Two-component mixed acrylic fibres wherein acrylic components have different amounts of non-ionizable plasticizing comonomer
Assignee: Rhone Poulenc Textile SA
•
Filing: 1979-11-28
•
Granted: 1981-10-27
•
Expires: 1999-11-28
Abstract
Abstract The present invention relates to two-component acrylic fibres and yarns and their process of preparation. They consist of two copolymers based on acrylonitrile, in which the proportion of plasticizing comonomer differs by between 4 and 15% and which contain a total number of milliequivalents of acid of at least 50 per kg of polymer; they comprise a mixture of monolaminar, bilaminar and multilaminar strands; they possess a crimp, the direction of which depends on the heat and/or mechanical treatments to which they have been subjected, component B, which contains the smaller proportion of plasticizing comonomer, being located on the inside of the helix formed by the filaments, after treatment, without tension, at a temperature which is below about 110° C. and at least equal to ambient temperature, and being located on the outside of the helix after treatment under tension or after heat treatment at a temperature above 110° C., and the contraction and the crimp spacing varying from one strand to the next and along one and the same strand. The yarns and fibres according to the invention can be used in all the known textile-converting techniques, namely stretch-breaking, converting, carding and the like.
Inventors
- 👤 Georges Achard
- 👤 Pierre Chion
- 👤 Jacques Menault
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 23:19
CPC Classifications
D; D01; D01F; D01F8/00; D01F8/04; D01F8/08; Y; Y10; Y10T; Y10T428/00; Y10T428/29; Y10T428/2913; Y10T428/2922; Y10T428/2924; Y10T428/2929; Y10T428/2931
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
272 words
Two-component mixed acrylic composite fibres and yarns with a natural crimp, suitable for carding, stretch breaking and converting said fibers consisting of a mixture of monolaminar, bilaminar and multilaminar strands and made of two polymers A and B, polymer A comprising at least 83% by weight of acrylonitrile, 4 to 15% by weight of a non-ionisable plasticising comonomer, and up to 2% by weight of an acid comonomer which is copolymerisable with acrylonitrile, and polymer B comprising at least 94% by weight of acrylonitrile, 0 to 4% by weight of a non-ionisable plasticising comonomer and up to 2% by weight of an acid comonomer which is copolymerisable with acrylonitrile, the difference in the proportion of plasticising comonomer in the polymers A and B being between 4 and 15% by weight and the total number of milliequivalents of acid in the two polymers being at least 50 per kg of polymer, the said composite fibres and yarns possessing a three-dimensional crimp, the direction of which depends on the heat and/or mechanical treatments to which the composite fibres or yarns have been subjected, polymer B being located on the inside of the helix formed by strands which have been subjected, without tension, to a temperature below about 110° C. and at least equal to ambient temperatures (crimp C 1), and being located on the outside of the helix formed by strands which have been subjected to tension and/or heat treatment at a temperature above about 110° C. (crimp C 2), the contraction and frequency of the two types of crimp varying from one strand to the next and along the length of one strand.
Claim 2
Dependent Claim
272 words
Two-component mixed acrylic composite fibres and yarns with a natural crimp, suitable for carding, stretch breaking and converting said fibers consisting of a mixture of monolaminar, bilaminar and multilaminar strands and made of two polymers A and B, polymer A comprising at least 83% by weight of acrylonitrile, 4 to 15% by weight of a non-ionisable plasticising comonomer, and up to 2% by weight of an acid comonomer which is copolymerisable with acrylonitrile, and polymer B comprising at least 94% by weight of acrylonitrile, 0 to 4% by weight of a non-ionisable plasticising comonomer and up to 2% by weight of an acid comonomer which is copolymerisable with acrylonitrile, the difference in the proportion of plasticising comonomer in the polymers A and B being between 4 and 15% by weight and the total number of milliequivalents of acid in the two polymers being at least 50 per kg of polymer, the said composite fibres and yarns possessing a three-dimensional crimp, the direction of which depends on the heat and/or mechanical treatments to which the composite fibres or yarns have been subjected, polymer B being located on the inside of the helix formed by strands which have been subjected, without tension, to a temperature below about 110° C. and at least equal to ambient temperatures (crimp C 1), and being located on the outside of the helix formed by strands which have been subjected to tension and/or heat treatment at a temperature above about 110° C. (crimp C 2), the contraction and frequency of the two types of crimp varying from one strand to the next and along the length of one strand.
Claim 3
Dependent Claim
34 words
Composite fibres and yarns according to claim 1, in which the crimp C 1 possesses a non-uniform contraction of between 3 and 35% and a non-uniform crimp frequency of between 4 and 40 half-waves/cm.
Claim 4
Dependent Claim
32 words
Composite fibres and yarns according to claim 1 or 2, comprising from 15 to 30% of monolaminar strands, from 40% to 60% of bilaminar strands, and 20 to 45% of multilaminar strands.
Claim 5
Dependent Claim
40 words
Composite fibres and yarns according to claim 1, 2 or 3, in which polymer A contains at least 90% by weight of acrylonitrile, 6 to 9% of the plasticising comonomer, and up to 1% of the comonomer providing acid groups.
Claim 6
Dependent Claim
40 words
Composite fibres and yarns according to any one of claims 1 to 4, in which polymer B contains at least 97% of acrylonitrile, 0 to 2% of the plasticising comonomer, and up to 1% of the comonomer providing acid groups.
Claim 7
Dependent Claim
34 words
Composite fibres and yarns according to any one of claims 1 to 5 in which the plasticising comonomer is methyl methacrylate or vinyl acetate, and the comonomer providing acid groups is a methallylsulphonate salt.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-10-26 | 1985-04-27 | 1985-10-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-10-26 | 1989-04-27 | 1989-10-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-10-26 | 1993-04-27 | 1993-10-27 | $7700.00 | Window Closed / Lapsed |