Process and apparatus for welding tubular bodies

Claim 2

Process for manufacturing a tubular body for a preserved food can, comprising the steps of rolling up a metal sheet of small thickness until the opposite edge portions of the sheet contact to form a tube section and welding said edge portions in edge to edge relation without overlap with a laser beam which insures a resistance to tensile forces equivalent to that of the metal sheet and subjecting the tube section to radial expansion to obtain a tubular body having an increased cross-sectional area and a decreased wall thickness as compared with said tube section.

Claim 3

Process according to claim 1, wherein the cross sectional area of the tubular body is increased by approximately 50% by said expansion.

Claim 4

Process according to claim 1, wherein the thickness of the metal sheet is of from 0.2 to 0.3 mm before expansion.

Claim 5

Process for manufacturing a tubular body for a preserved food can, comprising the steps of rolling up a metal sheet of thickness of from 0.2 to 0.3 mm until the opposite edge portions of the sheet contact to form a tube section and welding said edge portions in edge to edge relation without overlap with a laser beam which insures a resistance to tensile forces equivalent to that of the metal sheet, wherein the rolling and welding steps are carried out by circulating a metal sheet having a length much in excess of the length of an individual food can tubular body into an external guide which rolls up said sheet until its opposite edges are in contact and said edges are pressed against a stationary internal core, said core and said guide being proportioned to define a radial gap of a size selected for preventing overlapping of the edges, and then through a location where the laser beam is focussed for forming said tube section and wherein said tube section is later severed into individual tubular bodies.

Claim 6

Process for manufacturing a tubular body for a preserved food can, comprising the steps of rolling up a metal sheet of thickness of from 0.2 to 0.3 mm until the opposite edge portions of the sheet contact to form a tube section and welding said edge portions in edge to edge relation without overlap with a laser beam which insures a resistance to tensile forces equivalent to that of the metal sheet, wherein the rolling and welding steps are carried out by circulating a metal sheet having a length much in excess of the length of an individual food can tubular body into an external guide which rolls up said sheet until its opposite edges are in contact and said edges are pressed against a stationary internal core, said core and said guide being proportioned to define a radial gap of a size selected for preventing overlapping of the edges, and then through a location where the laser beam is focussed for forming said tube section and wherein said tube section is later severed into individual tubular bodies.

Claim 7

Process according to claim 1, wherein the edges are maintained in contact during welding by claws against which the regions of the sheet close to the edges are retained by vacuum forces, said claws being located to retain the edges in edge to edge relation without exerting substantial edge to edge abutting forces directed transversely to the weld in the circumferential direction of the tube section.

Claim 8

Process according to claim 1, wherein the laser beam is focussed over a width less than 0.05 mm in the thickness of the joint between the edges and the power density is 5000 kW/cm 2 at least.

Claim 9

Process according to claim 1, wherein the edges of the sheet are maintained, during welding, with a vertical offset at most equal to 20% of the thickness of the sheet.

Claim 10

Process according to claim 1, for manufacturing a tubular body for preserved food can, wherein the metal of the sheet is black iron, black iron coated on the inside with a protecting varnish, chrome iron, or iron superficially alloyed with tin.

Claim 11

A welding apparatus comprising: support means provided with a pair of elongated parallel clamping means actuatable for clamping two opposite edge regions of a metal sheet portion formed into a tube section, with corresponding confronting edges of the edge regions situated between the pair of clamping means next to each other and level to each other for forming a rectilinear junction line situated between the pair of clamping means, and for releasing said edge regions, said clamping means being adapted to cooperate with the sheet portion for clamping the latter with clamping forces which are substantially perpendicular to the edge regions without substantially forcing said edges into abutment, said clamping means forming the only means which holds the sheet material portions in edge-to-edge relation forming said junction line, stationary guiding means operatively associated with said support means for guiding the latter along a path parallel to said junction line, laser beam generating means having, with respect to said support means, a location for directing a laser-beam between said clamping means at a point in the path of said junction line to engage the sheet portion at the junction line formed by the edges thereof, and means operatively associated with said support means for moving the latter with respect to said laser-beam generating means in a direction and with a speed causing the sheet portion to be welded progressively along said junction line.

Claim 12

A welding apparatus comprising: support means provided with a pair of elongated parallel clamping means actuatable for clamping two opposite edge regions of a metal sheet portion formed into a tube section, with corresponding confronting edges of the edge regions situated between the pair of clamping means next to each other and level to each other for forming a rectilinear junction line situated between the pair of clamping means, and for releasing said edge regions, said clamping means being adapted to cooperate with the sheet portion for clamping the latter with clamping forces which are substantially perpendicular to the edge regions without substantially forcing said edges into abutment, said clamping means forming the only means which holds the sheet material portions in edge-to-edge relation forming said junction line, stationary guiding means operatively associated with said support means for guiding the latter along a path parallel to said junction line, laser beam generating means having, with respect to said support means, a location for directing a laser-beam between said clamping means at a point in the path of said junction line to engage the sheet portion at the junction line formed by the edges thereof, and means operatively associated with said support means for moving the latter with respect to said laser-beam generating means in a direction and with a speed causing the sheet portion to be welded progressively along said junction line.