Process for the continuous mass polymerization of polyblends
Assignee: Bayer Antwerpen NV
•
Filing: 1980-05-15
•
Granted: 1982-02-09
•
Expires: 2000-05-15
Abstract
Abstract The present invention relates to an improved process for the continuous mass polymerization of solutions comprising alkenyl aromatic monomers having about 1 to 10% by weight of a polybutadiene rubber dissolved therein, the steps comprising, (A) continuously charging said solution to a first reaction zone operating at about 10 to 40% conversion forming a first partially polymerized mixture, (B) continuously charging said first mixture to a second reaction zone operating at about 50-90% conversion forming a second partially polymerized mixture, and finally, (C) separating the residual monomer from said second mixture providing a polyblend of a matrix phase of said monomers having polybutadiene rubber particles grafted with said monomers dispersed therein, the improvement comprising: charging a monomer-polybutadiene solution in step (A) having in addition about 1 to 10% by weight of a diene block copolymer and about 1 to 20% by weight of a polymer of said monomers dissolved in said solution followed by carrying out steps (B) and (C) to provide a polyblend of a polymer of said monomers having dispersed therein rubber particles grafted with said monomers, said rubber particles containing said polybutadiene and diene block copolymer rubbers and forming a gel phase of said rubber particles containing grafted and occluded polymers of said monomers in an amount of about 0.5 to 5 parts per part of total rubber.
Inventors
- 👤 Raymond D. Burk
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 12:01
CPC Classifications
C; C08; C08F; C08F279/00; C08F279/02
Claims Analysis
Total Claims: 24
Claim 1
Independent Claim
255 words
In an improved method for the mass polymerizing of a solution comprising an alkenyl aromatic monomer having a polybutadiene rubber dissolved therein, the steps comprising: A. continuously charging said monomer solution having 1 to 10% by weight of a polybutadiene rubber dissolved therein to a first reaction zone operating at steady state polymerization of about 20 to 45% of said monomers to a first partially polymerized mixture, said mixture being said monomer having polymers of said monomer and polybutadiene rubber particles grafted with said monomer dispersed in said monomers, B. continuously charging said partially polymerized mixture to a second reaction zone operating at a final polymerization of about 50 to 85% of said monomer forming a second partially polymerized mixture, C. continuously separating the residual monomer from said second mixture providing a matrix phase polymer of said monomer having said grafted rubber particles dispersed therein, said improvement comprising: charging a monomer-polybutadiene solution in step (A) having in addition about 1 to 10% by weight of a diene block copolymer and about 1 to 20% by weight of a polymer of said monomer dissolved in said solution followed by carrying out steps (B) and (C) to form a polyblend of said matrix phase polymer having rubber particles grafted with said monomers dispersed therein, said rubber particles containing rubbers consisting of polybutadiene and diene block copolymer, said rubber particles being a gel fraction in said polyblend containing grafted and occluded polymers of said monomers in amount of about 0.5 to 5 parts per part of total rubber.
Claim 2
Dependent Claim
255 words
In an improved method for the mass polymerizing of a solution comprising an alkenyl aromatic monomer having a polybutadiene rubber dissolved therein, the steps comprising: A. continuously charging said monomer solution having 1 to 10% by weight of a polybutadiene rubber dissolved therein to a first reaction zone operating at steady state polymerization of about 20 to 45% of said monomers to a first partially polymerized mixture, said mixture being said monomer having polymers of said monomer and polybutadiene rubber particles grafted with said monomer dispersed in said monomers, B. continuously charging said partially polymerized mixture to a second reaction zone operating at a final polymerization of about 50 to 85% of said monomer forming a second partially polymerized mixture, C. continuously separating the residual monomer from said second mixture providing a matrix phase polymer of said monomer having said grafted rubber particles dispersed therein, said improvement comprising: charging a monomer-polybutadiene solution in step (A) having in addition about 1 to 10% by weight of a diene block copolymer and about 1 to 20% by weight of a polymer of said monomer dissolved in said solution followed by carrying out steps (B) and (C) to form a polyblend of said matrix phase polymer having rubber particles grafted with said monomers dispersed therein, said rubber particles containing rubbers consisting of polybutadiene and diene block copolymer, said rubber particles being a gel fraction in said polyblend containing grafted and occluded polymers of said monomers in amount of about 0.5 to 5 parts per part of total rubber.
Claim 3
Dependent Claim
28 words
A process of claim 1 wherein said alkenyl aromatic monomer is selected from the group consisting of styrene, a-methyl styrene, chlorostyrene, dichlorostyrene, bromostyrene or dibromostyrene and mixtures thereof.
Claim 4
Dependent Claim
33 words
A process of claim 1 wherein said diene rubber is selected from the group consisting of polybutadiene, polyisoprene, poly-2-chlorobutadiene, poly-1-chlorobutadiene, copolymers and block copolymers of butadiene-styrene, butadiene-chloroprene, chloroprene-styrene, chloroprene-isoprene, 2-chlorobutadiene-1-chlorobutadiene and mixtures thereof.
Claim 5
Dependent Claim
11 words
A process of claim 1 wherein said diene rubber is polybutadiene.
Claim 6
Dependent Claim
31 words
A process of claim 4 wherein said polybutadiene rubber has a cis isomer content of about 30 to 98% and a Tg range of from about -50° C. to -105° C.
Claim 7
Dependent Claim
12 words
A process of claim 1 wherein said alkenyl aromatic monomer is styrene.
Claim 8
Dependent Claim
48 words
A process of claim 1, said first reaction zone operating with essentially constant fillage of 10 to 90% of its volume with said solution at a temperature of about 100° to 140° C. under a pressure of about 1 to 150 psig with isothermal and steady state polymerization.
Claim 9
Dependent Claim
72 words
A process of claim 1 wherein said second reaction zone is a staged, isobaric, stirred reaction zone, said partially polymerized solution being polymerized by progressive multistage substantially linear flow polymerization, all said stages operating with agitation and common evaporative vapor phase cooling under isobaric conditions, providing each said stage with steady state polymerization at a controlled temperature of about 130° to 180° C. and a pressure of about 7 to 28 psia.
Claim 10
Dependent Claim
22 words
A process of claim 1 wherein said solution has present about 0.001 to 3.0% by weight of a free radical generating catalyst.
Claim 11
Dependent Claim
38 words
A process of claim 9 wherein said free radical generating catalyst is selected from the group consisting of di-tert-butyl peroxide, tert-butyl peracetate, benzoyl peroxide, lauroyl peroxide, tert-butyl perbenzoate, dicumyl peroxide, tert-butyl peroxide and isopropyl carbonate or mixtures thereof.
Claim 12
Dependent Claim
17 words
A process of claim 1 wherein said solution comprises a solution of a diene rubber in styrene.
Claim 13
Dependent Claim
20 words
A process of claim 1 wherein said solution comprises a solution of a diene rubber dissolved in styrene and acrylonitrile.
Claim 14
Dependent Claim
27 words
A process of claim 12 wherein said styrene and acrylonitrile are present in amounts having a weight ratio of styrene to acrylonitrile of about 90:10 to 50:50.
Claim 15
Dependent Claim
10 words
A process of claim 1 wherein said polymer is polystyrene.
Claim 16
Dependent Claim
19 words
A process of claim 14 wherein said polystyrene has a weight average molecular weight of about 100,000 to 300,000.
Claim 17
Dependent Claim
25 words
A process of claim 1 wherein said polymer is a styrene-acrylonitrile polymer having a weight ratio of styrene to acrylonitrile of about 90:10 to 50:50.
Claim 18
Dependent Claim
20 words
A process of claim 16 wherein said styrene-acrylonitrile polymer has a weight average molecular weight of about 100,000 to 300,000.
Claim 19
Dependent Claim
24 words
A process of claim 1 wherein said matrix phase comprises a matrix polymer selected from the group consisting of a polystyrene and styrene-acrylonitrile polymer.
Claim 20
Dependent Claim
26 words
A process of claim 1 wherein said diene block copolymer has the structure: polybutadiene-polystyrene, having a weight ratio of polybutadiene to polystyrene of 95:5 to 60:40.
Claim 21
Dependent Claim
26 words
A process of claim 1 wherein said diene block copolymer has the structure: polystyrene-polybutadiene-polystyrene, having a weight ratio of polybutadiene to polystyrene of 95:5 to 60:40.
Claim 22
Dependent Claim
150 words
A process for the mass polymerization of monomer-rubber solutions comprising the steps: A. continuously charging monomer having polybutadiene, butadiene-styrene block copolymer and polymer of said monomer dissolved therein to a first reaction zone operating at a steady-state polymerization conversion of about 20-45%, said monomer being styrene or a styrene-acrylonitrile mixture, said polymers being polystyrene or styrene-acrylonitrile copolymers forming a first partially polymerized mixture, B. charging continuously said first mixture to a second polymerization zone operating at a steady-state polymerization conversion of about 50 to 85% forming a second partially polymerized mixture, C. continuously separating residual monomers from said second mixture providing a polyblend with a matrix phase of said monomer having a dispersed mixed rubber phase of said polybutadiene and butadiene-styrene block copolymer, said rubber phase being dispersed as rubber particles having present about 1 to 5 parts of grafted and occluded polymers of said monomer per part of rubber.
Claim 23
Dependent Claim
150 words
A process for the mass polymerization of monomer-rubber solutions comprising the steps: A. continuously charging monomer having polybutadiene, butadiene-styrene block copolymer and polymer of said monomer dissolved therein to a first reaction zone operating at a steady-state polymerization conversion of about 20-45%, said monomer being styrene or a styrene-acrylonitrile mixture, said polymers being polystyrene or styrene-acrylonitrile copolymers forming a first partially polymerized mixture, B. charging continuously said first mixture to a second polymerization zone operating at a steady-state polymerization conversion of about 50 to 85% forming a second partially polymerized mixture, C. continuously separating residual monomers from said second mixture providing a polyblend with a matrix phase of said monomer having a dispersed mixed rubber phase of said polybutadiene and butadiene-styrene block copolymer, said rubber phase being dispersed as rubber particles having present about 1 to 5 parts of grafted and occluded polymers of said monomer per part of rubber.
Claim 24
Dependent Claim
8 words
A product of the process of claim 21.
References Cited (Backward Citations)
US3658946A
Cited
US3907939A
Cited
US3660535A
Cited
US3676527A
Cited
US3903202A
Cited
US4146589A
Cited
US4252911A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-02-08 | 1985-08-10 | 1986-02-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-02-08 | 1989-08-10 | 1990-02-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-02-08 | 1993-08-10 | 1994-02-09 | $7700.00 | Window Closed / Lapsed |