Abstract A method for producing activated catalysts in which a catalyst containing chromium on a silica-containing support is (1) contacted with a gaseous environment consisting essentially of sulfur dioxde and oxygen at a temperature in a range of about 450° C. to about 1100° C. for a time ranging from about one to about five hours and (2) subsequently maintaining a temperature within the contact temperature range while contacting the catalyst with a gaseous environment consisting essentially of oxygen and gases inert to reaction with the catalyst. In another embodiment of the invention the temperature for a succeeding step is not raised above that attained in the previous step. In an embodiment of the invention the catalyst is contacted with a gaseous environment consisting essentially of oxygen and gases inert to reaction with the catalyst while the temperature is being increased prior to contact with sulfur dioxide.
A method for producing an activated catalyst said method comprising: (1) contacting a catalyst comprising chromium on a silica-containing support with a gaseous environment consisting essentially of sulfur dioxide and oxygen at a temperature within a temperature range and for a time sufficient to activate the catalyst and subsequently (2) maintaining a temperature within the contact temperature range of step (1) while contacting said catalyst with a gaseous environment consisting essentially of oxygen and gases inert to reaction with the catalyst.
Claim 2
Independent Claim
81 words
A method for producing an activated catalyst said method comprising: (1) contacting a catalyst comprising chromium on a silica-containing support with a gaseous environment consisting essentially of sulfur dioxide and oxygen at a temperature within a temperature range and for a time sufficient to activate the catalyst and subsequently (2) maintaining a temperature within the contact temperature range of step (1) while contacting said catalyst with a gaseous environment consisting essentially of oxygen and gases inert to reaction with the catalyst.
Claim 3
Dependent Claim
38 words
A method of claim 1 wherein the catalyst is contacted with a gaseous environment consisting essentially of oxygen and gases inert to reaction with the catalyst while the temperature is being increased prior to contact with sulfur dioxide.
Claim 4
Dependent Claim
31 words
A method of claim 1 wherein the catalyst is contacted with a gaseous environment consisting essentially of sulfur dioxide and oxygen while the temperature is being increased to the activation range.
Claim 5
Dependent Claim
23 words
A method of claim 1, 2 or 3 wherein the temperature for step (b) is not raised above that attained in step (a).
Claim 6
Dependent Claim
25 words
A method of claim 1, 2 or 3 wherein the mole ratio of sulfur dioxide:oxygen is in the range of about 1:0.55 to about 1:10.
Claim 7
Dependent Claim
79 words
A method of claim 1, 2 or 3 wherein said gaseous environment consisting essentially of sulfur dioxide and oxygen is within a temperature range of about 450° to about 1100° C. (840° to 2000° F.), the contact time between the gaseous environment of sulfur dioxide and oxygen is in the range of about 1 to about 5 hours, and the total contact time between catalyst and gaseous environment is in the range of about 2 to about 20 hours.
Claim 8
Dependent Claim
34 words
A method of claim 6 wherein the contact between the catalyst and the gaseous environment of sulfur dioxide and oxygen is within a temperature range of about 540° to about 900° C. (1000°-1650° F.).
Claim 9
Dependent Claim
14 words
An activated catalyst produced by the method of claims 1, 2, 3 or 6.