Method for producing propylene copolymers using a catalyst activated prior to copolymerization

Claim 1

A method for producing a crystalline copolymer consisting of 0.5-3% by weight of ethylene, 85-97% by weight of propylene and 2-11% by weight of another α-olefin having 4-12 carbon atoms, which comprises: (a) preparing a catalyst solution by mixing together (i) a titanium trichloride composition obtained by mixing and milling (1) a titanium trichloride obtained by reducing TiCl 4 by metallic aluminum or by further milling the resulting reduction product, together with (2) a reaction product of a mixture of titanium tetrachloride with an ether, in a mixing ratio of said titanium trichloride (1) to said reaction product (2) of 1:0.001 to 0.3, (ii) a dialkylaluminum halide, (iii) an electron donor compound, and (iv) an inert solvent, (b) feeding propylene into the resulting catalyst solution at a temperature of 10°-50° C. (i) at a feeding rate in a ratio by weight of 0.02-1/said titanium trichloride composition/hr. (ii) in a feeding amount in a ratio by weight of 0.5-5/said titanium trichloride composition, and (iii) under a pressure of atmospheric pressure to 10 atmospheres, to obtain an activated catalyst solution containing polypropylene in an amount of 0.5-5 times the weight of the titanium trichloride composition contained in said catalyst solution, in advance of the subsequent copolymerization, and (c) feeding into a polymerization zone containing said activated catalyst solution, (1) 100 parts by weight of propylene, (2) 2 to 13 parts by weight of an α-olefin having 4 to 12 carbon atoms, and (3) 1 to 5 parts by weight of ethylene, said propylene and said α-olefin having 4-12 carbon atoms being fed into the catalyst solution at the same time and continuously, said ethylene being fed into the gas phase part of the polymerization zone intermittently at time intervals of 5 to 60 minutes, the once feeding time being 1 to 5 minutes, and the polymerization condition being under a temperature of 50° to 75° C. and a pressure of 5 to 40 kg/cm 2 .

Claim 2

A method for producing a crystalline copolymer consisting of 0.5-3% by weight of ethylene, 85-97% by weight of propylene and 2-11% by weight of another α-olefin having 4-12 carbon atoms, which comprises: (a) preparing a catalyst solution by mixing together (i) a titanium trichloride composition obtained by mixing and milling (1) a titanium trichloride obtained by reducing TiCl 4 by metallic aluminum or by further milling the resulting reduction product, together with (2) a reaction product of a mixture of titanium tetrachloride with an ether, in a mixing ratio of said titanium trichloride (1) to said reaction product (2) of 1:0.001 to 0.3, (ii) a dialkylaluminum halide, (iii) an electron donor compound, and (iv) an inert solvent, (b) feeding propylene into the resulting catalyst solution at a temperature of 10°-50° C. (i) at a feeding rate in a ratio by weight of 0.02-1/said titanium trichloride composition/hr. (ii) in a feeding amount in a ratio by weight of 0.5-5/said titanium trichloride composition, and (iii) under a pressure of atmospheric pressure to 10 atmospheres, to obtain an activated catalyst solution containing polypropylene in an amount of 0.5-5 times the weight of the titanium trichloride composition contained in said catalyst solution, in advance of the subsequent copolymerization, and (c) feeding into a polymerization zone containing said activated catalyst solution, (1) 100 parts by weight of propylene, (2) 2 to 13 parts by weight of an α-olefin having 4 to 12 carbon atoms, and (3) 1 to 5 parts by weight of ethylene, said propylene and said α-olefin having 4-12 carbon atoms being fed into the catalyst solution at the same time and continuously, said ethylene being fed into the gas phase part of the polymerization zone intermittently at time intervals of 5 to 60 minutes, the once feeding time being 1 to 5 minutes, and the polymerization condition being under a temperature of 50° to 75° C. and a pressure of 5 to 40 kg/cm 2 .