US4297140A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Ceramic foam cement
Assignee: Corning Glass Works
•
Filing: 1980-07-03
•
Granted: 1981-10-27
•
Expires: 2000-07-03
Abstract
Abstract Foamable particulate cement is capable of forming sintered cordierite foamed ceramic masses. It consists essentially, by weight, of 1-40% cordierite grog, 99-60% ceramic base material and foaming agent, such as SiC. The ceramic base material is raw ceramic material that has an analytical molar composition consisting essentially of about 1.7-2.4 MO . 1.2-2.4 Al 2 O 3 . 4.5-5.4 SiO 2 wherein MO comprises about 0-55 mole % MgO and at least 45 mole % MnO. The grog is ceramic material that has been previously fired and comminuted, and that has an analytical molar composition consisting essentially of about 1.7-2.4 RO . 1.9-2.4 Al 2 O 3 . 4.5-5.2 SiO 2 wherein RO comprises MnO in an amount of 0 mole % up to a mole % that is about 20 mole % lower than the mole % of MO that is MnO and the balance is substantially MgO.
Inventors
- 👤 Robert J. Paisley
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 17:24
CPC Classifications
F; F01; F01N; F01N3/00; F01N3/02; F01N3/021; F01N3/022; F01N3/0222; C; C04; C04B; C04B35/00; C04B35/01; C04B35/16; C04B35/18; C04B35/195; C04B37/00; C04B37/003; C04B37/005; C04B38/00; C04B38/02; F01N3/0211; C04B2235/00; C04B2235/65; C04B2235/656; C04B2235/6562; C04B2237/00; C04B2237/02; C04B2237/04; C04B2237/06; C04B2237/062; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/341; F01N2330/00; F01N2330/06; F02; F02B; F02B3/00; F02B3/06; Y; Y02; Y02T; Y02T10/00; Y02T10/10; Y02T10/12; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24149; Y10T428/249921; Y10T428/249953; Y10T428/249967; Y10T428/249969; Y10T428/249971; Y10T428/249973; Y10T428/249982; Y10T428/249985
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
165 words
A foamable particulate ceramic cement capable of forming a sintered cordierite foamed ceramic mass and consisting essentially, by weight, of: 1-40% cordierite grog, 99-60% ceramic base material and an effective amount of a foaming agent to effect foaming of the cement upon firing to produce the foamed ceramic mass, the base material being raw ceramic material that has an analytical molar composition consisting essentially of about: 1.7-2.4 MO·1.2-2.4 Al 2 O 3 ·4.5-5.4 SiO 2 wherein MO comprises, as mole % of MO, about 0-55% MgO and at least 45% MnO, and the grog being ceramic material that has been previously fired and comminuted, and that has an analytical molar composition consisting essentially of about: 1.7-2.4 RO·1.9-2.4 Al 2 O 3 ·4.5-5.2 SiO 2 wherein RO comprises, as mole % of RO, MnO in an amount of 0% up to a mole % that is about 20 mole % lower than the mole % of MO that is MnO and the balance is substantially MgO.
Claim 2
Dependent Claim
165 words
A foamable particulate ceramic cement capable of forming a sintered cordierite foamed ceramic mass and consisting essentially, by weight, of: 1-40% cordierite grog, 99-60% ceramic base material and an effective amount of a foaming agent to effect foaming of the cement upon firing to produce the foamed ceramic mass, the base material being raw ceramic material that has an analytical molar composition consisting essentially of about: 1.7-2.4 MO·1.2-2.4 Al 2 O 3 ·4.5-5.4 SiO 2 wherein MO comprises, as mole % of MO, about 0-55% MgO and at least 45% MnO, and the grog being ceramic material that has been previously fired and comminuted, and that has an analytical molar composition consisting essentially of about: 1.7-2.4 RO·1.9-2.4 Al 2 O 3 ·4.5-5.2 SiO 2 wherein RO comprises, as mole % of RO, MnO in an amount of 0% up to a mole % that is about 20 mole % lower than the mole % of MO that is MnO and the balance is substantially MgO.
Claim 3
Dependent Claim
24 words
Cement of claim 1 wherein the foaming agent is SiC in an amount up to about 5% by weight of grog plus base material.
Claim 4
Dependent Claim
17 words
Cement of claim 2 wherein SiC is at least 0.25% by weight of grog plus base material.
Claim 5
Dependent Claim
24 words
Cement of claim 3 wherein the grog is at least 5 wt. % and the base material is not more than 95 wt. %.
Claim 6
Dependent Claim
25 words
Cement of claim 3 wherein the analytical molar composition of the base material is about: 1.7-2.4 MO·1.9-2.4 Al 2 O 3 ·4.5-5.2 SiO 2 .
Claim 7
Dependent Claim
17 words
Cement of claim 5 wherein the grog is 5-20 wt.% and the base material is 95-80 wt.%.
Claim 8
Dependent Claim
11 words
Cement of claim 6 wherein SiC is at least 1 wt.%.
Claim 9
Dependent Claim
15 words
Cement of claim 7 wherein MO comprises not more than about 15 mole % MgO.
Claim 10
Dependent Claim
30 words
Cement of claim 7 or 8 wherein the analytical molar composition of the grog is about: 1.8-2.1 RO·1.9-2.1 Al 2 O 3 ·4.9-5.2 SiO 2 and MO is wholly MnO.
Claim 11
Dependent Claim
12 words
Cement of claim 9 wherein SiC is not more than 2 wt.%.
Claim 12
Dependent Claim
29 words
Cement of claim 9 wherein the analytical molar composition of the base material is about: 1.8-2.1 MO·1.9-2.1 Al 2 O 3 ·4.9-5.2 SiO 2 and MO is wholly MnO.
Claim 13
Dependent Claim
41 words
A ceramic structure comprising at least two closely spaced cordierite ceramic surfaces having a sintered cordierite foamed ceramic mass in the space between and bonded to those surfaces, and the foamed ceramic mass being formed of the cement of claim 1.
Claim 14
Dependent Claim
70 words
A method of providing a sintered cordierite foamed ceramic mass between and bonded to at least two closely spaced cordierite ceramic surfaces of a ceramic structure, which method comprises: disposing the cement of claim 1 between the surfaces, firing the structure with the cement so disposed to foaming temperature in the range of about 1160°-1325° C., and thereafter cooling the structure with the cement converted to the foamed ceramic mass.
Claim 15
Dependent Claim
16 words
The method of claim 13 wherein the foaming temperature is in the range of 1170°-1250° C.
Claim 16
Dependent Claim
25 words
The method of claim 13 or 14 wherein firing to foaming temperature is at an average rate of at least about 1000° C. per hour.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-10-26 | 1985-04-27 | 1985-10-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-10-26 | 1989-04-27 | 1989-10-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-10-26 | 1993-04-27 | 1993-10-27 | $7700.00 | Window Closed / Lapsed |