US4309295A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Grain boundary barrier layer ceramic dielectrics and the method of manufacturing capacitors therefrom
Assignee: US Philips Corp
•
Filing: 1980-02-08
•
Granted: 1982-01-05
•
Expires: 2000-02-08
Abstract
Abstract A major amount of strontium titanate is modified with additions of lanthanide series rare earth aluminates, titanates and transition metal oxides to provide sintered semiconductive ceramics with enhanced temperature and voltage stability. The modified strontium titanate ceramic, having the general formula: (1-x)SrTiO.sub.3 +x(1-y)[(1-z)LnAlO.sub.3 +zLn.sub..66 TiO 3]+xyLnMO 3 , is coated with a fritted electrode material and fired at a temperature below the melting point of the electrode material to cause the frit to diffuse into the ceramic and form insulating boundaries around the ceramic grains. Ceramic capacitors so formed are characterized by their excellent electrical properties, particularly their improved temperature stability as evidenced by extremely low changes in capacitance with temperature.
Inventors
- 👤 Robert T. McSweeney
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 20:05
CPC Classifications
H; H01; H01G; H01G4/00; H01G4/002; H01G4/018; H01G4/06; H01G4/08; H01G4/12; H01G4/1272; H01G4/1281; C; C04; C04B; C04B35/00; C04B35/01; C04B35/46; C04B35/462; C04B35/465; C04B35/47
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
119 words
A grain boundary barrier layer ceramic composition consisting essentially of a major amount of sintered strontium titanate and having the formula: (1-x)SrTiO.sub.3 +x(1-y)((1-z)LnAlO.sub.3 +zLn.sub.0.66 TiO.sub.3)+xyLnMO.sub.3 ; where Ln is selected from the group consisting of Y, La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb and Lu; where M is selected from the group consisting of V, Cr, Mn, Fe, Co, Ni, Cu, Nb, Mo, Ta and W; and, where x=0.02 to 0.06, y=0 to 0.50 and z=0 to 1.00; and, having diffused therein a barrier layer material consisting essentially of Bi 2 O 3 or a mixture of a major amount of Bi 2 O 3 with the balance comprising CdO or PbO.
Claim 2
Dependent Claim
119 words
A grain boundary barrier layer ceramic composition consisting essentially of a major amount of sintered strontium titanate and having the formula: (1-x)SrTiO.sub.3 +x(1-y)((1-z)LnAlO.sub.3 +zLn.sub.0.66 TiO.sub.3)+xyLnMO.sub.3 ; where Ln is selected from the group consisting of Y, La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb and Lu; where M is selected from the group consisting of V, Cr, Mn, Fe, Co, Ni, Cu, Nb, Mo, Ta and W; and, where x=0.02 to 0.06, y=0 to 0.50 and z=0 to 1.00; and, having diffused therein a barrier layer material consisting essentially of Bi 2 O 3 or a mixture of a major amount of Bi 2 O 3 with the balance comprising CdO or PbO.
Claim 3
Dependent Claim
26 words
The composition as defined in claim 1 wherein Ln is selected from the group consisting of Y, La, Ce, Pr, Nd, Sm, Gd, Dy and Ho.
Claim 4
Dependent Claim
22 words
The composition as defined in claim 2 wherein M is selected from the group consisting of Cr, Fe, Co, Ni and Cu.
Claim 5
Dependent Claim
22 words
The composition as defined in claim 3 wherein said barrier layer material comprises from 3% to 15% by weight of said ceramic.
Claim 6
Dependent Claim
55 words
The composition as defined in claim 1 wherein the strontium titanate is modified by substituting for the strontium (Sr) and titanium (Ti), respectively, in the formula SrTiO 3 , minor amounts of elements selected from the groups consisting of calcium (Ca), barium (Ba) and lead (Pb) and zirconium (Zr) and consisting of tin (Sn), respectively.
Claim 7
Dependent Claim
59 words
The composition as defined in claim 5 wherein the substitutions for Sr and Ti are made in accordance with the formula: (Sr.sub.1-a A.sub.a)(Ti.sub.1-b B.sub.b)O.sub.3 ; where A is selected from the group consisting of Ca, Ba and Pb and B is selected from the group consisting of Sr and Sn, and where a=0 to 0.05 and b=0 to 0.05.
Claim 8
Dependent Claim
17 words
The composition as claimed in claim 3 or 4, wherein Ln is lanthanum and M is chromium.
Claim 9
Dependent Claim
18 words
The composition as claimed in claim 7, wherein x is 0.04, y is 0.2, and z is 0.5.
Claim 10
Independent Claim
173 words
The method of manufacturing an intergranular barrier layer ceramic capacitor comprising the steps of: (a) preparing a ceramic composition having the formula (1-x)SrTiO.sub.3 +x(1-y)((1-z)LnAlO.sub.3 +zLn.sub.0.66 TiO.sub.3)+xyLnMO.sub.3 ; where Ln is selected from the group consisting of Y, La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, and Lu; where M is selected from the group consisting of Cr, Mn, Fe, Co, Ni and Cu; and, where x=0.02 to 0.04, y=0 to 0.50 and z=0 to 1.00; (b) sintering said composition at a temperature in the range of from 1380° C. to 1500° C. in a reducing atmosphere; (c) applying a fritted electrode material to said sintered composition, where the frit consists essentially of Bi 2 O 3 or mixtures of Bi 2 O 3 with oxides selected from the group consisting of CdO and PbO; and, (d) firing said electrode material at a temperature in the range of from 850° C. to 950° C. to cause said frit to diffuse into the grain boundaries of said sintered composition.
Claim 11
Independent Claim
173 words
The method of manufacturing an intergranular barrier layer ceramic capacitor comprising the steps of: (a) preparing a ceramic composition having the formula (1-x)SrTiO.sub.3 +x(1-y)((1-z)LnAlO.sub.3 +zLn.sub.0.66 TiO.sub.3)+xyLnMO.sub.3 ; where Ln is selected from the group consisting of Y, La, Ce, Pr, Nd, Pm, Sm, Eu, Gd, Tb, Dy, Ho, Er, Tm, Yb, and Lu; where M is selected from the group consisting of Cr, Mn, Fe, Co, Ni and Cu; and, where x=0.02 to 0.04, y=0 to 0.50 and z=0 to 1.00; (b) sintering said composition at a temperature in the range of from 1380° C. to 1500° C. in a reducing atmosphere; (c) applying a fritted electrode material to said sintered composition, where the frit consists essentially of Bi 2 O 3 or mixtures of Bi 2 O 3 with oxides selected from the group consisting of CdO and PbO; and, (d) firing said electrode material at a temperature in the range of from 850° C. to 950° C. to cause said frit to diffuse into the grain boundaries of said sintered composition.
Claim 12
Dependent Claim
24 words
The method of claim 9 wherein Ln is selected from the group consisting of Y, La, Ce, Pr, Nd, Sm, Gd, Dy and Ho.
Claim 13
Dependent Claim
24 words
The method of claim 10 wherein said ceramic composition is sintered at a temperature in the range of from 1380° C. to 1430° C.
Claim 14
Dependent Claim
24 words
The method of claim 11 wherein said electrode material is fired at a temperature in the range of from 875° C. to 950° C.
Claim 15
Dependent Claim
19 words
The method of claim 12 wherein said frit comprises from 3% to 15% by weight of said ceramic composition.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1985-01-04 | 1985-07-06 | 1986-01-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1989-01-04 | 1989-07-06 | 1990-01-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1993-01-04 | 1993-07-06 | 1994-01-05 | $7700.00 | Window Closed / Lapsed |