Process for producing flyback transformer
Assignee: Resonac Corp
•
Filing: 1980-07-09
•
Granted: 1982-01-05
•
Expires: 2000-07-09
Abstract
Abstract Flyback transformers having good adhesiveness, crack resistance, arc resistance, without producing corona discharge can be produced by insulation treating flyback transformers with a low-shrinkage resin composition comprising (a) an unsaturated polyester produced by reacting partially esterified dicyclopentadiene carboxylic acid, which has been obtained by reacting dicyclopentadiene or hydroxylated dicyclopentadiene, and maleic acid or anhydride, with one or more polyhydric alcohols, (b) a monomer having a vinyl group and (c) a low-shrinkage agent.
Inventors
- 👤 Mitsuo Obara
- 👤 Akira Kageyama
- 👤 Isao Uchigasaki
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 22:35
CPC Classifications
H; H01; H01F; H01F27/00; H01F27/28; H01F27/32; H01F27/327; C; C08; C08L; C08L67/00; C08L67/06; H01B; H01B3/00; H01B3/18; H01B3/30; H01B3/42; H01B3/421; H01B3/425
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
90 words
A process for producing a flyback transformer which comprises insulatin treating the flyback transformer with a low-shrinkage resin composition comprising: (a) a polyester produced by an addition-condensation reaction of a partially esterified dicyclopentadiene carboxylic acid obtained by reacting one of the following reactant groups (1) to (3) at 150° C. or lower: (1) dicyclopentadiene and maleic acid, (2) dicyclopentadiene, maleic acid and water, or (3) hydroxylated dicyclopentadiene and maleic anhydride, with one or more polyhydric alcohols, (b) a monomer having one or more vinyl groups, and (c) a low-shrinkage agent.
Claim 2
Dependent Claim
90 words
A process for producing a flyback transformer which comprises insulatin treating the flyback transformer with a low-shrinkage resin composition comprising: (a) a polyester produced by an addition-condensation reaction of a partially esterified dicyclopentadiene carboxylic acid obtained by reacting one of the following reactant groups (1) to (3) at 150° C. or lower: (1) dicyclopentadiene and maleic acid, (2) dicyclopentadiene, maleic acid and water, or (3) hydroxylated dicyclopentadiene and maleic anhydride, with one or more polyhydric alcohols, (b) a monomer having one or more vinyl groups, and (c) a low-shrinkage agent.
Claim 3
Dependent Claim
24 words
A process according to claim 1, wherein the monomer b) is styrene, α-methylstyrene, o-methylstyrene, m-methylstryene, p-methylstyrene, dimethylstyrene, ethylstyrene, p-t-butylstyrene, chlorostyrene or a mixture thereof.
Claim 4
Dependent Claim
28 words
A process according to claim 1, wherein the polyhydric alcohol is ethylene glycol, propylene glycol, diethylene glycol, dipropylene glycol, 1,3-butylene glycol, neopentyl glycol, 1,6-hexanediol, or a mixture thereof.
Claim 5
Dependent Claim
21 words
A process according to claim 1, wherein the low-shrinkage agent (c) is a polystyrene, a poly(vinyl acetate) or a saturated polyester.
Claim 6
Dependent Claim
44 words
A process according to claim 1, wherein the low-shrinkage resin composition comprises 50 to 40 parts by weight of the polyester (a), 44 to 54 parts by weight of the monomer (b) and 4 to 10 parts by weight of the low-shrinkage agent (c).
Claim 7
Dependent Claim
31 words
A process according to claim 1 or 5, wherein the low-shrinkage resin composition further contains one or more members selected from curing catalysts, curing accelerators, polymerization inhibitors, fillers, and fire retardants.
Claim 8
Dependent Claim
81 words
A flyback transformer insulation treated with a low-shrinkage resin composition comprising: (a) a polyester produced by an addition-condensation reaction of a partially esterified dicyclopentadiene carboxylic acid obtained by reacting one of the following reactant groups (1) to (3) at 150° C. or lower; (1) dicyclopentadiene and maleic acid, (2) dicyclopentadiene, maleic acid and water, or (3) hydroxylated dicyclopentadiene and maleic anhydride, with one or more polyhydric alcohols, (b) a monomer having one or more vinyl groups, and (c) a low-shrinkage agent.
Claim 9
Dependent Claim
81 words
A flyback transformer insulation treated with a low-shrinkage resin composition comprising: (a) a polyester produced by an addition-condensation reaction of a partially esterified dicyclopentadiene carboxylic acid obtained by reacting one of the following reactant groups (1) to (3) at 150° C. or lower; (1) dicyclopentadiene and maleic acid, (2) dicyclopentadiene, maleic acid and water, or (3) hydroxylated dicyclopentadiene and maleic anhydride, with one or more polyhydric alcohols, (b) a monomer having one or more vinyl groups, and (c) a low-shrinkage agent.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-01-04 | 1985-07-06 | 1986-01-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-01-04 | 1989-07-06 | 1990-01-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-01-04 | 1993-07-06 | 1994-01-05 | $7700.00 | Window Closed / Lapsed |