High yield silicon carbide from alkylated or arylated pre-ceramic polymers

Claim 1

A method of preparing a polysilane having the average formula {(CH.sub.3).sub.2 Si}{CH.sub.3 Si} (I) in which polysilane there is from 0 to 60 mole percent (CH 3 ) 2 Si═units and 40 to 100 mole percent CH 3 Si.tbd.units, wherein there is also bonded to the silicon atoms other silicon atoms and additional alkyl radicals of 1 to 4 carbon atoms or phenyl, which method consists of (A) reacting under anhydrous conditions, a polysilane which is a solid at 25° C. having the average unit formula {(CH.sub.3).sub.2 Si}{CH.sub.3 Si} (II) in which there is from 0 to 60 mole percent (CH 3 ) 2 Si═units and 40 to 100 mole percent CH 3 Si.tbd.units, wherein the remaining bonds on the silicon atoms are attached to either another silicon atom, a chlorine atom or a bromine atom such that the polysilane contains from 10-38 weight percent, based on the weight of the polysilane, of hydrolyzable chlorine of 21-58 weight percent based on the weight of the polysilane of hydrolyzable bromine, with an alkyl or aryl Grignard reagent having the general formula RMgX where X is a halogen and R is an alkyl group of 1 to 4 carbon atoms or phenyl at a temperature of from 0° to 120° C. for a period of from 1 to 48 hours, in a suitable solvent, and (B) thereafter recovering the polysilane (I).

Claim 2

A method of preparing a polysilane having the average formula {(CH.sub.3).sub.2 Si}{CH.sub.3 Si} (I) in which polysilane there is from 0 to 60 mole percent (CH 3 ) 2 Si═units and 40 to 100 mole percent CH 3 Si.tbd.units, wherein there is also bonded to the silicon atoms other silicon atoms and additional alkyl radicals of 1 to 4 carbon atoms or phenyl, which method consists of (A) reacting under anhydrous conditions, a polysilane which is a solid at 25° C. having the average unit formula {(CH.sub.3).sub.2 Si}{CH.sub.3 Si} (II) in which there is from 0 to 60 mole percent (CH 3 ) 2 Si═units and 40 to 100 mole percent CH 3 Si.tbd.units, wherein the remaining bonds on the silicon atoms are attached to either another silicon atom, a chlorine atom or a bromine atom such that the polysilane contains from 10-38 weight percent, based on the weight of the polysilane, of hydrolyzable chlorine of 21-58 weight percent based on the weight of the polysilane of hydrolyzable bromine, with an alkyl or aryl Grignard reagent having the general formula RMgX where X is a halogen and R is an alkyl group of 1 to 4 carbon atoms or phenyl at a temperature of from 0° to 120° C. for a period of from 1 to 48 hours, in a suitable solvent, and (B) thereafter recovering the polysilane (I).

Claim 6

A method of preparing silicon carbide ceramic material which consists of heating to at least 1200° C. a polysilane having the average unit formula {(CH.sub.3).sub.2 Si}{CH.sub.3 Si} in which polysilane there is from 0 to 60 mole percent (CH 3 ) 2 Si═units and 40 to 100 mole percent CH 3 Si.tbd.units wherein there is also bonded to the silicon atoms other silicon atoms and additional alkyl radicals of 1 to 4 carbon atoms or phenyl.

Claim 7

A method of preparing silicon carbide ceramic material which consists of heating to at least 1200° C. a polysilane having the average unit formula {(CH.sub.3).sub.2 Si}{CH.sub.3 Si} in which polysilane there is from 0 to 60 mole percent (CH 3 ) 2 Si═units and 40 to 100 mole percent CH 3 Si.tbd.units wherein there is also bonded to the silicon atoms other silicon atoms and additional alkyl radicals of 1 to 4 carbon atoms or phenyl.

Claim 9

A method of preparing a silicon carbide-containing ceramic article which consists of (A) forming an article of the desired shape from a polysilane having the average formula {(CH.sub.3).sub.2 Si}{CH.sub.3 Si} in which polysilane there is from 0 to 60 mole percent (CH 3 ) 2 Si═units and 40 to 100 mole percent CH 3 Si.tbd.units, wherein there is also bonded to the silicon atoms other silicon atoms and additional alkyl radicals of 1 to 4 carbon atoms or phenyl; and (B) heating the article formed in (A) in an inert atmosphere or in a vacuum to an elevated temperature in the range of 1200° C. to 1600° C. until the polysilane is converted to silicon carbide-containing ceramic.

Claim 10

A method of preparing a silicon carbide-containing ceramic article which consists of (A) forming an article of the desired shape from a polysilane having the average formula {(CH.sub.3).sub.2 Si}{CH.sub.3 Si} in which polysilane there is from 0 to 60 mole percent (CH 3 ) 2 Si═units and 40 to 100 mole percent CH 3 Si.tbd.units, wherein there is also bonded to the silicon atoms other silicon atoms and additional alkyl radicals of 1 to 4 carbon atoms or phenyl; and (B) heating the article formed in (A) in an inert atmosphere or in a vacuum to an elevated temperature in the range of 1200° C. to 1600° C. until the polysilane is converted to silicon carbide-containing ceramic.

Claim 12

A method of preparing a filled ceramic article which consists of (A) mixing a polysilane with at least one conventional ceramic filler which polysilane has the average formula {(CH.sub.3).sub.2 Si}{CH.sub.3 Si} in which polysilane there is from 0 to 60 mole percent (CH 3 ) 2 Si═units and 40 to 100 mole percent CH 3 Si.tbd.units, wherein there is also bonded to the silicon atoms other silicon atoms and additional alkyl radicals of 1 to 4 carbon atoms or phenyl; (B) forming an article of the desired shape from the mixture of polysilane and fillers and, (C) heating the article formed in (B) in an inert atmosphere or in a vacuum to an elevated temperature in the range of 1200° C. to 1600° C. until the polysilane is converted to a silicon carbide-containing ceramic.

Claim 13

A method of preparing a filled ceramic article which consists of (A) mixing a polysilane with at least one conventional ceramic filler which polysilane has the average formula {(CH.sub.3).sub.2 Si}{CH.sub.3 Si} in which polysilane there is from 0 to 60 mole percent (CH 3 ) 2 Si═units and 40 to 100 mole percent CH 3 Si.tbd.units, wherein there is also bonded to the silicon atoms other silicon atoms and additional alkyl radicals of 1 to 4 carbon atoms or phenyl; (B) forming an article of the desired shape from the mixture of polysilane and fillers and, (C) heating the article formed in (B) in an inert atmosphere or in a vacuum to an elevated temperature in the range of 1200° C. to 1600° C. until the polysilane is converted to a silicon carbide-containing ceramic.

Claim 15

A method of preparing an article coated with ceramic which consists of (A) mixing a polysilane with at least one conventional ceramic filler which polysilane has the average unit formula {(CH.sub.3).sub.2 Si}{CH.sub.3 Si} in which polysilane there is from 0 to 60 mole percent (CH 3 ) 2 Si═units and 40 to 100 mole percent CH 3 Si.tbd.units, wherein there is also bonded to the silicon atoms other silicon atoms and additional alkyl radicals of 1 to 4 carbon atoms or phenyl; (B) coating a substrate with the mixture of polysilane and fillers and, (C) heating the coated substrate in an inert atmosphere or in a vacuum to an elevated temperature in the range of 1200° C. to 1600° C. until the coating is converted to a silicon carbide ceramic material whereby a silicon carbide-containing ceramic coated article is obtained.

Claim 16

A method of preparing an article coated with ceramic which consists of (A) mixing a polysilane with at least one conventional ceramic filler which polysilane has the average unit formula {(CH.sub.3).sub.2 Si}{CH.sub.3 Si} in which polysilane there is from 0 to 60 mole percent (CH 3 ) 2 Si═units and 40 to 100 mole percent CH 3 Si.tbd.units, wherein there is also bonded to the silicon atoms other silicon atoms and additional alkyl radicals of 1 to 4 carbon atoms or phenyl; (B) coating a substrate with the mixture of polysilane and fillers and, (C) heating the coated substrate in an inert atmosphere or in a vacuum to an elevated temperature in the range of 1200° C. to 1600° C. until the coating is converted to a silicon carbide ceramic material whereby a silicon carbide-containing ceramic coated article is obtained.