Abstract
Abstract The present invention resides broadly in a method for the preparation of paper having improved water and/or solvent resistance which comprises applying to a base paper a plastic particle containing formulation, and then wetting the formed coating with a solvent to which the plastic particles are sensitive. The present invention is particularly applicable to the preparation of electrostatic paper masters of improved water resistance for lithographic printing having a photoconductive layer and a barrier coat to which the photoconductive layer is applied. The barrier coat contains a binding amount of a binder resin and filler at least a portion of which is an amount of said plastic particles sensitive to the solvent system of the photoconductive layer, the amount of plastic particles and sensitivity being sufficient to materially increase water resistance.
Inventors
- 👤 Michael J. Shaw
- 👤 Robert J. Thiessen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-10 01:45
CPC Classifications
G; G03; G03G; G03G5/00; G03G5/14; G03G5/142; G03G5/10; G03G5/101; G03G5/144; Y; Y10; Y10S; Y10S430/00; Y10S430/131; Y10S430/162; Y10T; Y10T428/00; Y10T428/25; Y10T428/254; Y10T428/26; Y10T428/263; Y10T428/264; Y10T428/265; Y10T428/27; Y10T428/273; Y10T428/277
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
84 words
An electrostatic master having improved water resistance for lighographic printing comprising a base; a barrier coat; and a photoconductive layer containing a photoconductive material and a binder; said barrier coat comprising a binding amount of a natural or synthetic binder and a filler at least a portion of which is an amount of plastic polymeric particles sensitive to the solvent used in the application of the photoconductive layer, said plastic polymeric particles being in an at least partially coalesced state in said barrier coat.
Claim 2
Dependent Claim
84 words
An electrostatic master having improved water resistance for lighographic printing comprising a base; a barrier coat; and a photoconductive layer containing a photoconductive material and a binder; said barrier coat comprising a binding amount of a natural or synthetic binder and a filler at least a portion of which is an amount of plastic polymeric particles sensitive to the solvent used in the application of the photoconductive layer, said plastic polymeric particles being in an at least partially coalesced state in said barrier coat.
Claim 3
Dependent Claim
19 words
The master of claim 1 wherein said plastic polymeric particles comprise about 10 to 100% of the filler content.
Claim 4
Dependent Claim
21 words
The master of claim 2 wherein said plastic polymeric particles have an average particle size of about 0.01 to 20.0 microns.
Claim 5
Dependent Claim
25 words
The master of claim 3 wherein said binder is present in an amount of about 10 to 40% based on the total weight of filler.
Claim 6
Dependent Claim
20 words
The master of claim 4 wherein said plastic polymeric particles are a material which is water repellent and water insensitive.
Claim 7
Dependent Claim
41 words
The master of claim 5 wherein said plastic polymeric particles are a material selected from the group consisting of polystyrene, polyvinyl acetate and copolymers thereof, polyvinyl butyral and copolymers thereof, polyacrylates and copolymers thereof, and mixtures of any of the above.
Claim 8
Independent Claim
140 words
A method for the preparation of electrostatic masters having improved water resistance for lithographic printing comprising the steps of; (a) applying to a base a barrier coat comprising a binding amount of a natural or synthetic binder and a filler at least a portion of which is an amount of plastic polymeric particles; (b) drying the formed barrier coat, said plastic polymeric particles being in a non-coalesced state at time of application and non-film forming under the conditions of application and drying of the coating; and (c) applying to said barrier coat a photoconductive coating comprising a photoconductive material in a binder and solvent, the plastic polymeric particles of the barrier coat being sensitive to said solvent; (d) the amount of plastic polymeric particles and sensitivity to the solvent of the photoconductive layer being sufficient to materially increase water resistance.
Claim 9
Independent Claim
140 words
A method for the preparation of electrostatic masters having improved water resistance for lithographic printing comprising the steps of; (a) applying to a base a barrier coat comprising a binding amount of a natural or synthetic binder and a filler at least a portion of which is an amount of plastic polymeric particles; (b) drying the formed barrier coat, said plastic polymeric particles being in a non-coalesced state at time of application and non-film forming under the conditions of application and drying of the coating; and (c) applying to said barrier coat a photoconductive coating comprising a photoconductive material in a binder and solvent, the plastic polymeric particles of the barrier coat being sensitive to said solvent; (d) the amount of plastic polymeric particles and sensitivity to the solvent of the photoconductive layer being sufficient to materially increase water resistance.
Claim 10
Dependent Claim
19 words
The method of claim 7 wherein said plastic polymeric particles comprise about 10 to 100% of the filler content.
Claim 11
Dependent Claim
21 words
The method of claim 8 wherein said plastic polymeric particles have an average particle size of about 0.01 to 20.0 microns.
Claim 12
Dependent Claim
25 words
The method of claim 9 wherein said binder is present in an amount of about 10 to 40% based on the total weight of filler.
Claim 13
Dependent Claim
20 words
The method of claim 10 wherein said plastic polymeric particles are a material which is water repellent and water insensitive.
Claim 14
Dependent Claim
35 words
The method of claim 11 wherein said plastic polymeric particles are a material selected from the group consisting of polystyrene, polyvinyl acetate and copolymers thereof, polyvinyl butyral and copolymers thereof, and polyacrylates and copolymers thereof.
Claim 15
Dependent Claim
16 words
The method of claim 7 wherein said binder is styrene-butadiene having a low level of carboxylation.
Claim 16
Dependent Claim
29 words
The method of claim 7 wherein said solvent of the photoconductive layer is a compound selected from the group consisting of toluene, benzene, xylene, chlorinated aliphatic compounds and ketones.
Claim 17
Dependent Claim
20 words
The method of claim 7 wherein said barrier coat is applied in an amount sufficient to materially increase water resistance.
Claim 18
Dependent Claim
31 words
The method of claim 15 wherein said barrier coat is applied in an amount sufficient to achieve a 4 to 90-fold increase in water resistance as measured by the Cobb test.
Claim 19
Independent Claim
180 words
A method for the preparation of electrostatic masters having improved water resistance for lithographic printing comprising the steps of; (a) applying to a base a barrier coat comprising a binding amount of a natural or synthetic binder and a filler 10-100% of which are plastic polymeric particles of a material selected from the group consisting of polystyrene, polyvinyl acetate and copolymers thereof, polyvinyl butyral and copolymers thereof and polyacrylates and copolymers thereof, said plastic polymeric particles having an average particle size of about 0.01 to 20.0 microns, said binder being present in an amount of about 10 to 40% based on the total weight of filler; (b) drying the formed barrier coat, said plastic polymeric particles being in a non-coalesced state at time of application and non-film forming under the conditions of application and drying of the coating; and (c) applying to said barrier coat a photoconductive coating comprising a photoconductive material in a binder and solvent, the plastic polymeric particles of the barrier coat being sufficiently sensitive to said solvent as to obtain a material increase in water resistance.
Claim 20
Independent Claim
180 words
A method for the preparation of electrostatic masters having improved water resistance for lithographic printing comprising the steps of; (a) applying to a base a barrier coat comprising a binding amount of a natural or synthetic binder and a filler 10-100% of which are plastic polymeric particles of a material selected from the group consisting of polystyrene, polyvinyl acetate and copolymers thereof, polyvinyl butyral and copolymers thereof and polyacrylates and copolymers thereof, said plastic polymeric particles having an average particle size of about 0.01 to 20.0 microns, said binder being present in an amount of about 10 to 40% based on the total weight of filler; (b) drying the formed barrier coat, said plastic polymeric particles being in a non-coalesced state at time of application and non-film forming under the conditions of application and drying of the coating; and (c) applying to said barrier coat a photoconductive coating comprising a photoconductive material in a binder and solvent, the plastic polymeric particles of the barrier coat being sufficiently sensitive to said solvent as to obtain a material increase in water resistance.
Claim 21
Dependent Claim
16 words
The method of claim 17 wherein said binder is styrene-butadiene having a low level of carboxylation.
Claim 22
Independent Claim
138 words
A method for the preparation of electrostatic masters having improved water resistance for lithographic printing comprising the steps of; (a) applying to a base a barrier coat comprising a binding amount of a natural or synthetic binder and a filler at least a portion of which is an amount of plastic polymeric particles; (b) drying the formed barrier coat, said plastic polymeric particles being in a non-coalesced state at time of application and non-film forming under the conditions of application and drying of the coating; (c) wetting the formed barrier coating with a solvent to which the plastic polymeric particles are sensitive, the amount of plastic polymeric particles and sensitivity to the solvent being sufficient to materially increase water resistance; and (d) then applying to said barrier coat a photoconductive coating comprising a photoconductive material in a binder.
Claim 23
Independent Claim
138 words
A method for the preparation of electrostatic masters having improved water resistance for lithographic printing comprising the steps of; (a) applying to a base a barrier coat comprising a binding amount of a natural or synthetic binder and a filler at least a portion of which is an amount of plastic polymeric particles; (b) drying the formed barrier coat, said plastic polymeric particles being in a non-coalesced state at time of application and non-film forming under the conditions of application and drying of the coating; (c) wetting the formed barrier coating with a solvent to which the plastic polymeric particles are sensitive, the amount of plastic polymeric particles and sensitivity to the solvent being sufficient to materially increase water resistance; and (d) then applying to said barrier coat a photoconductive coating comprising a photoconductive material in a binder.
Claim 24
Dependent Claim
23 words
The method of claim 19 which includes the step of drying the formed coating of step (a) prior to wetting with a solvent.
Claim 25
Dependent Claim
22 words
The method of claim 20 wherein the formed coating from step (a) is calendered prior to and/or after wetting with a solvent.
References Cited (Backward Citations)
US2764085A
Cited
US3083637A
Cited
US3281267A
Cited
US3298831A
Cited
US3653894A
Cited
US3779800A
Cited
US3787235A
Cited
US3839033A
Cited
US3968319A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-10-05 | 1985-04-06 | 1985-10-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-10-05 | 1989-04-06 | 1989-10-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-10-05 | 1993-04-06 | 1993-10-06 | $7700.00 | Window Closed / Lapsed |