; B65D23/08; B65D23/0807; B65D23/0814; B32B2266/00; B32B2266/02; B32B2266/0214; B32B2266/0221; B32B2266/0228; B32B2266/025; B32B2439/00; B32B2439/70; Y; Y10; Y10S; Y10S215/00; Y10S215/06
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
69 words
The method of increasing the effective strength of a soda-lime glass container for its use in heating contents comprising the step of surrounding the heel and bearing surfaces of said glass container with a thin imperforate frangible coating of a thermoset polymeric resin having a thickness ranging from about 1 to 5 mils said coating making said container thermal shock-resistant and being non-fragment retentive upon breakage of said container.
Claim 2
Independent Claim
69 words
The method of increasing the effective strength of a soda-lime glass container for its use in heating contents comprising the step of surrounding the heel and bearing surfaces of said glass container with a thin imperforate frangible coating of a thermoset polymeric resin having a thickness ranging from about 1 to 5 mils said coating making said container thermal shock-resistant and being non-fragment retentive upon breakage of said container.
Claim 3
Dependent Claim
23 words
The method in accordance with claim 1, including the step of curing the said thin imperforate coating of resin into heat-resistant durable condition.
Claim 4
Dependent Claim
41 words
The method in accordance with claim 1, including the step of covering the major exterior side surfaces of said glass container above said thin imperforate coating with a thermoplastic tubular sleeve adapted to conform snugly to said major exterior side surfaces.
Claim 5
Dependent Claim
16 words
The method in accordance with claim 3, wherein the said thermoplastic tubular sleeve comprises foam polyethylene.
Claim 6
Dependent Claim
16 words
The method in accordance with claim 3, wherein the said thermoplastic tubular sleeve comprises foam polystyrene.
Claim 7
Independent Claim
71 words
The method of increasing the effective thermal shock strength of a soda-lime glass container for its use in heating contents comprising the steps of applying a thin imperforate frangible polymeric coating of epoxy resin in cured thermoset condition to at least the heel and bearing surfaces of said glass container, said coating having a thickness ranging from about 1 to 5 mils and being non-fragment retentive upon breakage of said container.
Claim 8
Independent Claim
71 words
The method of increasing the effective thermal shock strength of a soda-lime glass container for its use in heating contents comprising the steps of applying a thin imperforate frangible polymeric coating of epoxy resin in cured thermoset condition to at least the heel and bearing surfaces of said glass container, said coating having a thickness ranging from about 1 to 5 mils and being non-fragment retentive upon breakage of said container.
Claim 9
Dependent Claim
48 words
The method in accordance with claim 6, including the step of applying a foamed thermoplastic tubular sleeve over the major exterior side surfaces of said glass container above said frangible polymeric coating and heat shrinking said tubular sleeve in place to snugly conform to said exterior said surfaces.
Claim 10
Dependent Claim
26 words
The method in accordance with claim 7, wherein said foamed thermoplastic tubular sleeve comprises a heat-shrinkable biaxially-oriented tube of foam polystyrene having an axially-extending fusion seam.
Claim 11
Dependent Claim
69 words
A thermal shock-resistant soda-lime glass container adapted to heating contents therein comprising a hollow glass container having a wide-mouth and generally-cylindrical sidewalls and a thin imperforate frangible coating of a thermoset polymeric over at least the heel and bearing surfaces of said glass container, said coating having a thickness ranging from about 1 to 5 mils said coating being rupturable and substantially non-fragment retentive upon breakage of said container.
Claim 12
Dependent Claim
69 words
A thermal shock-resistant soda-lime glass container adapted to heating contents therein comprising a hollow glass container having a wide-mouth and generally-cylindrical sidewalls and a thin imperforate frangible coating of a thermoset polymeric over at least the heel and bearing surfaces of said glass container, said coating having a thickness ranging from about 1 to 5 mils said coating being rupturable and substantially non-fragment retentive upon breakage of said container.
Claim 13
Dependent Claim
67 words
A thermal shock-resistant soda-lime glass container adapted to heating contents therein comprising a hollow glass container having a wide-mouth and generally-cylindrical sidewalls and a thin imperforate frangible coating of an epoxy resin over at least the heel and bearing surfaces of said glass container, said coating having a thickness ranging from about 1 to 5 mils said coating being essentially non-fragment retentive upon breakage of said container.
Claim 14
Dependent Claim
67 words
A thermal shock-resistant soda-lime glass container adapted to heating contents therein comprising a hollow glass container having a wide-mouth and generally-cylindrical sidewalls and a thin imperforate frangible coating of an epoxy resin over at least the heel and bearing surfaces of said glass container, said coating having a thickness ranging from about 1 to 5 mils said coating being essentially non-fragment retentive upon breakage of said container.
Claim 15
Dependent Claim
42 words
The thermal shock-resistant soda-lime glass container in accordance with claim 10, wherein the cylindrical sidewalls of said glass container are covered with a snugly-conforming tubular sleeve of foamed heat-shrinkable biaxially-oriented thermoplastic material having a thickness ranging from about 5 to 20 mils.
Claim 16
Dependent Claim
20 words
The thermal shock-resistant soda-lime glass container in accordance with claim 11, wherein said sleeve of foamed thermoplastic material comprises polystyrene.
Claim 17
Dependent Claim
20 words
The thermal shock-resistant soda-lime glass container in accordance with claim 11, wherein said sleeve of foamed thermoplastic material comprises polyethylene.
Claim 18
Dependent Claim
25 words
The thermal shock-resistant soda-lime glass container in accordance with claim 11, wherein said sleeve of foamed thermoplastic material comprises a co-extruded film-foam laminate of polystyrene.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-02-15 | 1985-08-17 | 1986-02-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-02-15 | 1989-08-17 | 1990-02-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-02-15 | 1993-08-17 | 1994-02-16 | $7700.00 | Window Closed / Lapsed |