Process for improving the adhesion of paint to polyolefin surfaces
Assignee: EIDP Inc
•
Filing: 1980-08-18
•
Granted: 1981-12-01
•
Expires: 2000-08-18
Abstract
Abstract Surfaces of articles made of polyethylene, polypropylene, crystalline dipolymers of ethylene with propylene, blends of two or more of the above, and blends of any of the above with elastomeric ethylene/propylene copolymers or with EPDM copolymers are prepared for painting by priming with a chlorinated polymeric material selected from a chlorinated polypropylene and chlorinated polypropylene containing carboxylic anhydride groups, and exposing to ultraviolet radiation. This treatment improves both dry and wet adhesion of paint to surfaces of articles made of single polyolefins as well as of their blends with elastomeric copolymers in which the latter constitute at most 50% of the total polymer.
Inventors
- 👤 Gerald A. Baseden
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 23:49
CPC Classifications
C; C08; C08J; C08J7/00; C08J7/12; C08J7/123; B; B05; B05D; B05D7/00; B05D7/02; C08J7/04; C08J7/042; C08J7/043; B05D2506/00; B05D2506/20; B05D3/00; B05D3/06; B05D3/061; B05D3/062; B05D3/063; B05D3/065; B05D7/50; B05D7/52; C08J2323/00; C08J2323/02; C08J2423/00; C08J2423/02; C08J2423/10; C08J2423/12; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31855; Y10T428/31909; Y10T428/31928
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
173 words
A process for preparing for painting the surface of an article made of a polyolefin selected from: (1) polyethylene, polypropylene, and crystalline dipolymers of ethylene and propylene; (2) blends of at least two members of the group recited in (1) above; and (3) blends of at least one member of the group recited in (1) above with at least one elastomer selected from the class of ethylene/propylene dipolymers and EPDM copolymers in which the total amount of elastomeric polymers is at most about 50 weight percent of the final polymer blend; said process comprising the steps of: (a) cleaning said surface; (b) priming the cleaned surface with a thin layer of a chlorinated polymeric material selected from: (1) a chlorinated polypropylene containing about 5-25 weight percent of chlorine and having a number average molecular weight of about 5,000-50,000, and (2) a chlorinated polypropylene containing carboxylic anhydride groups and about 5-25 weight percent of chlorine and having a number average molecular weight of about 5,000-50,000; and (c) exposing the primed surface to ultraviolet radiation.
Claim 2
Dependent Claim
173 words
A process for preparing for painting the surface of an article made of a polyolefin selected from: (1) polyethylene, polypropylene, and crystalline dipolymers of ethylene and propylene; (2) blends of at least two members of the group recited in (1) above; and (3) blends of at least one member of the group recited in (1) above with at least one elastomer selected from the class of ethylene/propylene dipolymers and EPDM copolymers in which the total amount of elastomeric polymers is at most about 50 weight percent of the final polymer blend; said process comprising the steps of: (a) cleaning said surface; (b) priming the cleaned surface with a thin layer of a chlorinated polymeric material selected from: (1) a chlorinated polypropylene containing about 5-25 weight percent of chlorine and having a number average molecular weight of about 5,000-50,000, and (2) a chlorinated polypropylene containing carboxylic anhydride groups and about 5-25 weight percent of chlorine and having a number average molecular weight of about 5,000-50,000; and (c) exposing the primed surface to ultraviolet radiation.
Claim 3
Dependent Claim
19 words
The process of claim 1 wherein the ultraviolet radiation has a wavelength within the range of about 200-400 nm.
Claim 4
Dependent Claim
21 words
The process of claim 2 wherein the ultraviolet energy received by the polyolefin article surface is about 0.1-6.0 J/cm 2 .
Claim 5
Dependent Claim
21 words
The process of claim 3 wherein the ultraviolet energy received by the polyolefin article surface is about 0.2-3.0 J/cm 2 .
Claim 6
Dependent Claim
17 words
The process of claim 1 wherein the polyolefin is a crystalline, impact-resistant, hard grade of ethylene/propylene dipolymer.
Claim 7
Dependent Claim
17 words
The process of claim 1 wherein the polyolefin is a blend of polypropylene with an EPDM copolymer.
Claim 8
Dependent Claim
23 words
The process of claim 1 wherein the polyolefin is a blend of a crystalline, impact-resistant hard grade of ethylene/propylene dipolymer with an elastomer.
Claim 9
Dependent Claim
23 words
The process of claim 1 wherein the amount of dry primer deposited on the polyolefin article surface is about 0.017-1.08 mg/cm 2 .
Claim 10
Dependent Claim
17 words
The process of claim 8 wherein the amount of dry primer is about 0.03-0.2 mg/cm 2 .
References Cited (Backward Citations)
US2873241A
Cited
US3551235A
Cited
US3551311A
Cited
US3579485A
Cited
US3619246A
Cited
US3661614A
Cited
CA974928A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-11-30 | 1985-06-01 | 1985-12-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-11-30 | 1989-06-01 | 1989-12-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-11-30 | 1993-06-01 | 1993-12-01 | $7700.00 | Window Closed / Lapsed |