Process for producing aqueous emulsions of vinyl chloride/vinyl ester/ethylene copolymer
Assignee: Sumitomo Chemical Co Ltd
•
Filing: 1979-09-24
•
Granted: 1981-11-10
•
Expires: 1999-09-24
Abstract
Abstract An improved process for producing an aqueous emulsion of a vinyl chloride/vinyl ester/ethylene copolymer having a small heat fluidity and excellent strength which comprises continuously adding a solution of a specific polybasic acid polyallyl ester in the vinyl chloride and/or vinyl ester and further at least 60% by weight of the vinyl chloride and vinyl ester to the polymerization system during the polymerization reaction. The copolymer thus produced has a large benzene-insoluble part and the aqueous emulsion thereof is stable and is useful as an adhesive, as for paint compositions, or as a binder for fibers and papers.
Inventors
- 👤 Shizuo Narisawa
- 👤 Takeo Oyamada
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 10:33
CPC Classifications
C; C08; C08F; C08F214/00; C08F214/02; C08F214/04; C08F214/06; C08F218/00; C08F218/02; C08F218/04; C08F218/08; Y; Y10; Y10S; Y10S526/00; Y10S526/922
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
224 words
In a process for producing a stable aqueous emulsion of a vinyl chloride/vinyl ester/ethylene copolymer having less coarse particles and having a small heat fluidity and an excellent strength without adversely affecting its basic characteristics, including the water resistance, the alkali resistance, the fire retardant properties and the chemical resistance thereof, comprising copolymerizing vinyl chloride, a vinyl ester and ethylene in the presence of an emulsion-dispersing agent and a radical polymerization initiator, under an ethylene pressure, the improvement which comprises, dissolving a polybasic acid polyallyl ester selected from the group consisting of diallyl phthalate, diallyl isophthalate, diallyl terephthalate, diallyl maleate, diallyl itaconate, diallyl succinate, dially adipate and triallyl benzenetricarboxylate in the vinyl chloride and/or vinyl ester to be copolymerized in an amount of 0.1 to 1.0% by weight based on the total weight of the vinyl chloride and vinyl ester, and continuously adding the solution to the polymerization system during the polymerization reaction, and continuously adding at least 60% by weight of the vinyl chloride and vinyl ester to the polymerization system during the polymerization reaction, to give an aqueous emulsion of a vinyl chloride/vinyl ester/ethylene copolymer comprising 20 to 75% by weight of vinyl chloride, 15 to 70% by weight of the vinyl ester and 5 to 30% by weight of ethylene and containing 5 to 60% by weight of a benzene-insoluble part.
Claim 2
Dependent Claim
224 words
In a process for producing a stable aqueous emulsion of a vinyl chloride/vinyl ester/ethylene copolymer having less coarse particles and having a small heat fluidity and an excellent strength without adversely affecting its basic characteristics, including the water resistance, the alkali resistance, the fire retardant properties and the chemical resistance thereof, comprising copolymerizing vinyl chloride, a vinyl ester and ethylene in the presence of an emulsion-dispersing agent and a radical polymerization initiator, under an ethylene pressure, the improvement which comprises, dissolving a polybasic acid polyallyl ester selected from the group consisting of diallyl phthalate, diallyl isophthalate, diallyl terephthalate, diallyl maleate, diallyl itaconate, diallyl succinate, dially adipate and triallyl benzenetricarboxylate in the vinyl chloride and/or vinyl ester to be copolymerized in an amount of 0.1 to 1.0% by weight based on the total weight of the vinyl chloride and vinyl ester, and continuously adding the solution to the polymerization system during the polymerization reaction, and continuously adding at least 60% by weight of the vinyl chloride and vinyl ester to the polymerization system during the polymerization reaction, to give an aqueous emulsion of a vinyl chloride/vinyl ester/ethylene copolymer comprising 20 to 75% by weight of vinyl chloride, 15 to 70% by weight of the vinyl ester and 5 to 30% by weight of ethylene and containing 5 to 60% by weight of a benzene-insoluble part.
Claim 3
Dependent Claim
84 words
A process for producing an aqueous emulsion according to claim 1, wherein one or more vinyl monomers selected from the group consisting of a vinyl monomer having a glycidyl group, a vinyl monomer having an N-methylol group, a vinyl monomer having an alkoxymethyl group, a vinyl monomer having a carboxyl group and a vinyl monomer having a hydroxyalkyl group are copolymerized in an amount of not more than 10% by weight based on the total weight of the vinyl chloride, vinyl ester and ethylene.
Claim 4
Dependent Claim
40 words
A process for producing an aqueous emulsion according to claim 1, wherein the polybasic acid polyallyl ester is used in an amount of 0.2 to 0.8% by weight based on the total weight of the vinyl chloride and vinyl ester.
Claim 5
Dependent Claim
31 words
A process for producing an aqueous emulsion according to claim 1, wherein the benzene-insoluble part of the vinyl chloride/vinyl ester/ethylene copolymer is in the range of 10 to 50% by weight.
Claim 6
Dependent Claim
36 words
A process for producing an aqueous emulsion according to claim 1, wherein the vinyl ester is a member selected from the group consisting of vinyl acetate, vinyl propionate, vinyl butyrate, vinyl laurate and vinyl tertiary carboxylate.
Claim 7
Dependent Claim
18 words
A process for producing an aqueous emulsion according to claim 5, wherein the vinyl ester is vinyl acetate.
Claim 8
Dependent Claim
45 words
A process for producing an aqueous emulsion according to claim 2, wherein the vinyl monomer is a member selected from the group consisting of glycidyl acrylate, glycidyl methacrylate, N-methylolacrylamide, N-methylolmethacryamide, acrylic acid, itaconic acid, maleic acid, 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate, an N-alkoxymethylacrylamide and an N-alkoxymethylmethacrylamide.
References Cited (Backward Citations)
US2934529A
Cited
US3539488A
Cited
US3501440A
Cited
US3925327A
Cited
US3979366A
Cited
US4128518A
Cited
US4123405A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-11-09 | 1985-05-11 | 1985-11-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-11-09 | 1989-05-11 | 1989-11-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-11-09 | 1993-05-11 | 1993-11-10 | $7700.00 | Window Closed / Lapsed |