Abstract
Abstract The present invention relates to a method for the extrusion of tubular thermoplastic films, in particular films produced from polymers such as high density polyethylene, polypropylene, and the like. The method comprises coextrusion of the polymer in the form of a tube which has adhered to its surface, another polymer which is characterized by having a significantly higher melting point than the melting point of the first polymer tube. The tubular films produced in this manner exhibit improved physical properties including a reduced tendency for rupturing or splitting in the machine direction when stresses are applied to such films.
Inventors
- 👤 F. John Herrington, Jr.
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 07:14
CPC Classifications
B; B32; B32B; B32B37/00; B32B37/14; B32B37/15; B32B37/153; B29; B29C; B29C48/00; B29C48/03; B29C48/09; B29C48/10; B29C48/16; B29C48/18; B29C48/21; B29C48/25; B29C48/30; B29C48/32; B29C48/335; B32B1/00; B32B1/08; B32B27/00; B32B27/06; B32B27/08; B32B27/32; B32B27/34; B32B2307/00; B32B2307/70; B32B2307/704; B32B2323/00; B32B2323/04; B32B2323/043
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
115 words
A method for producing blown crystalline high density polyethylene film comprising the steps of: melt extruding a thin inner tubular layer of said high density polyethylene; coextruding a thinner outer tubular layer of higher-melting thermoplastic at a temperature at least 50° F. above the high density polyethylene melting point; inflating the tubular coextruded film utilizing an encapsulated fluid; cooling the tubular film to solidify the outer higher melting thermoplastic layer before solidifying the inner tubular layer; and externally supporting the molten high density polyethylene layer while permitting relaxation of molecular orientation before solidification of the inner tubular film; thereby reducing the tendency for machine direction rupturing or splitting of the high density polyethylene under stress.
Claim 2
Independent Claim
115 words
A method for producing blown crystalline high density polyethylene film comprising the steps of: melt extruding a thin inner tubular layer of said high density polyethylene; coextruding a thinner outer tubular layer of higher-melting thermoplastic at a temperature at least 50° F. above the high density polyethylene melting point; inflating the tubular coextruded film utilizing an encapsulated fluid; cooling the tubular film to solidify the outer higher melting thermoplastic layer before solidifying the inner tubular layer; and externally supporting the molten high density polyethylene layer while permitting relaxation of molecular orientation before solidification of the inner tubular film; thereby reducing the tendency for machine direction rupturing or splitting of the high density polyethylene under stress.
Claim 3
Dependent Claim
25 words
The method of claim 1 wherein said inner tubular layer consists essentially of crystalline high density polyethylene containing an adhesion enhancing amount of ionomoner resin.
Claim 4
Dependent Claim
14 words
The method of claim 2 wherein the outer tubular layer consists essentially of nylon-6.
Claim 5
Dependent Claim
19 words
The method of claim 3 wherein the inner and outer layers are both extruded at substantially the same temperature.
Claim 6
Dependent Claim
13 words
The method of claim 4 wherein the coextrusion temperature is about 480° F.
Claim 7
Dependent Claim
16 words
The method of claim 1 wherein the tubular blow up ratio during inflation is about 4:1.
Claim 8
Dependent Claim
30 words
The method of claim 1 wherein the tubular film has a thickness of about 1.12 to 1.2 mils and said outer layer constitutes about 8% of the overall film thickness.
References Cited (Backward Citations)
US3467565A
Cited
US4048428A
Cited
US3337665A
Cited
US3322870A
Cited
US3949042A
Cited
US3819792A
Cited
US3980744A
Cited
US3997383A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-09-14 | 1985-03-16 | 1985-09-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-09-14 | 1989-03-16 | 1989-09-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-09-14 | 1993-03-16 | 1993-09-15 | $7700.00 | Window Closed / Lapsed |