Process of producing reinforced laminates from crosslinkable thermoplastic olefin polymer material

Claim 2

A process of producing reinforced laminates from crosslinkable thermoplastic olefin polymer material, comprising the steps of heating a normally solid, high molecular weight crosslinkable thermoplastic olefin polymer selected from the group consisting of ethylene homopolymers, copolymers of ethylene and at least one acyclic mono-1 olefin hydrocarbon having 2 to 8 carbon atoms per molecule, and mixtures thereof, having a melt index of at least about 10, and a density in the range of 0.910 to 0.970 and containing an acetylenic diperoxy catalyst which reacts with and effects crosslinking of said polymer and which has a decomposition temperature between about 310° F. and about 525° F., to a molten state at a melting temperature between about 270° F. and 300° F., forming a continuous non-reinforced sheet from said molten polymer at a temperature below said decomposition temperature, cooling said continuous sheet to a temperature below said melting temperature to a self-supporting, two-dimensional molecular state, combining said sheet in said self-supporting state with a glass fibrous substrate treated with an unsaturated organosilanol coupling agent which reacts with said polymer and said glass fibrous substrate and effects bonding of said polymer to said substrate to form a laminate, heating said laminate under pressure to a temperature between about 310° F. and about 525° F. to react said catalyst with said polymer and effect at least 80% crosslinking of said polymer to a three-dimensional molecular state, and cooling said laminate to a temperature below said melting temperature to a self-supporting state.

Claim 3

The process recited in claim 1, wherein said polymer contains a thiodipropionate acid ester flame-retardant and said catalyst.

Claim 4

The process recited in claim 2, wherein said flame-retardant comprises dilaurylthiodipropionate.

Claim 5

The process recited in claim 1, wherein said catalyst comprises 2,5 dimethyl 2,5-di(t-butylperoxy)hexyne-3.

Claim 6

The process recited in claim 1, further comprising the steps of cutting and shaping said laminate subsequent to said step of combining and prior to said step of heating said laminate.

Claim 7

The process recited in claim 1, wherein said step of forming comprises extruding said molten polymer at a temperature between about 270° F. and about 300° F. to form a continuous sheet from said polymer.

Claim 8

The process recited in claim 1, wherein said step of forming comprises extruding said molten polymer at a temperature between about 270° F. and 300° F. to form a tube closed at one end thereof, blowing air into said tube under pressure from the other end thereof to expand said tube and form an elongated tube having a predetermined wall thickness, flattening said elongated tube, slitting said flattened tube along at least one side thereof so as to form a continuous sheet from said polymer.

Claim 9

The process recited in claim 7, wherein said step of slitting comprises slitting said flattened tube along one side thereof and laying said tube flat so as to form a continuous sheet from said polymer.

Claim 10

The process recited in claim 7, wherein said step of slitting comprises slitting said flattened tube along both sides thereof so as to form a continuous sheet from said polymer.

Claim 11

The process recited in claim 1, wherein said step of heating comprises heating said laminate under pressure to a temperature between about 310° F. and about 525° F. to react said catalyst with said polymer and effect about 95% crosslinking of said polymer.

Claim 12

The process recited in claim 1, further comprising the steps of cutting and shaping said laminate and superposing a plurality of said laminates subsequent to said step of combining and prior to said step of heating said laminate, and wherein said step of heating said laminate comprises heating said superposed laminates under pressure to a temperature between about 310° F. and about 525° F. to react said catalyst with said polymer and effect at least 80% crosslinking of said polymer to a three-dimensional molecular state and combine said plurality of superposed laminates.

Claim 13

The process recited in claim 11, further comprising the step of combining a sheet of metallic foil with said laminate subsequent to said steps of cutting and shaping and prior to said step of heating said laminate.

Claim 14

The process recited in claim 12, wherein said step of combining said sheet of metallic foil with said laminate comprises combining a sheet of copper foil with said laminate.

Claim 15

The process recited in claim 1, further comprising the step of combining a sheet of metallic foil with said laminate subsequent to said step of combining said continuous sheet with said substrate and prior to said step of heating said laminate.

Claim 16

The process recited in claim 14, wherein said step of combining said sheet of metallic foil with said laminate comprises combining a sheet of copper foil with said laminate.

Claim 17

The process recited in claim 1, wherein said coupling agent comprises gamma-methacryloxypropyltrimethoxy silane.

Claim 18

A process of producing reinforced laminates from crosslinkable thermoplastic olefin polymer material, comprising the steps of heating a normally solid, high molecular weight crosslinkable thermoplastic olefin polymer selected from the group consisting of ethylene homopolymers, copolymers of ethylene and at least one acyclic mono-1 olefin hydrocarbon having 2 to 8 carbon atoms per molecule, and mixtures thereof, having a melt index of at least about 10, and a density in the range of 0.910 to 0.970 and containing an acetylenic diperoxy catalyst which reacts with and effects crosslinking of said polymer and which has a decomposition temperature between about 310° F. and about 525° F., to a molten state at a melting temperature between about 270° F. and 300° F., forming a continuous non-reinforced sheet in a two-dimensional molecular state from said molten polymer at a temperature below said decomposition temperature, applying said continuous sheet to a glass fibrous substrate treated with an unsaturated organosilanol coupling agent which reacts with said polymer and said glass fibrous substrate and effects bonding of said polymer to said substrate under pressure at a temperature above said melting temperature to form a continuous laminate, heating said laminate to a temperature between about 310° F. and about 525° F. to react said catalyst with said polymer and effect at least 80% crosslinking of said polymer to a three-dimensional molecular state, and cooling said laminate to a temperature below said melting temperature to a self-supporting state.

Claim 19

A process of producing reinforced laminates from crosslinkable thermoplastic olefin polymer material, comprising the steps of heating a normally solid, high molecular weight crosslinkable thermoplastic olefin polymer selected from the group consisting of ethylene homopolymers, copolymers of ethylene and at least one acyclic mono-1 olefin hydrocarbon having 2 to 8 carbon atoms per molecule, and mixtures thereof, having a melt index of at least about 10, and a density in the range of 0.910 to 0.970 and containing an acetylenic diperoxy catalyst which reacts with and effects crosslinking of said polymer and which has a decomposition temperature between about 310° F. and about 525° F., to a molten state at a melting temperature between about 270° F. and 300° F., forming a continuous non-reinforced sheet in a two-dimensional molecular state from said molten polymer at a temperature below said decomposition temperature, applying said continuous sheet to a glass fibrous substrate treated with an unsaturated organosilanol coupling agent which reacts with said polymer and said glass fibrous substrate and effects bonding of said polymer to said substrate under pressure at a temperature above said melting temperature to form a continuous laminate, heating said laminate to a temperature between about 310° F. and about 525° F. to react said catalyst with said polymer and effect at least 80% crosslinking of said polymer to a three-dimensional molecular state, and cooling said laminate to a temperature below said melting temperature to a self-supporting state.

Claim 20

The process recited in claim 17, wherein said catalyst comprises 2,5 dimethyl 2,5-di(t-butylperoxy) hexyne-3.

Claim 21

The process recited in claim 17, wherein said step of forming comprises extruding said molten polymer at a temperature between about 270° F. and about 300° F. to form a continuous sheet from said polymer.

Claim 22

The process recited in claim 17, wherein said step of heating comprises heating said laminate under pressure to a temperature between about 310° F. and 525° F. to react said catalyst with said polymer and effect about 95% crosslinking of said polymer.

Claim 23

The process recited in claim 17, wherein said step of applying comprises applying said continuous sheet under pressure to a glass fibrous substrate at a temperature of at least 270° F. to cause said sheet to impregnate said glass fibrous substrate and form a continuous laminate.

Claim 24

The process recited in claim 17, wherein said coupling agent comprises gamma-methacryloxypropyltrimethoxy silane.

Claim 25

The process recited in claim 17, wherein said step of forming comprises extruding said molten polymer at a temperature between about 270° F. and 300° F. to form a tube closed at one end thereof, blowing air into said tube from the other end thereof under pressure to expand said tube and form an elongated tube having a predetermined wall thickness, flattening said elongated tube, and slitting said flattened tube along at least one side thereof so as to form a continuous sheet from said polymer.

Claim 26

The process recited in claim 23, wherein said step of slitting comprises slitting said flattened tube along one side thereof and laying said tube flat so as to form a continuous sheet from said polymer.

Claim 27

The process recited in claim 23, wherein said step of slitting comprises slitting said flattened tube along both sides thereof so as to form a continuous sheet from said polymer.

Claim 28

The process recited in claim 17, further comprising the step of applying a sheet of metallic foil to at least one surface of said laminate subsequent to said step of applying and prior to said step of heating said laminate.

Claim 29

The process recited in claim 26, wherein said step of applying said sheet of metallic foil comprises applying a sheet of copper foil to at least one surface of said laminate.

Claim 30

The process recited in claim 17, wherein said polymer contains a thiodipropionate acid ester flame-retardant and said catalyst.

Claim 31

The process recited in claim 28, wherein said flame-retardant comprises dilaurylthiodipropionate.

Claim 32

A process of producing reinforced laminates from crosslinkable thermoplastic olefin polymer material, comprising the steps of heating a normally solid, high molecular weight crosslinkable thermoplastic olefin polymer selected from the group consisting of ethylene homopolymers, copolymers of ethylene and at least one acyclic mono-1 olefin hydrocarbon having 2 to 8 carbon atoms per molecule, and mixtures thereof, having a melt index of at least about 10, and a density in the range of 0.910 to 0.970 and containing an acetylenic diperoxy catalyst which reacts with and effects crosslinking of said polymer and which has a decomposition temperature between about 310° F. and 525° F., to a molten state at a melting temperature between about 270° F. and 300° F., forming a continuous non-reinforced sheet in a two-dimensional molecular state from said molten polymer at a temperature below said decomposition temperature, applying said continuous sheet to a glass fibrous substrate treated with an unsaturated organosilanol coupling agent which reacts with said polymer and said glass fibrous substrate and effects bonding of said polymer to said substrate at a temperature above said melting temperature to form a continuous laminate, cooling said laminate to a temperature below said melting temperature to a self-supporting state, heating said laminate under pressure to a temperature between about 310° F. and about 525° F. to react said catalyst with said polymer and effect at least 80% crosslinking of said polymer to a three-dimensional molecular state, and cooling said heated laminate to a temperature below said melting temperature to a self-supporting state.

Claim 33

A process of producing reinforced laminates from crosslinkable thermoplastic olefin polymer material, comprising the steps of heating a normally solid, high molecular weight crosslinkable thermoplastic olefin polymer selected from the group consisting of ethylene homopolymers, copolymers of ethylene and at least one acyclic mono-1 olefin hydrocarbon having 2 to 8 carbon atoms per molecule, and mixtures thereof, having a melt index of at least about 10, and a density in the range of 0.910 to 0.970 and containing an acetylenic diperoxy catalyst which reacts with and effects crosslinking of said polymer and which has a decomposition temperature between about 310° F. and 525° F., to a molten state at a melting temperature between about 270° F. and 300° F., forming a continuous non-reinforced sheet in a two-dimensional molecular state from said molten polymer at a temperature below said decomposition temperature, applying said continuous sheet to a glass fibrous substrate treated with an unsaturated organosilanol coupling agent which reacts with said polymer and said glass fibrous substrate and effects bonding of said polymer to said substrate at a temperature above said melting temperature to form a continuous laminate, cooling said laminate to a temperature below said melting temperature to a self-supporting state, heating said laminate under pressure to a temperature between about 310° F. and about 525° F. to react said catalyst with said polymer and effect at least 80% crosslinking of said polymer to a three-dimensional molecular state, and cooling said heated laminate to a temperature below said melting temperature to a self-supporting state.

Claim 34

The process recited in claim 30, wherein said catalyst comprises 2,5 dimethyl 2,5-di(t-butylperoxy) hexyne-3.

Claim 35

The process recited in claim 30, wherein said step of forming comprises extruding said molten polymer at a temperature between about 270° F. and about 300° F. to form a continuous sheet from said polymer.

Claim 36

The process recited in claim 30, wherein said step of heating comprises heating said laminate under pressure to a temperature between about 310° F. and 525° F. to react said catalyst with said polymer and effect about 95% crosslinking of said polymer.

Claim 37

The process recited in claim 30, wherein said step of applying comprises applying said continuous sheet under pressure to a glass fibrous substrate at a temperature of at least 270° F. to cause said sheet to impregnate said glass fibrous substrate and form a continuous laminate.

Claim 38

The process recited in claim 30, wherein said coupling agent comprises gamma-methacryloxypropyltrimethoxy silane.

Claim 39

The process recited in claim 30, further comprising the steps of cutting and shaping said laminate subsequent to said step of cooling said laminate and prior to said step of heating said laminate.

Claim 40

The process recited in claim 30, wherein said step of forming comprises extruding said molten polymer at a temperature between about 270° F. and 300° F. to form a tube closed at one end thereof, blowing air into said tube from the other end thereof under pressure to expand said tube and form an elongated tube having a predetermined wall thickness, flattening said elongated tube, and slitting said flattened tube along at least one side thereof so as to form a continuous sheet from said polymer.

Claim 41

The process recited in claim 37, wherein said step of slitting comprises slitting said flattened tube along one side thereof and laying said tube flat so as to form a continuous sheet from said polymer.

Claim 42

The process recited in claim 37, wherein said step of slitting comprises slitting said flattened tube along both sides thereof so as to form a continuous sheet from said polymer.

Claim 43

The process recited in claim 30, further comprising the step of applying a sheet of metallic foil to at least one surface of said laminate subsequent to said step of applying and prior to said step of heating said laminate.

Claim 44

The process recited in claim 40, wherein said step of applying said sheet of metallic foil comprises applying a sheet of copper foil to at least one surface of said laminate.

Claim 45

The process recited in claim 30, wherein said polymer contains a thiodipropionate acid ester flame-retardant and said catalyst.

Claim 46

The process recited in claim 42, wherein said flame-retardant comprises dilaurylthiodipropionate.

Claim 47

The process recited in claim 30, further comprising the steps of cutting and shaping said laminate and superposing a plurality of said laminates subsequent to said step of cooling said laminate and prior to said step of heating said laminate, and wherein said step of heating said laminate comprises heating said superposed laminates under pressure to a temperature between about 310° F. and about 525° F. to react said catalyst with said polymer and effect at least 80% crosslinking of said polymer to a three-dimensional molecular state and combine said plurality of superposed laminates.

Claim 48

The process recited in claim 44, further comprising the step of applying a sheet of metallic foil to at least one surface of said laminate subsequent to said steps of cutting and shaping and prior to said step of heating said laminate.

Claim 49

The process recited in claim 45, wherein said step of applying said sheet of metallic foil comprises applying a sheet of copper foil to at least one surface of said laminate.

Claim 50

The process of producing reinforced laminates from crosslinkable thermoplastic olefin polymer material, comprising the steps of heating a normally solid, high molecular weight crosslinkable thermoplastic olefin polymer selected from the group consisting of ethylene homopolymers, copolymers of ethylene and at least one acyclic mono-1 olefin hydrocarbon having 2 to 8 carbon atoms per molecule, and mixtures thereof, having a melt index of at least about 10, and a density in the range of 0.910 to 0.970, and containing dilaurylthiodipropionate as a flame-retardant and 2,5 dimethyl 2,5-di(t-butylperoxy)hexyne-3 as a catalyst to a molten state at a temperature between about 270° F. and 300° F., extruding said molten polymer at a temperature between about 270° F. and about 300° F. to form a continuous non-reinforced sheet in a two-dimensional molecular state from said polymer, applying said continuous sheet under pressure at a temperature between about 270° F. and about 300° F. to a glass fibrous substrate treated with a gamma-methacryloxypropyltrimethoxy silane coupling agent which reacts with said polymer and said glass fibrous substrate and effects bonding of said sheet to said substrate to form a laminate, heating said laminate under pressure to a temperature between about 310° F. and about 525° F. to effect about 95% crosslinking of said polymer to a three-dimensional molecular state, and cooling said heated laminate to a temperature below 270° F. to a self-supporting state.

Claim 51

The process of producing reinforced laminates from crosslinkable thermoplastic olefin polymer material, comprising the steps of heating a normally solid, high molecular weight crosslinkable thermoplastic olefin polymer selected from the group consisting of ethylene homopolymers, copolymers of ethylene and at least one acyclic mono-1 olefin hydrocarbon having 2 to 8 carbon atoms per molecule, and mixtures thereof, having a melt index of at least about 10, and a density in the range of 0.910 to 0.970, and containing dilaurylthiodipropionate as a flame-retardant and 2,5 dimethyl 2,5-di(t-butylperoxy)hexyne-3 as a catalyst to a molten state at a temperature between about 270° F. and 300° F., extruding said molten polymer at a temperature between about 270° F. and about 300° F. to form a continuous non-reinforced sheet in a two-dimensional molecular state from said polymer, applying said continuous sheet under pressure at a temperature between about 270° F. and about 300° F. to a glass fibrous substrate treated with a gamma-methacryloxypropyltrimethoxy silane coupling agent which reacts with said polymer and said glass fibrous substrate and effects bonding of said sheet to said substrate to form a laminate, heating said laminate under pressure to a temperature between about 310° F. and about 525° F. to effect about 95% crosslinking of said polymer to a three-dimensional molecular state, and cooling said heated laminate to a temperature below 270° F. to a self-supporting state.

Claim 52

The process recited in claim 47, further comprising the step of applying a sheet of metallic foil to at least one surface of said laminate subsequent to said step of applying and prior to said step of heating said laminate.

Claim 53

The process recited in claim 48, wherein said step of applying said sheet of metallic foil comprises applying a sheet of copper foil to at least one surface of said laminate.

Claim 54

The process recited in claim 49, further comprising the step of cooling said laminate to a temperature below said melting temperature to a self-supporting state subsequent to said step of applying and prior to said step of heating said laminate, and wherein said step of applying comprises applying said continuous sheet to said glass fibrous substrate to form a continuous laminate.

Claim 55

The process recited in claim 50, further comprising the steps of cutting and shaping said laminate subsequent to said step of cooling said laminate and prior to said step of heating said laminate.

Claim 56

The process recited in claim 50, further comprising the steps of cutting and shaping said laminate and superposing a plurality of said laminates subsequent to said step of cooling said laminate and prior to said step of heating said laminate, and wherein said step of heating said laminate comprises heating said superposed laminates under pressure to a temperature between about 310° F. and about 525° F. to effect said crosslinking of said polymer to a three-dimensional molecular state and combine said plurality of superposed laminates.

Claim 57

The process recited in claim 52, further comprising the step of applying a sheet of metallic foil to at least one surface of said laminate subsequent to said steps of cutting and shaping and prior to said step of heating said laminate.

Claim 58

The process recited in claim 53, wherein said step of applying said sheet of metallic foil comprises applying a sheet of copper foil to at least one surface of said laminate.

Claim 59

The process recited in claim 47, wherein said step of extruding comprises extruding said molten polymer at a temperature between about 270° F. and 300° F. to form a tube closed at one end thereof, blowing air into said tube from the other end thereof under pressure to expand said tube and form an elongated tube having a predetermined wall thickness, flattening said elongated tube, and slitting said elongated tube along at least one side thereof so as to form a continuous sheet from said polymer.

Claim 60

The process recited in claim 55, wherein said step of slitting comprises slitting said flattened tube along one side thereof and laying said tube flat so as to form a continuous sheet from said polymer.

Claim 61

The process recited in claim 55, wherein said step of slitting comprises slitting said flattened tube along both sides thereof so as to form a continuous sheet from said polymer.