Zeolites as smoke suppressants for halogenated polymers

Claim 2

A composition comprising 100 parts by weight of a halogenated polymer and 0.1 to 30 parts by weight of a smoke suppressant selected from the group consisting of completely and partially metal-ion exchanged zeolites, both naturally occurring and synthetic, and mixtures thereof, wherein the exchanged metal is selected from from the group consisting of V, Mo, Mn, Fe, Co, Ni, Cu, Zn, Sb, Bi and mixtures thereof, the zeolite being represented by the general formula: M.sub.2/n O.Al.sub.2 O.sub.3.XSiO.sub.2.YH.sub.2 O where M is a metal, selected from the group consisting of alkali and alkaline earth metals, V, Mo, Mn, Fe, Co, Ni, Cu, Zn, Sb, Bi and mixtures thereof; n is the cation valence; X lies between 0.1 and 20 inclusive Y is the number of moles of water of crystallization and has a value of 0 to 20.

Claim 3

The composition of claim 1 wherein the halogenated polymer is poly(vinyl chloride) or poly(vinylidene chloride).

Claim 4

The composition of claim 1 wherein the halogenated polymer is chlorosulfonated polyethylene or polychloroprene.

Claim 5

The composition of claim 1 wherein said metal is selected from the group consisting of V, Mo, Mn, Fe, Co, Cu, Zn, Bi, and mixtures thereof.

Claim 6

The composition of claim 1 wherein said metal is selected from the group consisting of Mn, Fe, Co, Cu, Zn, and mixtures thereof.

Claim 7

The composition of claim 1 wherein said zeolites are in combination with 0.1-10 parts by weight of CuCO 3 , or with 0.1-10 parts by weight of MoO 3 , or mixtures thereof.

Claim 8

The composition of claim 6 wherein said zeolite is ion-exchanged with a water-soluble salt of iron.

Claim 9

The composition of claim 1 wherein the metal comprises 1-30% of the exchanged zeolite.

Claim 10

The composition of claim 1 wherein a stabilizer is present and the composition includes 6 to 30 parts by weight of said smoke suppressant.

Claim 11

The composition of claim 1 wherein the smoke suppressant is calcined at 200°-700° C. for a period of 1-10 hours.

Claim 12

A process for preparing a low smoke halogenated polymer using 0.1 to 30 parts by weight per 100 parts by weight of polymer of a smoke suppressant selected from the group consisting of completely and partially metal-ion exchanged zeolites, both naturally occurring and synthetic, and mixtures, wherein the exchanged metal is selected from the group consisting of V, Mo, Mn, Fe, Co, Ni, Cu, Zn, Sb, Bi, and mixtures thereof, the zeolite being represented by the general formula: M.sub.2/n O.Al.sub.2 O.sub.3.XSiO.sub.2.YH.sub.2 O where M is a metal, selected from the group consisting of alkali and alkaline earth metals, V, Mo, Mn, Fe, Co, Ni, Cu, Zn, Sb, Bi and mixtures thereof; n is the cation valence; X lies between 0.1 and 10, inclusive; Y is the number of moles of water of crystallization and has a value of 0 to 20 inclusive.

Claim 13

A process for preparing a low smoke halogenated polymer using 0.1 to 30 parts by weight per 100 parts by weight of polymer of a smoke suppressant selected from the group consisting of completely and partially metal-ion exchanged zeolites, both naturally occurring and synthetic, and mixtures, wherein the exchanged metal is selected from the group consisting of V, Mo, Mn, Fe, Co, Ni, Cu, Zn, Sb, Bi, and mixtures thereof, the zeolite being represented by the general formula: M.sub.2/n O.Al.sub.2 O.sub.3.XSiO.sub.2.YH.sub.2 O where M is a metal, selected from the group consisting of alkali and alkaline earth metals, V, Mo, Mn, Fe, Co, Ni, Cu, Zn, Sb, Bi and mixtures thereof; n is the cation valence; X lies between 0.1 and 10, inclusive; Y is the number of moles of water of crystallization and has a value of 0 to 20 inclusive.

Claim 14

The process of claim 11 wherein the halogenated polymer is poly(vinyl chloride).

Claim 15

The process of claim 11 wherein the halogenated polymer is chlorosulfonated polyethylene or polychloroprene.

Claim 16

The process of claim 11 wherein the metal comprises 1-30% of the exchanged zeolite.

Claim 17

The process of claim 11 wherein the smoke suppressant is calcined at 200°-700° C. for a period of 1-10 hours.