Separator plate for electrochemical cells

Claim 2

An electrochemical cell separator plate having a thickness no greater than 0.150 inch and having been made by molding and then heat treating a mixture comprising high purity graphite powder and a carbonizable thermosetting phenolic resin in a proportion 45-65 parts by weight graphite and 55-35 parts by weight resin, said graphite powder consisting of substantially 100% fully graphitic particles having a density of at least 2.0 gm/cc, an average aspect ratio of less than about 0.40, and a distribution of particle sizes up to a maximum of about 230 microns, with between 31 to 62 weight percent of the particles having a size less than 45 microns, said resin having a carbon yield of at least 50 percent, said finished plate having been graphitized to at least 2100° C. and having an initial threshold corrosion potential at 400° F. of at least 1,000 millivolts, a maximum initial thru-plane electrical resistivity of 0.011 ohm-cm, an initial flexural strength at 400 ° F. of at least 4000 psi and an electrolyte takeup no greater than 5.0 percent.

Claim 3

The separator plate according to claim 1 wherein said high purity graphite powder is a graphite which includes less than 1500 ppm total impurities, no impurities having a particle size of greater than 10 mils.

Claim 4

The separator plate according to claim 1 wherein the graphite powder in the molding mixture has a particle size distribution wherein 35-50 weight percent of the particles are less than 45 microns, 19-52 weight percent are between 45-100 microns, 5-30 weight percent are between 100-150 microns, less than 12 weight percent are greater than 150 microns, less than 5 weight percent are greater than 200 microns, and less than 0.5 weight percent are greater than 230 microns.

Claim 5

The separator plate according to claim 1 wherein the finished separator plate has an initial threshold corrosion potential of at least 1100 millivolts.

Claim 6

The separator plate according to claim 1 wherein said high purity graphite powder comprises less than 900 ppm impurities, the initial threshold corrosion potential is at least 1100 millivolts, electrolyte take-up is no greater than 3.0 percent, the initial flexural strength at 400° F. is not less than 5500 psi, and the maximum initial in-plane electrical resistivity is 0.002 ohm-cm.

Claim 7

The separator plate according to claim 1 wherein the finished plate is not greater than 0.100 inch thick.

Claim 8

The separator plate according to claim 1 wherein the initial hydrogen permeability of the plate is no greater than 0.03 cc/ft 2 /sec.

Claim 9

The separator plate according to claims 1, 3, 4, 5, 6 or 7, said plate having been made by molding and then heat treating a mixture comprising 50-60 weight percent of said graphite and 50-40 weight percent of said resin.

Claim 10

A fuel cell separator plate for use in phosphoric acid electrolyte fuel cells, said plate having a thickness no greater than 0.050 inch and having been made by molding a mixture comprising 50-40 weight percent carbonizable thermosetting phenolic resin, said graphite powder comprising less than 900 ppm impurities and consisting of graphite particles having a density of at least 2.0 gm/cc, an average aspect ratio of less than about 0.40, and a particle size distribution wherein 35-50 weight percent of the particles are less than 45 microns, 19-52 weight percent are between 45-100 microns, 5-30 weight percent are between 100 and 150 microns, less than 12 weight percent are greater than 150 microns, less than 5 weight percent are greater than 200 microns, and less than 0.5 weight percent are greater than 230 microns, said resin having a carbon yield of at least 50 percent, said finished plate being fully graphitic, having an initial threshold corrosion potential of at least 1100 millivolts, a maximum initial thru-plane electrical resistivity of 0.009 ohm-cm, an initial flexural strength of 400° F. of at least 5500 psi, and electrolyte take-up no greater than 3.0 percent, and an initial hydrogen permeability of no greter than 0.03 cc/ft 2 /sec.

Claim 11

A fuel cell separator plate for use in phosphoric acid electrolyte fuel cells, said plate having a thickness no greater than 0.050 inch and having been made by molding a mixture comprising 50-40 weight percent carbonizable thermosetting phenolic resin, said graphite powder comprising less than 900 ppm impurities and consisting of graphite particles having a density of at least 2.0 gm/cc, an average aspect ratio of less than about 0.40, and a particle size distribution wherein 35-50 weight percent of the particles are less than 45 microns, 19-52 weight percent are between 45-100 microns, 5-30 weight percent are between 100 and 150 microns, less than 12 weight percent are greater than 150 microns, less than 5 weight percent are greater than 200 microns, and less than 0.5 weight percent are greater than 230 microns, said resin having a carbon yield of at least 50 percent, said finished plate being fully graphitic, having an initial threshold corrosion potential of at least 1100 millivolts, a maximum initial thru-plane electrical resistivity of 0.009 ohm-cm, an initial flexural strength of 400° F. of at least 5500 psi, and electrolyte take-up no greater than 3.0 percent, and an initial hydrogen permeability of no greter than 0.03 cc/ft 2 /sec.

Claim 12

The separator plate according to claim 9, said plate having been molded from a mixture comprising about 50 weight percent of said graphite powder and 50 weight percent of said phenolic resin.

Claim 13

The separator plate according to claim 10 wherein said finished plate has an initial hydrogen permeability of no greater than 0.02 cc/ft 2 /sec.