US4305795A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for the manufacture of stampers
Assignee: RCA Licensing Corp
•
Filing: 1981-01-08
•
Granted: 1981-12-15
•
Expires: 2001-01-08
Abstract
Abstract It has been found that metal stampers, and more particularly nickel stampers, can be simultaneously hardened and passivated by cathodically treating the stampers in an aqueous bath of a passivation agent.
Inventors
- 👤 Charles A. Weaver
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 07:19
CPC Classifications
C; C25; C25D; C25D1/00; C25D1/10
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
146 words
The method for hardening and passivating the surface of a metal record stamper which comprises the steps of: (a) immersing the stamper in an aqueous electrolytic bath having dissolved therein a passivation agent selected from the group consisting of sodium dichromate, potassium dichromate, sodium permanganate, potassium permanganate, and mixtures thereof wherein the passivation agent is present in an amount of from about 0.15 to 1.0 gm/l; (b) connecting said stamper in a cathodic position in said bath; (c) applying a current across said bath sufficient to cause the evolution of hydrogen at the cathode position, said electric current being maintained so as to provide a current density at the stamper surface of about 4 to 6.5 amp/dm 2 ; and (d) maintaining said current until the surface of the metal reacts with the evolved hydrogen; whereby the surface of the stamper is simultaneously hardened and passivated.
Claim 2
Independent Claim
146 words
The method for hardening and passivating the surface of a metal record stamper which comprises the steps of: (a) immersing the stamper in an aqueous electrolytic bath having dissolved therein a passivation agent selected from the group consisting of sodium dichromate, potassium dichromate, sodium permanganate, potassium permanganate, and mixtures thereof wherein the passivation agent is present in an amount of from about 0.15 to 1.0 gm/l; (b) connecting said stamper in a cathodic position in said bath; (c) applying a current across said bath sufficient to cause the evolution of hydrogen at the cathode position, said electric current being maintained so as to provide a current density at the stamper surface of about 4 to 6.5 amp/dm 2 ; and (d) maintaining said current until the surface of the metal reacts with the evolved hydrogen; whereby the surface of the stamper is simultaneously hardened and passivated.
Claim 3
Dependent Claim
27 words
The method according to claim 1 wherein the said passivation agent is potassium dichromate and is present in said bath in an amount of about 0.25 gm/l.
Claim 4
Dependent Claim
20 words
The method according to claim 1 wherein said aqueous electrolytic bath further contains an alkali and an alkaline cleaning agent.
Claim 5
Dependent Claim
39 words
The method according to claim 3 wherein the alkali is present in said bath in an amount from about 7.5 to about 38.5 gm/l and is selected from the group consisting of sodium hydroxide, sodium carbonate and potassium hydroxide.
Claim 6
Dependent Claim
43 words
The method according to claim 3 wherein the alkaline cleaning agent is present in said bath in an amount from about 7.5 to about 38.5 gm/l and is selected from the group consisting of trisodium phosphate, tetrasodium pyrophosphate, tetrapotassium pyrophosphate, and mixtures thereof.
Claim 7
Dependent Claim
33 words
The method according to claim 1 wherein the aqueous electrolytic bath is comprised of about 0.25 gm/l of potassium dichromate, about 15 gm/l of potassium hydroxide, and about 15 gm/l of tetrasodium pyrophosphate.
Claim 8
Dependent Claim
21 words
The method according to claim 1 wherein said bath is maintained at a temperature of from about 66° to 77° C.
Claim 9
Dependent Claim
24 words
The method according to claim 1 wherein the current density at the surface of the stamper is maintained at about 5.5 amp/dm 2 .
Claim 10
Dependent Claim
13 words
The method according to claim 1 wherein said stamper is a nickel stamper.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-12-14 | 1985-06-15 | 1985-12-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-12-14 | 1989-06-15 | 1989-12-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-12-14 | 1993-06-15 | 1993-12-15 | $7700.00 | Window Closed / Lapsed |