Electroplating of thick film circuitry
Assignee: Hughes Missile Systems Co
•
Filing: 1977-08-01
•
Granted: 1981-12-01
•
Expires: 1997-08-01
Abstract
Abstract The improved circuit composite of the present invention is of the thick film type, but is readily solderable, weldable and bondable to wire without oxidizing. The composite comprises a refractory substrate such as alumina, beryllia or zirconia, a thick printed film pattern of oxidizable electrically conductive metal such as copper, nickel, or silver bonded to the substrate, and a thin electroplated film of non-oxidizable electrically conductive metal, such as gold or platinum, enclosing and adhering to the thick film pattern. The then-electroplated film allows wires and contacts to be soldered, welded or bonded to the pattern, as by ultrasonic or thermocompression bonding, without degrading the quality of the contact area and while permitting removal and subsequent reattachment of such wires and contacts. The method is simple, inexpensive and efficient. It calls for forming the thick film on the substrate and then electroplating the thin film thereover. The method results in durable circuit composites, particularly microcircuit composites of high quality and improved utility.
Inventors
- 👤 John H. Wood
- 👤 Victor A. Twaddell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 03:21
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/22; H05K3/24; H05K3/245; H05K3/246; C; C25; C25D; C25D5/00; C25D5/02; H10; H10D; H10D84/00; H10D84/01; H05K1/00; H05K1/02; H05K1/09; H05K1/092; Y; Y10; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12611
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
49 words
An improved direct thermobondable and solderable thin film-thick film printed circuit composite consisting essentially of, in combination: (a) a refractory substrate comprising alumina; (b) a thick printed film of copper bonded to said substrate; and (c) a thin electroplated film of gold enclosing and adherent to said thick film.
Claim 2
Dependent Claim
49 words
An improved direct thermobondable and solderable thin film-thick film printed circuit composite consisting essentially of, in combination: (a) a refractory substrate comprising alumina; (b) a thick printed film of copper bonded to said substrate; and (c) a thin electroplated film of gold enclosing and adherent to said thick film.
Claim 3
Dependent Claim
33 words
The improved composite of claim 1 wherein said thick film is of the order of about 0.0005-0.001 inch thick, and wherein said thin film is of the order of about 0.00005-0.0002 inch thick.
Claim 4
Dependent Claim
32 words
The improved composite of claim 1 wherein said composite is a microcircuit composite, wherein said thick film is about 0.0007 inch thick and wherein said thin film is about 0.0001 inch thick.
Claim 5
Independent Claim
126 words
The method of making an improved directly thermobondable and solderable, thin-film-over-thick-film, printed circuit composite, said method consisting essentially of the steps of: (a) printing a wet mixture of particulate, oxidizable, electrically conductive metal and binder in a desired thick film pattern on a refractory substrate, said thick film pattern being about 0.0005-0.001 inch thick; (b) drying the mixture in air to remove moisture; (c) firing said mixture on said substrate at about 900° C. in nitrogen to bond the metal in said thick film pattern to said substrate; (d) electroplating a thin, adherent film of gold which is essentially non-oxidizable and electrically conductive to enclose said thick film on said substrate; and (e) continuing the electroplating until said electroplated gold film is about 0.00005-0.0002 inch thick.
Claim 6
Independent Claim
126 words
The method of making an improved directly thermobondable and solderable, thin-film-over-thick-film, printed circuit composite, said method consisting essentially of the steps of: (a) printing a wet mixture of particulate, oxidizable, electrically conductive metal and binder in a desired thick film pattern on a refractory substrate, said thick film pattern being about 0.0005-0.001 inch thick; (b) drying the mixture in air to remove moisture; (c) firing said mixture on said substrate at about 900° C. in nitrogen to bond the metal in said thick film pattern to said substrate; (d) electroplating a thin, adherent film of gold which is essentially non-oxidizable and electrically conductive to enclose said thick film on said substrate; and (e) continuing the electroplating until said electroplated gold film is about 0.00005-0.0002 inch thick.
Claim 7
Dependent Claim
20 words
The method of claim 4 wherein said substrate comprises alumina, and wherein said metal in said wet mixture comprises copper.
Claim 8
Dependent Claim
29 words
The method of claim 4 wherein said electroplated film is about 0.0001 inch thick, wherein said pattern is copper about 0.0007 inch thick and wherein said substrate is alumina.
Claim 9
Dependent Claim
35 words
The method of claim 4 wherein the printing step further comprises forming a circuit pattern for said composite on a photosensitive emulsion-covered screen to a total thickness for both wire and emulsion of 2.7 mils.
Claim 10
Dependent Claim
19 words
The method of claim 7 wherein said screen is constructed of 325 mesh wire strung at a 45° angle.
Claim 11
Dependent Claim
48 words
The method of claim 7 wherein said printing step further comprises placing the screen against a 96% alumina substrate and squeezing the wet mixture of metal and binder in paste form through the screen onto the substrate surface to form a pattern of paste corresponding to said composite.
Claim 12
Dependent Claim
25 words
The method of claim 4 further including the step of drying the printed thick pattern for 10 minutes at 135° C. before firing said mixture.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-11-30 | 1985-06-01 | 1985-12-01 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-11-30 | 1989-06-01 | 1989-12-01 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-11-30 | 1993-06-01 | 1993-12-01 | $7700.00 | Window Closed / Lapsed |