Method for overaging of hot dip metal coated steel material
Assignee: Nippon Steel Nisshin Co Ltd
•
Filing: 1979-09-24
•
Granted: 1981-10-13
•
Expires: 1999-09-24
Abstract
Abstract Method for overaging hot dip metal coated steel material to improve formability, comprising rapidly heating the material to a temperature of above 300° C. but below that at which the coating is undesirably denatured at heating rate of at least 50° C./sec., followed by controlled slow cooling of cooling rate of not more than 20° C./sec. Total processing time required can be one or two minutes, thus the method can be continuously carried out.
Inventors
- 👤 Michio Kubota
- 👤 Kazuhiro Takagi
- 👤 Yorimasa Mitani
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 16:23
CPC Classifications
C; C21; C21D; C21D9/00; C21D9/52
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
147 words
A continuous method for the overaging of a hot dip metal coated steel sheet material to improve the formability of the material, which is hard due to the presence of C and N in the form of supersaturated solid solution, said method comprising the steps of continuously passing the material through a heating zone so as to rapidly heat the material at a rate of heating of at least 50° C./sec. to a temperature above 300° C. but below that at which alloying of the coating with the base steel or formation of additional alloys not already present in the coated material will substantially take place, and continuously passing the heated material through a cooling zone so as to cool the material at a controlled rate of cooling of not more than 20° C./sec. until the supersaturation of C and N in the base steel substantially disappears.
Claim 2
Dependent Claim
147 words
A continuous method for the overaging of a hot dip metal coated steel sheet material to improve the formability of the material, which is hard due to the presence of C and N in the form of supersaturated solid solution, said method comprising the steps of continuously passing the material through a heating zone so as to rapidly heat the material at a rate of heating of at least 50° C./sec. to a temperature above 300° C. but below that at which alloying of the coating with the base steel or formation of additional alloys not already present in the coated material will substantially take place, and continuously passing the heated material through a cooling zone so as to cool the material at a controlled rate of cooling of not more than 20° C./sec. until the supersaturation of C and N in the base steel substantially disappears.
Claim 3
Dependent Claim
30 words
The method in accordance with claim 1 wherein said material is an aluminum coated steel sheet material and is rapidly heated to a temperature of 300° C. to 600° C.
Claim 4
Dependent Claim
31 words
The method in accordance with claim 1 wherein said material is a zinc-iron alloy coated steel sheet material and is rapidly heated to a temperature of 300° C. to 550° C.
Claim 5
Dependent Claim
29 words
The method in accordance with claim 1 wherein said material is a zinc-coated steel sheet material and is rapidly heated to a temperature of 300° C. to 450° C.
Claim 6
Independent Claim
23 words
The method in accordance with any one of the preceding claims wherein said material is internally heated by a high frequency induction technique.
References Cited (Backward Citations)
US4052234A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-10-12 | 1985-04-13 | 1985-10-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-10-12 | 1989-04-13 | 1989-10-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-10-12 | 1993-04-13 | 1993-10-13 | $7700.00 | Window Closed / Lapsed |