Apparatus and process for automatic control of the production of optical fiber
Assignee: Times Fiber Communications Inc
•
Filing: 1979-07-13
•
Granted: 1981-10-13
•
Expires: 1999-07-13
Abstract
Abstract Apparatus and process for automatic control of the production of optical fiber are disclosed. The process comprises continuously depositing and sintering borosilicate glass particles on a fused silica rod or a graded index rod in such a manner that the glass exhibits a uniform, radially increasing concentration of boron. The appropriate boron oxide/silica concentration ratio in the glass particles is controlled by the time of deposit and the weight and diameter of the rod, which are continuously monitored. The concentration of boron oxide and silica in the particulate is likewise continuously monitored to insure that the correct portion of boron oxide/silica is deposited. The apparatus for conducting the process, includes means for continuously monitoring the weight and diameter of the rod and the boron oxide content of the glass particles and means for automatically regulating the equipment used to produce the optical fiber in response to readings from the monitoring means.
Inventors
- 👤 Franklin W. Dabby
- 👤 Ronald B. Chesler
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 14:41
CPC Classifications
C; C03; C03B; C03B37/00; C03B37/01; C03B37/012; C03B37/014; C03B37/01413; C03B37/0148; C03B2201/00; C03B2201/06; C03B2201/08; C03B2201/10; C03B2207/00; C03B2207/50; C03B2207/54; C03B2207/70
Claims Analysis
Total Claims: 23
Claim 1
Independent Claim
93 words
A process for the production of optical fiber comprising preparing a preform by depositing and sintering borosilicate particles on a cylindrical glass rod, heating said preform to the drawing temperature, and drawing said preform into optical fiber, wherein the diameter of the glass rod is continuously monitored during deposition of the borosilicate particles and the composition of said particles is adjusted in response to the diameter measurements such that the particles are uniformly distributed across the length of the rod at the appropriate composition for a given radial distance from the rod axis.
Claim 2
Dependent Claim
93 words
A process for the production of optical fiber comprising preparing a preform by depositing and sintering borosilicate particles on a cylindrical glass rod, heating said preform to the drawing temperature, and drawing said preform into optical fiber, wherein the diameter of the glass rod is continuously monitored during deposition of the borosilicate particles and the composition of said particles is adjusted in response to the diameter measurements such that the particles are uniformly distributed across the length of the rod at the appropriate composition for a given radial distance from the rod axis.
Claim 3
Dependent Claim
38 words
The process as defined by claim 1, wherein the borosilicate particles are continuously sintered after they are deposited so that each layer of borosilicate particles after the first layer is deposited on a previously sintered layer of borosilicate.
Claim 4
Dependent Claim
27 words
The process as defined by claim 1, further comprising continuously monitoring the boron oxide content of the borosilicate particles as they are deposited via infra-red absorption spectrophotometry.
Claim 5
Dependent Claim
26 words
The process as defined by claim 1, further comprising adjusting the translation and/or rotation rates of said cylindrical glass rod in response to said diameter measurements.
Claim 6
Dependent Claim
58 words
The process as defined by claim 1, wherein said borosilicate particles are produced by high temperature pyrolysis of a first gaseous reactant selected from the group consisting of SiH 4 , SiCl 4 and SiBr 4 and a second gaseous reactant selected from the group consisting of B 2 H 6 , BCl 3 and BBr 3 .
Claim 7
Dependent Claim
17 words
The process as defined by claim 5, wherein said reactants are SiCl 4 and BCl 3 .
Claim 8
Dependent Claim
23 words
The process as defined by claim 6, wherein the weight of the glass rod is continuously monitored during deposition of the borosilicate particles.
Claim 9
Dependent Claim
27 words
The process as defined by claim 5, wherein said high temperature pyrolysis is conducted as a flame pyrolysis by burning natural gas in the presence of oxygen.
Claim 10
Independent Claim
111 words
An apparatus for the production of optical fiber comprising means for holding a cylindrical glass start rod and imparting translational and rotational motion thereto, means for producing high temperature pyrolysis of silicon and boron containing gaseous mixtures and directing the particulate product towards the glass start rod, means for continuously monitoring the infra-red absorption spectrophotometry of the particulate produced by the pyrolysis reaction and directed toward the rod, means for continuously monitoring the diameter of the rod and means for co-ordinating and adjusting the flow of the gaseous reactants to the pyrolysis reaction and the translation and/or rotation rates of the rod in response to diameter and infra-red absorption spectrophotometry measurements.
Claim 11
Independent Claim
111 words
An apparatus for the production of optical fiber comprising means for holding a cylindrical glass start rod and imparting translational and rotational motion thereto, means for producing high temperature pyrolysis of silicon and boron containing gaseous mixtures and directing the particulate product towards the glass start rod, means for continuously monitoring the infra-red absorption spectrophotometry of the particulate produced by the pyrolysis reaction and directed toward the rod, means for continuously monitoring the diameter of the rod and means for co-ordinating and adjusting the flow of the gaseous reactants to the pyrolysis reaction and the translation and/or rotation rates of the rod in response to diameter and infra-red absorption spectrophotometry measurements.
Claim 12
Dependent Claim
38 words
The apparatus as defined by claim 9, further comprising means for continuously sintering the particulate after it is deposited so that each layer of particulate after the first layer is deposited on a previously sintered layer of borosilicate.
Claim 13
Dependent Claim
28 words
The apparatus as defined by claim 10, wherein said means for continuously sintering said deposited particles is a furnace which surrounds a portion of said glass start rod.
Claim 14
Dependent Claim
26 words
The apparatus as defined by claim 9, wherein said means for continuously monitoring the diameter of the rod utilizes a laser beam directed at the rod.
Claim 15
Dependent Claim
28 words
The apparatus as defined by claim 9, wherein said means for continuously monitoring the infra-red absorption spectrophotometry of the particulate produced by the pyrolysis reaction comprises a monochromator.
Claim 16
Dependent Claim
47 words
The apparatus as defined by claim 9, wherein said means for coordinating and adjusting the flow of gaseous reactants to the pyrolysis reaction and the translation and/or rotation rates of the rod in response to diameter and infra-red absorption spectrophotometry measurements comprises a high speed digital computer.
Claim 17
Dependent Claim
18 words
The apparatus as defined by claim 9, further comprising means for continuously monitoring the weight of the rod.
Claim 18
Dependent Claim
94 words
In a process for the production of optical fiber comprising preparing a preform by depositing and sintering glass particles on a cylindrical glass rod, heating said preform to the drawing temperature, and drawing said preform into optical fiber, the improvement comprising continuously monitoring the diameter of the glass rod during deposition of the glass particles and adjusting the composition of said particles in response to the diameter measurement such that the particles are uniformly distributed across the length of the rod at the appropriate composition for a given radial distance from the rod axis.
Claim 19
Dependent Claim
94 words
In a process for the production of optical fiber comprising preparing a preform by depositing and sintering glass particles on a cylindrical glass rod, heating said preform to the drawing temperature, and drawing said preform into optical fiber, the improvement comprising continuously monitoring the diameter of the glass rod during deposition of the glass particles and adjusting the composition of said particles in response to the diameter measurement such that the particles are uniformly distributed across the length of the rod at the appropriate composition for a given radial distance from the rod axis.
Claim 20
Dependent Claim
26 words
The process as defined by claim 16, wherein said improvement further comprises continuously monitoring the weight of the glass rod during deposition of the glass particles.
Claim 21
Independent Claim
116 words
An apparatus for the production of optical fiber comprising means for holding a cylindrical glass start rod and imparting translational and rotational motion thereto, means for producing high temperature pyrolysis of gaseous mixtures capable of forming a glass particulate product and for directing said glass particulate product towards the glass start rod, means for continuously monitoring the infra-red absorption spectrophotometry of the particulate produced by the pyrolysis reaction and directed toward the rod, means for continuously monitoring the diameter of the rod, and means for co-ordinating and adjusting the flow of the gaseous reactants to the pyrolysis reaction and the translation and/or rotation rates of the rod in response to diameter and infra-red absorption spectrophotometry measurements.
Claim 22
Independent Claim
116 words
An apparatus for the production of optical fiber comprising means for holding a cylindrical glass start rod and imparting translational and rotational motion thereto, means for producing high temperature pyrolysis of gaseous mixtures capable of forming a glass particulate product and for directing said glass particulate product towards the glass start rod, means for continuously monitoring the infra-red absorption spectrophotometry of the particulate produced by the pyrolysis reaction and directed toward the rod, means for continuously monitoring the diameter of the rod, and means for co-ordinating and adjusting the flow of the gaseous reactants to the pyrolysis reaction and the translation and/or rotation rates of the rod in response to diameter and infra-red absorption spectrophotometry measurements.
Claim 23
Dependent Claim
18 words
The apparatus as defined by claim 18, further comprising means for continuously monitoring the weight of the rod.
References Cited (Backward Citations)
US3765774A
Cited
US3879128A
Cited
US3957474A
Cited
US3982816A
Cited
US3932160A
Cited
US4046536A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-10-12 | 1985-04-13 | 1985-10-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-10-12 | 1989-04-13 | 1989-10-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-10-12 | 1993-04-13 | 1993-10-13 | $7700.00 | Window Closed / Lapsed |