Insulation system for winding of electric rotating machines and process of production thereof
Assignee: Hitachi Ltd
•
Filing: 1979-12-14
•
Granted: 1981-12-08
•
Expires: 1999-12-14
Abstract
Abstract An insulation system for winding of electric rotating machines having thermal resistance of class H or more and excellent adhesiveness between a conductor and an insulating layer and resistance to thermal stress can be produced by wrapping a plurality of layers of an insulating tape or sheet having thermal resistance of class H or more around a winding conductor, impregnating the thus treated winding conductor with a solventless varnish consisting essentially of 1 equivalent of an epoxy compound containing at least two vicinal epoxy groups, more than one equivalent of an organic polyisocyanate, and then heating the inpregnated winding conductor at a temperature above 60 DEG C. for a time sufficient to form and cure a resin containing as recurring units at least two isocyanurate rings directly bonded to one another through the residue of the polyisocyanate and two oxazolidone rings directly bonded to each other through the residue of the polyepoxide in the presence of 0.01-10% by weight of a catalyst which forms the isocyanurate rings and oxazolidone rings based on the total amount of the polyepoxide and polyisocyanate.
Inventors
- 👤 Hideyo Hirata
- 👤 Takeshi Hakamada
- 👤 Misao Souma
- 👤 Masao Matsui
- 👤 Yoshiyuki Suda
- 👤 Yoshiharu Karasawa
- 👤 Toshikazu Narahara
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 01:26
CPC Classifications
C; C08; C08G; C08G73/00; C08G73/06; C08G18/00; C08G18/003; C08G59/00; C08G59/18; C08G59/40; C08G59/4007; C08G59/4014; C08G59/4028; C08G73/0622; C08G73/0638; H; H01; H01B; H01B3/00; H01B3/18; H01B3/30; H01B3/302; H01B3/303; H01B3/40; H02; H02K; H02K3/00; H02K3/30; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2933; Y10T428/2936; Y10T428/2964; Y10T428/2967; Y10T428/2969; Y10T428/2971; Y10T428/31504; Y10T428/31511; Y10T428/31533; Y10T428/31547; Y10T428/31551; Y10T428/31562; Y10T428/31598; Y10T428/31601; Y10T428/31721; Y10T428/31725
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
112 words
A winding for electric rotating machines having a plurality of layers of a sheet-form insulating material having thermal resistance of at least class H wrapped around a conductor and a cured resin impregnated in said layers, said cured resin having recurring units represented by the formula, ##STR4## wherein R is a residue of a polyisocyanate, R' is a residue of a polyepoxide, p is an integer of at least 2, and m and r are integers of at least 1, at least two isocyanurate rings directly bonded to one another through the residue of the polyisocyanate and the two oxazolidone rings directly bonded to each other through the residue of the polyepoxide.
Claim 2
Dependent Claim
112 words
A winding for electric rotating machines having a plurality of layers of a sheet-form insulating material having thermal resistance of at least class H wrapped around a conductor and a cured resin impregnated in said layers, said cured resin having recurring units represented by the formula, ##STR4## wherein R is a residue of a polyisocyanate, R' is a residue of a polyepoxide, p is an integer of at least 2, and m and r are integers of at least 1, at least two isocyanurate rings directly bonded to one another through the residue of the polyisocyanate and the two oxazolidone rings directly bonded to each other through the residue of the polyepoxide.
Claim 3
Dependent Claim
34 words
An insulated winding for electric rotating machines according to claim 1, wherein said sheet-form insulating material having thermal resistance of at least class H is a glass fiber, a polyimide, polyamideimide or aromatic polyamide.
Claim 4
Dependent Claim
234 words
A process for producing an insulated winding for electric rotating machines which comprises wrapping a plurality of layers of a sheet-form insulating material having thermal resistance of at least class H around a winding conductor, impregnating the thus treated winding conductor with a varnish consisting essentially of (a) 1 equivalent of a polyepoxide compound containing at least two vicinal epoxy groups, and (b) more than one equivalent of an organic polyisocyanate, and then heating the impregnated winding conductor at a first temperature such that isocyanurate rings are formed by the trimerization of the polyisocyanate and then a second temperature such that oxazolidone rings are formed and cross-linking and curing occur to form and cure a resin having recurring units represented by the formula: ##STR5## wherein R is a residue of the polyisocyanate, R' is a residue of the polyepoxide, p is an integer of at least 2, and m and r are integers of at least 1, at least two isocyanurate rings directly bonded to one another through the residue of the polyisocyanate and two oxazolidone rings directly bonded to each other through the residue of the polyepoxide in the insulating layers, in the presence of 0.01-10% by weight of a catalyst which forms an isocyanurate ring and an oxazolidone ring and is selected from the group consisting of imidazole and morpholine derivatives based on the total amount of the polyepoxide and the polyisocyanate.
Claim 5
Dependent Claim
234 words
A process for producing an insulated winding for electric rotating machines which comprises wrapping a plurality of layers of a sheet-form insulating material having thermal resistance of at least class H around a winding conductor, impregnating the thus treated winding conductor with a varnish consisting essentially of (a) 1 equivalent of a polyepoxide compound containing at least two vicinal epoxy groups, and (b) more than one equivalent of an organic polyisocyanate, and then heating the impregnated winding conductor at a first temperature such that isocyanurate rings are formed by the trimerization of the polyisocyanate and then a second temperature such that oxazolidone rings are formed and cross-linking and curing occur to form and cure a resin having recurring units represented by the formula: ##STR5## wherein R is a residue of the polyisocyanate, R' is a residue of the polyepoxide, p is an integer of at least 2, and m and r are integers of at least 1, at least two isocyanurate rings directly bonded to one another through the residue of the polyisocyanate and two oxazolidone rings directly bonded to each other through the residue of the polyepoxide in the insulating layers, in the presence of 0.01-10% by weight of a catalyst which forms an isocyanurate ring and an oxazolidone ring and is selected from the group consisting of imidazole and morpholine derivatives based on the total amount of the polyepoxide and the polyisocyanate.
Claim 6
Dependent Claim
20 words
A process according to claim 3, wherein said insulating material is of glass fiber, a polyimide, polyamide-imide or aromatic polyamide.
Claim 7
Dependent Claim
22 words
A process according to claim 3, wherein said catalyst which forms an isocyanurate ring and an oxazolidone ring is an imidazole derivative.
Claim 8
Dependent Claim
252 words
A process for producing an insulated winding for electric rotating machines which comprises wrapping a plurality of layers of a sheet-form insulating material having thermal resistance of at least class H around a winding conductor, impregnating the thus treated winding conductor with a solution of a catalyst, for forming isocyanurate rings and oxazolidone rings and selected from the group consisting of imidazole and morpholine derivatives, dissolved in an organic solvent, until 0.01 to 10% by weight of the catalyst is held in the layers based on the total amount of a polyepoxide and an organic polyisocyanate as described below, removing the solvent, impregnating the treated winding with a varnish consisting essentially of (a) one equivalent of a polyepoxide containing at least two vicinal epoxy groups and (b) more than one equivalent of the organic polyisocyanate, and then heating the impregnated winding conductor at a first temperature such that isocyanurate rings formed by the trimerization of the polyisocyanate and then at a second temperature such that oxazolidone rings are formed and cross-linking and curing occur to form and cure a resin having recurring units represented by the formula: ##STR6## wherein R is a residue of the polyisocyanate, R' is a residue of the polyepoxide, p is an integer of at least 2, and m and r are integers of at least 1, at least two isocyanurate rings directly bonded to one another through the residue of the polyisocyanate and two oxazolidone rings directly bonded to each other through the residue of the polyepoxide.
Claim 9
Dependent Claim
252 words
A process for producing an insulated winding for electric rotating machines which comprises wrapping a plurality of layers of a sheet-form insulating material having thermal resistance of at least class H around a winding conductor, impregnating the thus treated winding conductor with a solution of a catalyst, for forming isocyanurate rings and oxazolidone rings and selected from the group consisting of imidazole and morpholine derivatives, dissolved in an organic solvent, until 0.01 to 10% by weight of the catalyst is held in the layers based on the total amount of a polyepoxide and an organic polyisocyanate as described below, removing the solvent, impregnating the treated winding with a varnish consisting essentially of (a) one equivalent of a polyepoxide containing at least two vicinal epoxy groups and (b) more than one equivalent of the organic polyisocyanate, and then heating the impregnated winding conductor at a first temperature such that isocyanurate rings formed by the trimerization of the polyisocyanate and then at a second temperature such that oxazolidone rings are formed and cross-linking and curing occur to form and cure a resin having recurring units represented by the formula: ##STR6## wherein R is a residue of the polyisocyanate, R' is a residue of the polyepoxide, p is an integer of at least 2, and m and r are integers of at least 1, at least two isocyanurate rings directly bonded to one another through the residue of the polyisocyanate and two oxazolidone rings directly bonded to each other through the residue of the polyepoxide.
Claim 10
Dependent Claim
28 words
A process according to claim 6, wherein said sheet-form insulating material having thermal resistance of at least class H is glass fiber, a polyimide, polyamideimide or aromatic polyamide.
Claim 11
Dependent Claim
22 words
A process according to claim 6, wherein said catalyst which forms an isocyanurate ring and an oxazolidone ring is an imidazole derivative.
Claim 12
Dependent Claim
18 words
A process according to claim 3 or 6, wherein more than 2 equivalents of the polyisocyanate is used.
Claim 13
Dependent Claim
16 words
A process according to claim 9, wherein 5 to 10 equivalents of the polyisocyanate is used.
Claim 14
Dependent Claim
31 words
A process according to claim 3 or 6, wherein the heating is carried out at a first temperature of 60°-130° C. and then at a temperature of 150° C. or more.
Claim 15
Dependent Claim
38 words
A process according to claim 11, wherein the heating at a temperature of 60°-130° C. is carried out for 5-15 hours, and the heating at a temperature of 150° C. or more is carried out for 5-15 hours.
Claim 16
Dependent Claim
31 words
A process according to claim 12, wherein the catalyst is included in an amount of 0.1 to 2% by weight based on the total amount of the polyepoxide and the polyisocyanate.
Claim 17
Dependent Claim
8 words
Product formed by the process of claim 13.
Claim 18
Dependent Claim
42 words
The process of claim 12, wherein said catalyst is selected from the group consisting of N-dodecylmorpholine, butylene dimorpholine, hexamethylene dimorpholine, cyanoethyl morpholine, triazinoethyl morpholine, N-methyl morpholine, N-ethyl morpholine, 2-methylimidazole, 2-ethylimidazole, 2-undecylimidazole, 2-heptadecylimidazole, 2-methyl-4-ethylimidazole, 1-butylimidazole, 1-propyl-2-methyl-imidazole, 1-benzyl-2-methylimidazole, 1-cyanoethyl-2-methylimidazole, 1-cyanoethyl-2-undecylimidazole, 1-cyanoethyl-2-phenylimidazole, 2,4-diamino-6-(2'-methylimidazolyl-1'-)-ethyl-s-triazine, and 2,4-diamino-6-(2'-undecylimidazolyl-1'-)-ethyl-s-triazine.
Claim 19
Dependent Claim
8 words
Product formed by the process of claim 15.
Claim 20
Dependent Claim
31 words
A process according to claim 11, wherein the catalyst is included in an amount of 0.1 to 2% by weight based on the total amount of the polyepoxide and the polyisocyanate.
Claim 21
Dependent Claim
8 words
Product formed by the process of claim 12.
Claim 22
Dependent Claim
44 words
The process of claim 3 or 6, wherein said catalyst is selected from the group consisting of N-dodecylmorpholine, butylene dimorpholine, hexamethylene dimorpholine, cyanoethyl morpholine, triazinoethyl morpholine, N-methyl morpholine, N-ethyl morpholine, 2-methylimidazole, 2-ethylimidazole, 2-undecylimidazole, 2-heptadecylimidazole, 2-methyl-4-ethylimidazole, 1-butylimidazole, 1-propyl-2-methyl-imidazole, 1-benzyl-2-methylimidazole, 1-cyanoethyl-2-methylimidazole, 1-cyanoethyl-2-undecylimidazole, 1-cyanoethyl-2-phenylimidazole, 2,4-diamino-6-(2'-methylimidazolyl-1'-)-ethyl-s-triazine, and 2,4-diamino-6-(2'-undecylimidazolyl-1'-)-ethyl-s-triazine.
Claim 23
Dependent Claim
17 words
A process according to claim 6, wherein the impregnating with said varnish takes place under reduced pressure.
Claim 24
Dependent Claim
20 words
A process according to claim 20, wherein the varnish has a viscosity of 7 poises or less during the impregnation.
Claim 25
Dependent Claim
20 words
A process according to claim 21, wherein the varnish has a viscosity of 2 poises or less during the impregnation.
Claim 26
Dependent Claim
10 words
Product formed by the process of claim 3 or 6.
References Cited (Backward Citations)
US3793236A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-12-07 | 1985-06-08 | 1985-12-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-12-07 | 1989-06-08 | 1989-12-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-12-07 | 1993-06-08 | 1993-12-08 | $7700.00 | Window Closed / Lapsed |