Inorganic gels and ceramic papers, films, fibers, boards, and coatings made therefrom
Assignee: Corning Glass Works
•
Filing: 1980-06-25
•
Granted: 1981-10-27
•
Expires: 2000-06-25
Abstract
Abstract The present invention is related to the production of crystal-containing gels and papers, films, fibers, boards, and coatings made therefrom. The process for making the gels comprises three general steps: first, a fully or predominantly crystalline body is formed containing crystals consisting essentially of a lithium and/or sodium water-swelling mica selected from the group of fluorhectorite, hydroxyl hectorite, boron fluorphlogopite, hydroxyl boron phlogopite, and solid solutions among those and between those and other structurally-compatible species selected from the group of talc, fluortalc, polylithionite, fluorpolylithionite, phlogopite, and fluorphlogopite; second, that body is contacted with a polar liquid, desirably water, to cause swelling and disintegration of the body accompanied with the formation of a gel; and, third, the solid:liquid ratio of the gel is adjusted to a desired value depending upon the application therefor. Where papers, films, fibers, boards, or coatings are desired, such are prepared from the gel, and, to impart good chemical durability thereto, are thereafter contacted with a source of large cations to effect an ion exchange reaction between the large cations and the Li + and/or Na + ions from the interlayer of the crystals, and the products then dried. Glass-ceramic bodies are the preferred starting materials.
Inventors
- 👤 George H. Beall
- 👤 David G. Grossman
- 👤 Syed N. Hoda
- 👤 Karen R. Kubinski
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 22:54
CPC Classifications
C; C03; C03C; C03C10/00; C03C10/0036; C03C10/0045; C03C10/0018; C03C10/0027; C04; C04B; C04B14/00; C04B14/02; C04B14/04; C04B14/20; C04B14/206; C04B14/208; D; D21; D21H; D21H13/00; D21H13/36; D21H13/38; D21H13/44; Y; Y10; Y10S; Y10S106/00; Y10S106/03
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
127 words
Inorganic gels containing a polar liquid and relatively uniformly-sized crystals consisting essentially of a lithium and/or sodium water-swelling mica selected from the group of fluorhectorite, hydroxyl hectorite, boron fluorphlogopite, hydroxyl boron fluorphlogopite, and solid solutions among those and between those and other structurally-compatible species selected from the group of talc, fluortalc, polylithionite, fluorpolylithionite, phlogopite, and fluorphlogopite, at least a substantial portion of said crystals exhibiting a morphology of a continuum of flakes, rectangular-like strips, and interwoven ribbons in parallel or sub-parallel zones or sheaths with said strips and ribbons being about 0.5-10 microns long, about 500 A-5000 A wide, and less than about 100 A thick, and said flakes being irregularly shaped with diameters between about 0.5-10 microns and cross sections of less than about 100 A.
Claim 2
Dependent Claim
127 words
Inorganic gels containing a polar liquid and relatively uniformly-sized crystals consisting essentially of a lithium and/or sodium water-swelling mica selected from the group of fluorhectorite, hydroxyl hectorite, boron fluorphlogopite, hydroxyl boron fluorphlogopite, and solid solutions among those and between those and other structurally-compatible species selected from the group of talc, fluortalc, polylithionite, fluorpolylithionite, phlogopite, and fluorphlogopite, at least a substantial portion of said crystals exhibiting a morphology of a continuum of flakes, rectangular-like strips, and interwoven ribbons in parallel or sub-parallel zones or sheaths with said strips and ribbons being about 0.5-10 microns long, about 500 A-5000 A wide, and less than about 100 A thick, and said flakes being irregularly shaped with diameters between about 0.5-10 microns and cross sections of less than about 100 A.
Claim 3
Dependent Claim
31 words
Inorganic gels according to claim 1 also containing inert fillers such that the total of the solids portion of said gels and said inert fillers ranges up to 95% by volume.
Claim 4
Dependent Claim
23 words
Inorganic gels according to claim 2 wherein said fillers are selected from the group of clays, barite, talc, graphite, gypsum, and organic polymers.
Claim 5
Independent Claim
230 words
A method for preparing inorganic gels containing relatively uniformly-sized crystals consisting essentially of a lithium and/or sodium water-swelling mica selected from the group of fluorhectorite, hydroxyl hectorite, boron fluorphlogopite, hydroxyl boron phlogopite, and solid solutions among those and between those and other structurally-compatible species selected from the group of talc, fluortalc, polylithionite, fluorpolylithionite, phlogopite, and fluorphlogopite, which consists in the steps of: (a) forming a glass-ceramic body containing relatively uniformly-sized crystals consisting essentially of a lithium and/or sodium water-swelling mica selected from the group of fluorhectorite, hydroxyl hectorite, boron fluorphlogopite, hydroxyl boron phlogopite, and solid solutions among those and between those and other structurally-compatible species selected from the group of talc, fluortalc, polylithionite, fluorpolylithionite, phlogopite, and fluorphlogopite; (b) contacting said body with a polar liquid for a time sufficient to cause swelling and disintegration thereof accompanied with the formation of a gel, at least a substantial portion of the crystals in said gel exhibiting a morphology of a continuum of flakes, rectangular-like strips, and interwoven ribbons in parallel or sub-parallel zones or sheaths with said strips and ribbons being about 0.5-10 microns long, about 300 A-5000 A wide, and less than about 100 A thick, and said flakes being irregularly shaped with diameters between about 0.5-10 microns and cross sections of less than about 100 A; and then (c) adjusting the solid:liquid ratio of said gel to a desired fluidity.
Claim 6
Independent Claim
230 words
A method for preparing inorganic gels containing relatively uniformly-sized crystals consisting essentially of a lithium and/or sodium water-swelling mica selected from the group of fluorhectorite, hydroxyl hectorite, boron fluorphlogopite, hydroxyl boron phlogopite, and solid solutions among those and between those and other structurally-compatible species selected from the group of talc, fluortalc, polylithionite, fluorpolylithionite, phlogopite, and fluorphlogopite, which consists in the steps of: (a) forming a glass-ceramic body containing relatively uniformly-sized crystals consisting essentially of a lithium and/or sodium water-swelling mica selected from the group of fluorhectorite, hydroxyl hectorite, boron fluorphlogopite, hydroxyl boron phlogopite, and solid solutions among those and between those and other structurally-compatible species selected from the group of talc, fluortalc, polylithionite, fluorpolylithionite, phlogopite, and fluorphlogopite; (b) contacting said body with a polar liquid for a time sufficient to cause swelling and disintegration thereof accompanied with the formation of a gel, at least a substantial portion of the crystals in said gel exhibiting a morphology of a continuum of flakes, rectangular-like strips, and interwoven ribbons in parallel or sub-parallel zones or sheaths with said strips and ribbons being about 0.5-10 microns long, about 300 A-5000 A wide, and less than about 100 A thick, and said flakes being irregularly shaped with diameters between about 0.5-10 microns and cross sections of less than about 100 A; and then (c) adjusting the solid:liquid ratio of said gel to a desired fluidity.
Claim 7
Dependent Claim
12 words
A method according to claim 4 wherein said polar liquid is water.
Claim 8
Dependent Claim
21 words
A method according to claim 4 wherein said time sufficient to effect swelling, disintegration, and gelation ranges between about 1-48 hours.
Claim 9
Dependent Claim
22 words
A method according to claim 4 wherein the viscosity of said gel is adjusted by adding a deflocculating or peptizing agent thereto.
Claim 10
Dependent Claim
34 words
A method according to claim 4 wherein said gels also contain inert fillers such that the total of the solids portion of said gels and said inert fillers ranges up to 95% by volume.
Claim 11
Dependent Claim
23 words
A method according to claim 8 wherein said fillers are selected from the group of clays, talc, barite, graphite, gypsum, and organic polymers.
References Cited (Backward Citations)
US3586478A
Cited
US3936383A
Cited
US3985531A
Cited
US3985534A
Cited
US4045241A
Cited
US4067819A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-10-26 | 1985-04-27 | 1985-10-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-10-26 | 1989-04-27 | 1989-10-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-10-26 | 1993-04-27 | 1993-10-27 | $7700.00 | Window Closed / Lapsed |