Process for producing acrylamide polymers
Assignee: Diafloc Co Ltd
•
Filing: 1980-06-02
•
Granted: 1981-12-15
•
Expires: 2000-06-02
Abstract
Abstract In the production of a dried acrylamide polymer by polymerizing, in an aqueous medium, acrylamide alone or a monomer mixture comprising 50 mole % or more of acrylamide and at least one monomer copolymerizable therewith with a radical initiator, and then drying the resulting hydrous acrylamide polymer, the allowing of 2-mercaptobenzimidazole to be present in the drying step or a step prior thereto enables the dried acrylamide polymer having a high molecular weight and a good dissolvability in water to be obtained.
Inventors
- 👤 Norimasa Yoshida
- 👤 Yasuo Ogawa
- 👤 Ryoji Handa
- 👤 Jun Hosoda
- 👤 Nobuo Kurashige
- 👤 Akihisa Furuno
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:39
CPC Classifications
C; C08; C08F; C08F20/00; C08F20/02; C08F20/52; C08F20/54; C08F20/56; C08F6/00; C08F6/06; C08F6/12
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
85 words
A process for producing a dried, high molecular weight acrylamide polymer by polymerizing, in an aqueous medium, acrylamide alone or a monomer mixture comprising 50 mole % or more of acrylamide and at least one monomer copolymerizable therewith with a radical initiator, and then drying the resulting hydrous acrylamide polymer, wherein there is present in the drying step or a step prior thereto 2-mercaptobenzimidazole in an amount of 0.001 to 10% by weight based on the weight of the monomer or monomers or the polymer.
Claim 2
Dependent Claim
85 words
A process for producing a dried, high molecular weight acrylamide polymer by polymerizing, in an aqueous medium, acrylamide alone or a monomer mixture comprising 50 mole % or more of acrylamide and at least one monomer copolymerizable therewith with a radical initiator, and then drying the resulting hydrous acrylamide polymer, wherein there is present in the drying step or a step prior thereto 2-mercaptobenzimidazole in an amount of 0.001 to 10% by weight based on the weight of the monomer or monomers or the polymer.
Claim 3
Dependent Claim
58 words
A process according to claim 1, wherein the at least one monomer copolymerizable with the acrylamide is selected from the group consisting of methacrylamide, acrylic acid, methacrylic acid, salts and aminoalkyl esters of acrylic and methacrylic acids, quaternary ammonium salts of the aminoalkyl esters of acrylic and methacrylic acids, ethylenesulfonic acid, acrylamidoalkylsulfonic acids, and salts of acrylamidoalkylsulfonic acids.
Claim 4
Dependent Claim
46 words
A process according to claim 1 wherein at least one monomer is selected from the group consisting of acrylonitrile, styrene and lower alkyl acrylates and methacrylates, said at least one monomer being present in an amount insufficient to impair the water solubility of the polymer produced.
Claim 5
Dependent Claim
21 words
A process according to claim 1 or 2, wherein the monomer concentration in the polymerization is 5 to 70% by weight.
Claim 6
Dependent Claim
21 words
A process according to claim 1 or 2, wherein the monomer concentration in the polymerization is 5 to 30% by weight.
Claim 7
Dependent Claim
30 words
A process according to claim 1, wherein the amount of 2-mercaptobenzimidazole added is 0.01 to 5% by weight based on the weight of the monomer or monomers or the polymer.
Claim 8
Dependent Claim
35 words
A process according to any one of claims 6, 1 or 2, wherein the amount of the polymerization initiator added is 0.0001 to 0.2% by weight based on the weight of the monomer or monomers.
Claim 9
Dependent Claim
22 words
A process according to any one of claims 6, 1 or 2, wherein the polymerization is effected in the presence of 2-mercaptobenzimidazole.
Claim 10
Dependent Claim
31 words
A process according to claim 8, wherein the polymerization is effected with a combination of a redox type initiator with an azo initiator at a temperature of 0° to 100° C.
Claim 11
Dependent Claim
46 words
A process according to claim 9, wherein the redox type initiator is a combination of a persulfate, hydrogen peroxide or an alkyl peroxide with a tertiary amine, polyethylenepolyamine, a sulfite, a ferrous or a ferric salt, and the azo initiator is azobis(2-amidinopropane) dihydrochloride, or 4,4'-azobis(4-cyanovaleric acid).
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-12-14 | 1985-06-15 | 1985-12-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-12-14 | 1989-06-15 | 1989-12-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-12-14 | 1993-06-15 | 1993-12-15 | $7700.00 | Window Closed / Lapsed |