Patent US4291470A successfully refreshed from Google Patents.
US4291470A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for preshrinking semipermeable membranes
Assignee: Baxter International Inc
•
Filing: 1979-05-25
•
Granted: 1981-09-29
•
Expires: 1999-05-25
Abstract
Abstract A method of preshrinking a semipermeable membrane or blood bag of the type used in an artificial-kidney coil dialyzer, so as to prevent or minimize shrinkage of the membrane during sterilization of the dialyzer. The preshrinking method of the present invention includes the steps of passing the membrane through a humidity chamber in a free-hanging state and then into a warm air drying chamber. The amount of membrane shrinkage can be controlled by varying the residence time, the temperature and the humidity of the chamber. By preshrinking the membrane to approximate the amount of shrinkage which normally occurs during the sterilization, substantially all shrinkage during sterilization is eliminated.
Inventors
- 👤 Ferris E. Newman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 16:19
CPC Classifications
B; B01; B01D; B01D67/00; B01D67/0081; B01D67/0095; A; A61; A61L; A61L2/00; A61L2/16; A61L2/20; A61L2/206; B01D65/00; B01D65/02; B01D65/022; B01D2321/00; B01D2321/08
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
93 words
A method of treating cellulose semi-permeable membranes, of the type used in coil dialyzers, so as to minimize shrinkage of the membrane during sterilization of the dialyzer, the method including the steps of: providing a supply of cellulose semi-permeable membrane material; transporting said material from said supply through a humidity chamber maintained at a very high relative humidity, at a temperature and for a time effective to permit said material to relax; and passing said material into a drying chamber in which warm air is circulated for permitting the membrane material to shrink.
Claim 2
Independent Claim
93 words
A method of treating cellulose semi-permeable membranes, of the type used in coil dialyzers, so as to minimize shrinkage of the membrane during sterilization of the dialyzer, the method including the steps of: providing a supply of cellulose semi-permeable membrane material; transporting said material from said supply through a humidity chamber maintained at a very high relative humidity, at a temperature and for a time effective to permit said material to relax; and passing said material into a drying chamber in which warm air is circulated for permitting the membrane material to shrink.
Claim 3
Dependent Claim
19 words
A method as in claim 1, wherein the relative humidity of the humidity chamber is maintained between about 80%-100%.
Claim 4
Dependent Claim
15 words
A method as in claim 2, wherein the relative humidity is maintained at about 100%.
Claim 5
Dependent Claim
25 words
A method as in claim 1, wherein the temperature in the humidity chamber is maintained at a value between about 70° F. and 212° F.
Claim 6
Dependent Claim
18 words
A method as in claim 4, wherein the temperature is maintained between about 150° F. and 212° F.
Claim 7
Dependent Claim
19 words
A method as in claim 1, wherein the time of treatment is between about 3 seconds and 70 hours.
Claim 8
Dependent Claim
19 words
A method as in claim 6, wherein the time of treatment is between about 3 seconds and 10 minutes.
Claim 9
Dependent Claim
16 words
A method as in claim 1, wherein said chamber includes a volatile liquid which is water.
Claim 10
Independent Claim
123 words
A method of treating cellulose semi-permeable membranes, of the type used in coil dialyzers, so as to minimize shrinkage of the membrane during sterilization of the dialyzer, the method including the steps of: providing a supply of cellulose semipermeable membrane material; transporting said material from said supply through a humidity chamber maintained at a very high relative humidity, at a temperature and for a time effective to permit said material to relax; passing said material into a drying chamber in which warm air is circulated for permitting the membrane material to shrink; and wherein said humidity chamber includes a volatile liquid having between 50%-100% water and up to 50% of a liquid selected from the group ethyl alcohol, trichlorethylene, ethyl acetate and cyclohexane.
Claim 11
Independent Claim
123 words
A method of treating cellulose semi-permeable membranes, of the type used in coil dialyzers, so as to minimize shrinkage of the membrane during sterilization of the dialyzer, the method including the steps of: providing a supply of cellulose semipermeable membrane material; transporting said material from said supply through a humidity chamber maintained at a very high relative humidity, at a temperature and for a time effective to permit said material to relax; passing said material into a drying chamber in which warm air is circulated for permitting the membrane material to shrink; and wherein said humidity chamber includes a volatile liquid having between 50%-100% water and up to 50% of a liquid selected from the group ethyl alcohol, trichlorethylene, ethyl acetate and cyclohexane.
Claim 12
Independent Claim
84 words
A method of pretreating regenerated cellulose semipermeable membranes of the type used in coil dialyzers so as to prevent shrinkage during subsequent sterilization, the method including the steps of: providing a supply of regenerated cellulose semi-permeable membrane material; transporting said material through a treatment chamber maintained at about 100% relative humidity and at a temperature between about 150° F.-212° F. for a time between 3 seconds and 10 minutes; and thereafter passing said material into a drying chamber in which warm air is circulated.
Claim 13
Independent Claim
84 words
A method of pretreating regenerated cellulose semipermeable membranes of the type used in coil dialyzers so as to prevent shrinkage during subsequent sterilization, the method including the steps of: providing a supply of regenerated cellulose semi-permeable membrane material; transporting said material through a treatment chamber maintained at about 100% relative humidity and at a temperature between about 150° F.-212° F. for a time between 3 seconds and 10 minutes; and thereafter passing said material into a drying chamber in which warm air is circulated.
References Cited (Backward Citations)
US1482717A
Cited
US2062193A
Cited
US2254200A
Cited
US2364467A
Cited
US2459345A
Cited
US2770053A
Cited
US2934400A
Cited
US3684553A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-09-28 | 1985-03-30 | 1985-09-29 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-09-28 | 1989-03-30 | 1989-09-29 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-09-28 | 1993-03-30 | 1993-09-29 | $7700.00 | Window Closed / Lapsed |