Cladding and method of making same
Assignee: Fletcher Wood Panels Ltd
•
Filing: 1979-10-22
•
Granted: 1981-11-10
•
Expires: 1999-10-22
Abstract
Abstract A method of manufacturing cladding which comprises the steps of making cellulosic material in the form of particles in which about 20 to 30% of the particles comprise fine particles and the remaining percentage comprise coarse particles which have a thickness of 0.35 to 0.7 mm. A bonding resin is then added to the cellulosic material and the cellulosic material is then formed into a mat. The mat is then passed to a hot press and the press is operated in a manner to obtain rapid closure from the initial contacting of the press platens with the mat until the cladding material so formed is of required thickness. The coarse particles form a core between two layers of fine particles and the core has a void content of between 10 and 30% preferably about 25%.
Inventors
- 👤 Deane W. Smart
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-23 23:56
CPC Classifications
C; C08; C08L; C08L97/00; C08L97/02; B; B27; B27N; B27N3/00; B27N3/08; B27N3/10; Y; Y10; Y10S; Y10S428/00; Y10S428/92; Y10S428/921; Y10T; Y10T428/00; Y10T428/24; Y10T428/24942; Y10T428/25; Y10T428/253; Y10T428/26; Y10T428/31504; Y10T428/31942; Y10T428/31949; Y10T428/31957
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
175 words
A method of manufacturing cladding, said method comprising the steps of making cellulosic material in the form of particles, in which about 20% to 30% of the particles comprise fine particles the remaining percentage comprising coarse particles having a thickness of 0.35 mm to 0.7 mm, adding a bonding resin to the cellulosic material, forming the cellulosic material into a mat, passing that mat to a hot press in a manner such that said coarse particles form a core between two layers of said fine particles, operating the press in a rapid manner such that the elapsed time between the initial contacting of the press platens with the mat until the cladding material so formed is of the required thickness is between 10 seconds and 25 seconds, said pressing operation maintaining between 10% and 30% of the core void, maintaining the press temperature at temperatures of the order of 180° to 240° C., maintaining the pressure and temperature for a sufficient time to cure the cladding and removing the wall board cladding from the press.
Claim 2
Independent Claim
175 words
A method of manufacturing cladding, said method comprising the steps of making cellulosic material in the form of particles, in which about 20% to 30% of the particles comprise fine particles the remaining percentage comprising coarse particles having a thickness of 0.35 mm to 0.7 mm, adding a bonding resin to the cellulosic material, forming the cellulosic material into a mat, passing that mat to a hot press in a manner such that said coarse particles form a core between two layers of said fine particles, operating the press in a rapid manner such that the elapsed time between the initial contacting of the press platens with the mat until the cladding material so formed is of the required thickness is between 10 seconds and 25 seconds, said pressing operation maintaining between 10% and 30% of the core void, maintaining the press temperature at temperatures of the order of 180° to 240° C., maintaining the pressure and temperature for a sufficient time to cure the cladding and removing the wall board cladding from the press.
Claim 3
Dependent Claim
114 words
A method of manufacturing cladding as claimed in claim 1 including the steps of making a mixture of said cellulosic particles but adding said bonding resin to said particles before mixing, passing the mixture past air separation means which causes the mixture to separate into a stream of coarse particles having a stream of fine particles on two sides thereof, passing a surface on which the cladding is to be formed beneath the air separating means in a manner such that one of the streams of fine particles is first collected on the surface, the stream of coarse particles is then collected and the further stream of fine particles collected resulting in said mat.
Claim 4
Dependent Claim
20 words
A method of manufacturing cladding as claimed in claim 1 wherein said void content of said core is about 25%.
Claim 5
Dependent Claim
27 words
A method of manufacturing cladding as claimed in claim 1 or claim 2 wherein said method includes the step of adding urea formaldehyde as the bonding resin.
Claim 6
Dependent Claim
25 words
A method of manufacturing cladding as claimed in claim 4 wherein about 5% by weight of bonding resin, based on the cellulosic material, is used.
Claim 7
Dependent Claim
33 words
A method of manufacturing cladding as claimed in claim 1 wherein the proportion of fine particles to coarse particles is about 25% by weight fine particles to about 75% by weight coarse particles.
Claim 8
Dependent Claim
23 words
A method of manufacturing cladding as claimed in claim 5 wherein a greater amount of bonding resin is added to the fine material.
Claim 9
Dependent Claim
18 words
A method of manufacturing cladding as claimed in claim 1 wherein the pressing temperature is about 220° C.
Claim 10
Dependent Claim
27 words
A method of manufacturing cladding as claimed in claim 8 wherein the time of closing between open and closed positions of said press is about 15 seconds.
Claim 11
Dependent Claim
24 words
A method of manufacturing cladding is claimed in claim 1 wherein fireproof coatings are applied to the cladding either during manufacture or during erection.
Claim 12
Dependent Claim
118 words
A cladding comprising cellulosic material in the form of particles of which about 20%-30% of the particles comprise fine particles and the remaining percentage comprise coarse particles having a thickness of 0.35 mm to 0.7 mm which coarse particles form a core between two layers of fine particles, said particles being bonded by bonding resin and the cladding being formed by the layers being pressed in a hot press at a temperature between 180° C. and 240° C. and the pressing pressures being arranged so that the wall board is pressed to its final thickness within 10 seconds to 25 seconds and such that said core has a void content between 10% and 30% of the volume thereof.
Claim 13
Dependent Claim
118 words
A cladding comprising cellulosic material in the form of particles of which about 20%-30% of the particles comprise fine particles and the remaining percentage comprise coarse particles having a thickness of 0.35 mm to 0.7 mm which coarse particles form a core between two layers of fine particles, said particles being bonded by bonding resin and the cladding being formed by the layers being pressed in a hot press at a temperature between 180° C. and 240° C. and the pressing pressures being arranged so that the wall board is pressed to its final thickness within 10 seconds to 25 seconds and such that said core has a void content between 10% and 30% of the volume thereof.
Claim 14
Dependent Claim
14 words
A cladding as claimed in claim 11 wherein said void content is about 25%.
Claim 15
Dependent Claim
55 words
A cladding is claimed in claim 11 wherein said wall board has a core of said particles having a thickness between 0.35 mm to 0.7 mm and said core having surface layers comprising fine particles, the proportion of fine to coarse particles being between 20% fine and 80% coarse and 30% fine and 70% coarse.
Claim 16
Dependent Claim
16 words
A cladding as claimed in claim 13 wherein said particles are 25% fine and 75% coarse.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-11-09 | 1985-05-11 | 1985-11-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-11-09 | 1989-05-11 | 1989-11-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-11-09 | 1993-05-11 | 1993-11-10 | $7700.00 | Window Closed / Lapsed |