Polyurethane urea heat seal adhesive for the preparation of heat sealable padding material
Assignee: Carl Freudenberg KG
•
Filing: 1980-02-08
•
Granted: 1981-12-22
•
Expires: 2000-02-08
Abstract
Abstract The invention disclosed herein relates to a method for bonding the opposing surfaces of textile materials to each other with a heat-seal adhesive. The heat-seal adhesive is a polyurethane urea heat-seal adhesive prepared by first preparing a chain-extended polyurethane from at least one diisocyanate, at least one polydiol, and chain-extenders. The chain-extenders may comprise a mixture of low molecular weight diols comprised of at least one low molecular weight diol having a molecular weight below about 500 and having side chains or ether groups, and at least one unbranched low molecular weight diol having a molecular weight below about 500. The chain-extended polyurethane has a free-isocyanate group content which comprises from about 10 to about 40 mole percent of the isocyanate content of the starting mixture. An emulsifier is added to the chain-extended polyurethane, and the polyurethane and emulsifier mixture is emulsified with water. Diamines or diamine mixtures may be added to the emulsion.
Inventors
- 👤 Gunter Schuhmacher
- 👤 Erich Fahrbach
- 👤 Gerhard Schaut
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 14:53
CPC Classifications
D; D06; D06M; D06M17/00; D06M17/04; D06M17/10; C; C08; C08G; C08G18/00; C08G18/06; C08G18/08; C08G18/0838; C08G18/0842; C08G18/0861; C08G18/0866; C08G18/10; C08G18/12; C08G18/28; C08G18/65; C08G18/66; C08G18/6603; C08G18/6607; C08G18/6633; C08G18/6637; C08G18/664; C09; C09J; C09J175/00; C09J175/04; C09J175/06; C08G2170/00; C08G2170/20; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24843; Y10T428/31504; Y10T428/31551; Y10T428/31554
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
168 words
A printable adhesive paste comprising a polyurethane urea heat-seal adhesive, an emulsifier and a thickener; wherein said polyurethane urea is prepared by: A. preparing a polyurethane by reacting a diisocyanate, a polyester polyol and a mixture of at least three low molecular weight diols, wherein at least one of said diols has alkyl side chains or includes an ether group and wherein at least one of said diols is unbranched, said diols in said mixture having a molecular weight below about 500; said polyurethane having a free isocyanate group content which comprises from about 10 to about 40 mole percent of the isocyanate content of the starting reactants; followed by B. adding an emulsifier to said polyurethane of step A, and adding water at a temperature above about 70° C. to said emulsifier and polyurethane; followed by C. adding water at a temperature of below about 25° C. to said emulsion to provide an oil-in-water emulsion, and treating said emulsion with a chain extending diamine or diamine mixture.
Claim 2
Dependent Claim
168 words
A printable adhesive paste comprising a polyurethane urea heat-seal adhesive, an emulsifier and a thickener; wherein said polyurethane urea is prepared by: A. preparing a polyurethane by reacting a diisocyanate, a polyester polyol and a mixture of at least three low molecular weight diols, wherein at least one of said diols has alkyl side chains or includes an ether group and wherein at least one of said diols is unbranched, said diols in said mixture having a molecular weight below about 500; said polyurethane having a free isocyanate group content which comprises from about 10 to about 40 mole percent of the isocyanate content of the starting reactants; followed by B. adding an emulsifier to said polyurethane of step A, and adding water at a temperature above about 70° C. to said emulsifier and polyurethane; followed by C. adding water at a temperature of below about 25° C. to said emulsion to provide an oil-in-water emulsion, and treating said emulsion with a chain extending diamine or diamine mixture.
Claim 3
Dependent Claim
39 words
The printable adhesive paste according to claim 1 wherein said low molecular weight diols have a molecular weight between about 60 and 500, and said polyester polyol has an average molecular weight of from about 500 to about 5000.
Claim 4
Dependent Claim
34 words
The printable adhesive paste according to claim 2 wherein the mole ratio of said low molecular weight diols having side chains or ether groups, to said unbranched diols is from about 25:75 to 60:40.
Claim 5
Dependent Claim
51 words
The printable adhesive paste according to claim 3 wherein said thickener is selected from the group consisting of polyvinyl pyrrolidone thickeners, and polyurethane based thickeners, wherein said thickener is added to said paste in an amount which comprises up to about 8% by weight of the polyurethane content of said paste.
Claim 6
Dependent Claim
46 words
The printable adhesive paste according to claim 3 wherein said thickener is a polyacrylic acid or polymethacrylate thickener and wherein said thickener is added to said paste in an amount which equals not more than about 5% by weight of the polyurethane content of said paste.
Claim 7
Dependent Claim
68 words
The adhesive paste according to claim 1 wherein said polyurethane is prepared by reacting a solvent-free mixture of said low molecular weight diols, polyester polyol and diisocyanate in the presence of about 5 mole percent of a monofunctional compound based on the isocyanate content of the said mixture, wherein said monofunctional compound is selected from the group consisting of amides, amines, alcohols, ε-caprolactam, dibutyl amine and neopentyl alcohol.
Claim 8
Dependent Claim
13 words
The adhesive paste according to claim 6 wherein said monofunctional compound is ε-caprolactam.
Claim 9
Dependent Claim
25 words
The adhesive paste according to claim 1 wherein said polyester polyol is a polybutylene glycol-ethylene glycol-adipic acid polyester having a molecular weight of about 2,000.
Claim 10
Dependent Claim
21 words
The adhesive paste according to claim 1 wherein said low molecular weight diols comprise 1,4-butane diol, 1,6-hexane diol and neopentyl glycol.
Claim 11
Dependent Claim
51 words
The adhesive paste according to claim 1 wherein said low molecular weight diols comprise 1,4-butane diol, 1,6-hexane diol and neopentyl glycol; said polyester polyol is a polybutylene glycol-ethylene glycol-adipic acid polyester having a molecular weight of about 2000 and a hydroxyl number of about 56, and said diisocyanate is 1,6-hexamethylene diisocyanate.
Claim 12
Dependent Claim
18 words
The adhesive paste according to claim 1 wherein said diamine mixture comprises a mixture of 2,2,4-trimethyl-1,6-hexamethylene-diamine and 1,6-hexamethylene-diamine.
Claim 13
Dependent Claim
42 words
The adhesive paste according to claim 1 wherein said emulsifier is a nonionic ethoxylated castor oil or ethoxylated fatty alcohol and wherein from about 5 to about 15 parts by weight of said emulsifier are added per 100 parts of said polyurethane.
References Cited (Backward Citations)
US2968575A
Cited
US3252848A
Cited
US3401133A
Cited
US3463690A
Cited
US3684639A
Cited
US3655627A
Cited
GB1379633A
Cited
US4116741A
Cited
US4160686A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-12-21 | 1985-06-22 | 1985-12-22 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-12-21 | 1989-06-22 | 1989-12-22 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-12-21 | 1993-06-22 | 1993-12-22 | $7700.00 | Window Closed / Lapsed |