Composition for forming inorganic hardened products and process for producing inorganic hardened products using the same
Assignee: Panasonic Electric Works Co Ltd
•
Filing: 1980-10-14
•
Granted: 1982-01-12
•
Expires: 2000-10-14
Abstract
Abstract A composition for forming inorganic hardened products, which comprises a precursor for forming TSH, gypsum and a cement material selected from the group consisting of Portland cement, blast furnace slag and a mixture thereof, the amount of each ingredient satisfying the following relations by weight: 1/0.2>TSH/Cement material>1/5 1/0.1>Precursor/Gypsum>1/1 wherein TSH is the theoretical amount produced by the reaction of the TSH precursor and gypsum, and a process for producing inorganic hardened products from the composition.
Inventors
- 👤 Tomisaburo Azuma
- 👤 Takeru Murakami
- 👤 Haruyuki Date
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 09:21
CPC Classifications
C; C04; C04B; C04B28/00; C04B28/02; C04B28/06; C04B28/065; C04B7/00
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
85 words
A composition for forming inorganic hardened products, which comprises a precursor for forming calcium aluminate sulfate trihydrate, which precursor is calcium aluminate monosulfate, gypsum and a cement material selected from the group consisting of Portland cement, blast furnace slag and a mixture thereof, the amount of each ingredient satisfying the following relations by weight: 1/0.2>calcium aluminate sulfate trihydrate>1/1.5 1/0.1>Precursor/Gypsum>1/1 wherein the calcium aluminate sulfate trihydrate is present in the theoretical amount produced by the reaction of said precursor of calcium aluminate sulfate trihydrate and gypsum.
Claim 2
Dependent Claim
85 words
A composition for forming inorganic hardened products, which comprises a precursor for forming calcium aluminate sulfate trihydrate, which precursor is calcium aluminate monosulfate, gypsum and a cement material selected from the group consisting of Portland cement, blast furnace slag and a mixture thereof, the amount of each ingredient satisfying the following relations by weight: 1/0.2>calcium aluminate sulfate trihydrate>1/1.5 1/0.1>Precursor/Gypsum>1/1 wherein the calcium aluminate sulfate trihydrate is present in the theoretical amount produced by the reaction of said precursor of calcium aluminate sulfate trihydrate and gypsum.
Claim 3
Dependent Claim
17 words
The composition of claim 1, which includes about 40% by weight or less of a reinforcing fiber.
Claim 4
Dependent Claim
14 words
The composition of claim 1, which includes about 20% by weight or less fillers.
Claim 5
Dependent Claim
23 words
The composition of claim 1, which includes a magnesium compound selected from the group consisting of MgO, Mg(OH) 2 and a mixture thereof.
Claim 6
Dependent Claim
21 words
The composition of claim 4, wherein the amount of said magnesium compound is about 3 to 10% by weight of less.
Claim 7
Dependent Claim
8 words
The composition of claim 1, which includes zeolite.
Claim 8
Dependent Claim
22 words
The composition of claim 1, which includes a chloride selected from the group consisting of NaCl, KCl, MgCl, HCl and mixtures thereof.
Claim 9
Dependent Claim
17 words
The composition of claim 7, wherein the amount of chloride is about 5% by weight or less.
Claim 10
Dependent Claim
12 words
The composition of claim 1, wherein said calcium aluminate monosulfate is activated.
Claim 11
Dependent Claim
89 words
A process for producing inorganic hardened products which comprises shaping a slurry containing a precursor for calcium aluminate sulfate trihydrate, which precursor is calcium aluminate monosulfate, gypsum and a cement material into the desired form and ageing and hardening the formed product to form an inorganic hardened product, characterized in that the ageing and hardening of the product is initiated within about 4-8 hours from shaping and the ageing is carried out at about 80° to 90° C. for about 6 to 48 hours in a high humidity atmosphere.
Claim 12
Dependent Claim
89 words
A process for producing inorganic hardened products which comprises shaping a slurry containing a precursor for calcium aluminate sulfate trihydrate, which precursor is calcium aluminate monosulfate, gypsum and a cement material into the desired form and ageing and hardening the formed product to form an inorganic hardened product, characterized in that the ageing and hardening of the product is initiated within about 4-8 hours from shaping and the ageing is carried out at about 80° to 90° C. for about 6 to 48 hours in a high humidity atmosphere.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-01-11 | 1985-07-13 | 1986-01-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-01-11 | 1989-07-13 | 1990-01-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-01-11 | 1993-07-13 | 1994-01-12 | $7700.00 | Window Closed / Lapsed |