Temperature stabilized silicon dioxide-mixed oxide, the process for its production and use

Claim 2

Pyrogenically produced, temperature stabilized silicon dioxide-mixed oxide having a BET surface of 50 to 400 m 2 /g , the other component of the mixed oxide being 0.01 to 10 weight % zirconium dioxide or 0.01 to 10 weight % ferric oxide or 0.1 to 9.9 weight % titanium dioxide.

Claim 3

A mixed oxide according to claim 1 wherein the silicon dioxide is stabilized up to a temperature of 1150° C. against reduction in surface area to below 50 m 2 /g.

Claim 4

A mixed oxide according to claim 1 wherein said other component is zirconium dioxide.

Claim 5

A mixed oxide according to claim 3 containing about 0.2% zirconium dioxide.

Claim 6

A mixed oxide according to claim 4 having a BET surface area of 296 m 2 /g and an average particle diameter of about 7 nm.

Claim 7

A mixed oxide according to claim 5 which is capable upon heating to 1150° C. for 3 hours of still having a BET surface area of 125 m 2 /g and an average particle diameter of not over about 10 nm.

Claim 8

A mixed oxide according to claim 1 wherein said other component in ferric oxide.

Claim 9

A mixed oxide according to claim 7 containing about 0.5% Fe 2 O 3 .

Claim 10

A mixed oxide according to claim 8 having a BET surface area of about 300 m 2 /g and an average particle diameter of about 7 nm.

Claim 11

A mixed oxide according to claim 9 which is capable upon heating to 1150° C. for 3 hours to still having a BET surface area of 90 m 2 /g and an average particle diameter of not over about 12 nm.

Claim 12

A mixed oxide according to claim 1 wherein said other component is titanium dioxide.

Claim 13

A mixed oxide according to claim 11 containing about 3.6% TiO 2 .

Claim 14

A mixed oxide according to claim 12 having a BET surface area of about 280 m 2 /g and an average particle diameter of not over about 10 nm.

Claim 15

A mixed oxide according to claim 13 which is capable upon heating to 1150° C. for 3 hours to still having an average particle diameter of not over about 60 nm.

Claim 16

A mixed oxide according to claim 2 wherein said other component is zirconium dioxide or ferric oxide and the mixed oxide has a thermal conductivity of about 1.4×10 -2 W/m×°K and which is capable on heating to 1150° C. for 3 hours of maintaining its thermal conductivity at not over about 2.4×10 -2 W/m×°K at a load of 15 g/cm.

Claim 17

A mixed oxide according to claim 2 wherein said other component is titanium dioxide and the mixed oxide has a thermal conductivity of about 1.4×10 -2 W/m×°K and is capable on heating to 1150° C. for 3 hours of maintaining its thermal conductivity at not over about 4.3×10 -2 W/m×°K at a load of 15 g/cm.

Claim 18

A mixed oxide according to claim 15 wherein said other component is zirconium dioxide.

Claim 19

A mixed oxide according to claim 15 wherein said other component is ferric oxide.

Claim 20

A process of preparing a stabilized silicon dioxide-mixed oxide having a BET surface of 50 to 400 m 2 /g, the other component of the mixed oxide being 0.01 to 10 weight % zirconium dioxide or 0.01 to 10 weight % ferric oxide or 0.1 to 9.9 weight % titanium dioxide and wherein the silicon dioxide is stabilized up to a temperature of 1150° C. against reduction in surface area to below 50 m 2 /g, comprising vaporizing silicon tetrachloride, diluting it with preheated air in the ratio of 0.5 to 1.2 kg of silicon-tetrachloride to 0.8 to 1.2 Nm 3 of air, supplying it to a burner having a mixing chamber, mixing the diluted silicon tetrachloride in the mixing chamber with hydrogen and vapor form ferric chloride, zirconium tetrachloride or titanium tetrachloride in the ratio as to give an silicon dioxide-other component mixed oxide containing 0.01 to 10% zirconium dioxide or 0.1 to 10% ferric oxide or 0.1 to 9.9% titanium dioxide, and wherein the ratio of hydrogen to the total of silicon tetrachloride and the chloride of the other element is 0.8 to 1.5 Nm 3 of hydrogen to 2.8 to 3.3 kg of total chlorides, buring the 4-component mixture in a reaction chamber, separating the solid silicon dioxide-mixed from the gaseous reaction products and freeing the solid silicon dioxide-mixed oxide from adhering hydrogen chloride by heating in moist air.

Claim 21

A process of preparing a stabilized silicon dioxide-mixed oxide having a BET surface of 50 to 400 m 2 /g, the other component of the mixed oxide being 0.01 to 10 weight % zirconium dioxide or 0.01 to 10 weight % ferric oxide or 0.1 to 9.9 weight % titanium dioxide and wherein the silicon dioxide is stabilized up to a temperature of 1150° C. against reduction in surface area to below 50 m 2 /g, comprising vaporizing silicon tetrachloride, diluting it with preheated air in the ratio of 0.5 to 1.2 kg of silicon-tetrachloride to 0.8 to 1.2 Nm 3 of air, supplying it to a burner having a mixing chamber, mixing the diluted silicon tetrachloride in the mixing chamber with hydrogen and vapor form ferric chloride, zirconium tetrachloride or titanium tetrachloride in the ratio as to give an silicon dioxide-other component mixed oxide containing 0.01 to 10% zirconium dioxide or 0.1 to 10% ferric oxide or 0.1 to 9.9% titanium dioxide, and wherein the ratio of hydrogen to the total of silicon tetrachloride and the chloride of the other element is 0.8 to 1.5 Nm 3 of hydrogen to 2.8 to 3.3 kg of total chlorides, buring the 4-component mixture in a reaction chamber, separating the solid silicon dioxide-mixed from the gaseous reaction products and freeing the solid silicon dioxide-mixed oxide from adhering hydrogen chloride by heating in moist air.

Claim 22

A mixed oxide prepared by the process of claim 19.

Claim 23

A mixed oxide according to claim 20 wherein the other component is ferric oxide.

Claim 24

A mixed oxide according to claim 20 wherein the other component is zirconium dioxide.

Claim 25

A mixed oxide according to claim 20 wherein the other component is titanium dioxide.

Claim 26

A process according to claim 19 wherein the ratio of silicon tetrachloride to air is 0.8 to 0.95 kg of silicon tetrachloride to 0.9 to 1.1 Nm 3 and the ratio of hydrogen to total chloride is 0.9 to 1.2 Nm 3 of hydrogen to 2.9 to 3.3 Kg of total chlorides.

Claim 27

A process according to claim 19 wherein the air is heated to 120° to 180° C.

Claim 28

A mixed oxide according to claim 11 containing about 3.6 to 9.9% of TiO 2 .