Method of depositing uniform films of Six Ny or Six Oy in a plasma reactor
Assignee: AT&T Inc
•
Filing: 1979-10-11
•
Granted: 1981-09-15
•
Expires: 1999-10-11
Abstract
Abstract A method of depositing a uniform dielectric film on a silicon substrate comprising flowing a plasma comprising an RF-excited mixture of an inert gas such as argon and silane over the substrate to form a film of porous a-Si x H y over the surface of the substrate. The flow of plasma is then discontinued and a flow of a nitrogen or oxygen plasma is substituted therefor. The temperature of the substrate is increased to at least 360° C. to diffuse-out hydrogen from the Si x H y film on the substrate, each departing hydrogen atom leaving a dangling Si bond behind which combines with the activated oxygen or nitrogen thereby to form the desired dielectric film of formula Si x N y or Si x O y .
Inventors
- 👤 Aline Akselrad
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 15:15
CPC Classifications
C; C23; C23C; C23C16/00; C23C16/56; C23C16/44; C23C16/50; C23C16/505
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
159 words
A method of depositing a uniform dielectric film on a silicon substrate, comprising the steps of: flowing a first plasma comprising an excited mixture of inert gas and a volatile Si compound over said substrate thereby to form a film having porous a-Si x H y over the surface of said substrate; discontinuing the flow of said first plasma and substituting therefor a flow of a second excited plasma comprising an activated gas selected from the group consisting of oxygen and nitrogen over said substrate; and then elevating the temperature of said substrate to cause the hydrogen to diffuse-out from said porous a-Si x H y film, each departing hydrogen atom leaving behind a dangling Si bond which combines with an excited radical of the activated gas in said second plasma thereby to form said dielectric film of formula Si x M y , where M represents either oxygen or nitrogen, depending on the identity of said activated gas.
Claim 2
Independent Claim
159 words
A method of depositing a uniform dielectric film on a silicon substrate, comprising the steps of: flowing a first plasma comprising an excited mixture of inert gas and a volatile Si compound over said substrate thereby to form a film having porous a-Si x H y over the surface of said substrate; discontinuing the flow of said first plasma and substituting therefor a flow of a second excited plasma comprising an activated gas selected from the group consisting of oxygen and nitrogen over said substrate; and then elevating the temperature of said substrate to cause the hydrogen to diffuse-out from said porous a-Si x H y film, each departing hydrogen atom leaving behind a dangling Si bond which combines with an excited radical of the activated gas in said second plasma thereby to form said dielectric film of formula Si x M y , where M represents either oxygen or nitrogen, depending on the identity of said activated gas.
Claim 3
Dependent Claim
60 words
The method according to claim 1, wherein said substrate is physically located within an RF-excited, plasma reaction chamber and the gas which comprises said second excited plasma is activated by increasing the level of the RF power supplied to the reaction chamber over that which was supplied to excite the mixture of the inert gas and the volatile Si compound.
Claim 4
Dependent Claim
57 words
The method according to claim 1, wherein said substrate is physically positioned within an RF-excited, plasma reaction chamber and the gas which comprises the second excited plasma is activated by changing the frequency of the RF-excitation to a frequency which is above that used to excite the mixture of the inert gas and the volatile Si compound.
Claim 5
Dependent Claim
47 words
The method according to claim 1, wherein said substrate is physically positioned within a plasma reaction chamber and the gas which comprises the second excited plasma is activated by adjusting the pressure of the gas which comprises the second excited plasma to a value to permit activation.
Claim 6
Dependent Claim
43 words
The method according to claim 1, wherein said substituting step comprises: substituting the flow of a second excited plasma comprising a mixture of activated oxygen and nitrogen, whereby the dielectric film formed on said substrate comprises Si x N y O z .
Claim 7
Dependent Claim
22 words
The method according to claim 1, wherein said temperature-elevating step comprises raising the temperature of said substrate in excess of 360° C.
References Cited (Backward Citations)
US3485666A
Cited
US3287243A
Cited
US4089992A
Cited
US3600218A
Cited
US3757733A
Cited
US3983264A
Cited
US4028142A
Cited
US4058430A
Cited
US4066037A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-09-14 | 1985-03-16 | 1985-09-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-09-14 | 1989-03-16 | 1989-09-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-09-14 | 1993-03-16 | 1993-09-15 | $7700.00 | Window Closed / Lapsed |