US4314952A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process of preparing sintered urandium dioxide pellets
Assignee: CAMECO AB
•
Filing: 1979-04-23
•
Granted: 1982-02-09
•
Expires: 1999-04-23
Abstract
Abstract Sintered uranium dioxide pellets suitable for power reactor use are described, and a process for their manufacture. This process involves incorporating a small amount of sulphur into the uranium dioxide before sintering, as a consequence large grain sizes are found in the pellets. The increase in grain size results in an improvement in overall efficiency when such pellets are used in a power reactor.
Inventors
- 👤 Tadeusz W. Zawidzki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 22:47
CPC Classifications
C; C01; C01G; C01G43/00; C01G43/01; C01G43/025; G; G21; G21C; G21C3/00; G21C3/42; G21C3/58; G21C3/62; G21C3/623; C01P; C01P2004/00; C01P2004/60; C01P2004/61; C01P2006/00; C01P2006/80; Y; Y02; Y02E; Y02E30/00; Y02E30/30
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
138 words
A process for the preparation of a sintered, high density, large grain size uranium dioxide pellet which comprises the steps of: (i) reacting a uranyl nitrate of formula UO 2 (NO 3 ) 2 .6H 2 O with a sulphur source, at a temperature of from about 300° C. to about 400° C. to provide a sulphur containing uranium trioxide; (ii) reacting the thus-obtained modified uranium trioxide with ammonium nitrate to form an insoluble sulphur-containing ammonium uranate; (iii) neutralizing the thus-formed slurry with ammonium hydroxide to precipitate out as an insoluble ammonium uranate the remaining dissolved uranium; (iv) recovering the thus formed precipitates in a dry state; (v) reducing the dry precipitate to UO 2 , and forming it into "green" pellets; and (vi) sintering the thus obtained pellets in a hydrogen atmosphere and at an elevated temperature.
Claim 2
Dependent Claim
138 words
A process for the preparation of a sintered, high density, large grain size uranium dioxide pellet which comprises the steps of: (i) reacting a uranyl nitrate of formula UO 2 (NO 3 ) 2 .6H 2 O with a sulphur source, at a temperature of from about 300° C. to about 400° C. to provide a sulphur containing uranium trioxide; (ii) reacting the thus-obtained modified uranium trioxide with ammonium nitrate to form an insoluble sulphur-containing ammonium uranate; (iii) neutralizing the thus-formed slurry with ammonium hydroxide to precipitate out as an insoluble ammonium uranate the remaining dissolved uranium; (iv) recovering the thus formed precipitates in a dry state; (v) reducing the dry precipitate to UO 2 , and forming it into "green" pellets; and (vi) sintering the thus obtained pellets in a hydrogen atmosphere and at an elevated temperature.
Claim 3
Dependent Claim
22 words
Process according to claim 1, wherein the green pellets contain more than 200 ppm of a sulphur source, expressed as elemental sulphur.
Claim 4
Dependent Claim
16 words
Process according to claim 1 wherein the sulphur source used in step (i) is sulphuric acid.
Claim 5
Dependent Claim
47 words
Process according to claim 1 wherein an excess of sulphur source is used in step (i) over and above the level required in the "green" pellets obtained in step (v) thereby to compensate for sulphur losses from the sulphur-containing uranium oxides during steps (i) to (v) inclusive.
Claim 6
Dependent Claim
15 words
Process according to claim 1 wherein step (i) is carried out at an elevated temperature.
Claim 7
Dependent Claim
26 words
Process according to claims 1 or 3 wherein the step (i) is carried out at a temperature of from about 300° C. to about 400° C.
Claim 8
Dependent Claim
29 words
Process according to claim 1 wherein in step (vi) the rate at which the green pellets are brought to sintering temperature is adjusted to provide a desired grain size.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-02-08 | 1985-08-10 | 1986-02-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-02-08 | 1989-08-10 | 1990-02-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-02-08 | 1993-08-10 | 1994-02-09 | $7700.00 | Window Closed / Lapsed |