Polycrystalline cubic boron nitride abrasive and process for preparing same in the absence of catalyst
Assignee: General Electric Co
•
Filing: 1979-06-11
•
Granted: 1981-09-15
•
Expires: 1999-06-11
Abstract
Abstract Cubic boron nitride has been made from powdered hexagonal boron nitride by a process which comprises vacuum firing of the HBN and conversion by high pressure-high temperature processing at 55-80 kilobars and 1600° C. to the reconversion temperature. The high pressure reaction cell has a special design which prevents the entrance of impurities into the sample. This cell, referring to FIG. 2, comprises, for example, a carbon tube (8) enclosing concentric titanium sleeve (9). Within the cylinder defined by the tube and sleeve are: the HBN sample (4), carbon filler (3), shielding tantalum foil discs (2) and carbon end plugs (10). The vacuum firing is done at pressures of 10 -5 --10 -10 mm Hg, 1400°-1900° C., for 5 minutes--4 hours, and is believed to form a thin, free-boron coating on the HBN particles. The process works on both pyrolytic (turbostratic) and graphitic hexagonal boron nitride. Grinding grits formed by milling cubic boron nitride chunks recovered from the high pressure-high temperature process have resulted in higher grinding ratios than commercially available CBN.
Inventors
- 👤 Francis R. Corrigan
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 09:14
CPC Classifications
C; C01; C01B; C01B21/00; C01B21/06; C01B21/064; B; B01; B01J; B01J3/00; B01J3/06; B01J3/062; C04; C04B; C04B35/00; C04B35/515; C04B35/58; C04B35/583; C04B35/5831; C09; C09K; C09K3/00; C09K3/14; C09K3/1409; C09K3/1418; B01J2203/00; B01J2203/06; B01J2203/0605; B01J2203/0645; B01J2203/065; B01J2203/066; B01J2203/0675; B01J2203/0685
Claims Analysis
Total Claims: 43
Claim 1
Independent Claim
160 words
An improved process for making cubic boron nitride from hexagonal boron nitride powder which comprises subjecting hexagonal boron nitride to the high pressure-high temperature process: (i) at a pressure from 55-80 kilobars; (ii) at a temperature of 1600° C. to the reconversion temperature; (iii) for a time sufficient to convert the hexagonal boron nitride to cubic boron nitride and sinter the cubic boron nitride; and (iv) in the absence of catalysts and impurities which interfere with the conversion to cubic boron nitride or the sintering of cubic boron nitride; wherein the improvement comprises a pretreatment process consisting essentially of removing boric oxide from the surface of the hexagonal boron nitride powder--and generating a coating of boron on the surfaces of the oxide-free hexagonal boron nitride--before conversion to cubic boron nitride, which pretreatment is accomplished by a process carried out at a temperature in the hexagonal boron nitride thermal decomposition range and selected from vacuum firing and heating under inert atmosphere.
Claim 2
Dependent Claim
160 words
An improved process for making cubic boron nitride from hexagonal boron nitride powder which comprises subjecting hexagonal boron nitride to the high pressure-high temperature process: (i) at a pressure from 55-80 kilobars; (ii) at a temperature of 1600° C. to the reconversion temperature; (iii) for a time sufficient to convert the hexagonal boron nitride to cubic boron nitride and sinter the cubic boron nitride; and (iv) in the absence of catalysts and impurities which interfere with the conversion to cubic boron nitride or the sintering of cubic boron nitride; wherein the improvement comprises a pretreatment process consisting essentially of removing boric oxide from the surface of the hexagonal boron nitride powder--and generating a coating of boron on the surfaces of the oxide-free hexagonal boron nitride--before conversion to cubic boron nitride, which pretreatment is accomplished by a process carried out at a temperature in the hexagonal boron nitride thermal decomposition range and selected from vacuum firing and heating under inert atmosphere.
Claim 3
Dependent Claim
103 words
The improved process as recited in claim 1 wherein: the pretreatment process comprises the vacuum firing of hexagonal boron nitride powder: (i) in a non-reactive container; (ii) at an initial pressure of from 10 -3 -10 -10 mm Hg; (iii) at a temperature of about 1400°-1900° C.; and (iv) for a time of from 5 minutes to 4 hours; and the conditions of the high pressure-high temperature process are: (i) a pressure of from 65-75 kilobars; (ii) a temperature of 2000°-2300° C.; and (iii) a time of about 8 minutes; and which further comprises recovering CBN masses after the high pressure-high temperature conversion.
Claim 4
Dependent Claim
123 words
The improved process as recited in claim 2 wherein the high pressure-high temperature process is performed in a reaction cell which comprises: a carbon tube; a shield metal sleeve disposed within and concentric to the carbon tube, which sleeve is made of refractory metal, plugs made of a refractory material which is a thermal insulator disposed at the opposite ends of and within the cylinder defined by the shield metal sleeve; foil discs, made from a refractory metal, disposed inside the cylinder and adjacent to the end plugs; plugs of carbon disposed inside the cylinder and adjacent to the shield metal discs; and the hexagonal boron nitride powder disposed within the central cavity defined by the carbon plugs and the shield metal tube.
Claim 5
Dependent Claim
28 words
The improved process as recited in claim 2 which further comprises prepressing the hexagonal boron nitride samples in the shield metal sleeve before the high pressure-high temperature process.
Claim 6
Dependent Claim
23 words
The improved process as recited in claim 2 wherein graphite is mixed with the hexagonal boron nitride in the high pressure-high temperature process.
Claim 7
Dependent Claim
20 words
The improved process as recited in claim 2 which further comprises milling the cubic boron nitride masses into grinding grit.
Claim 8
Dependent Claim
18 words
The improved process as recited in claim 6 in which the hexagonal boron nitride is pyrolytic boron nitride.
Claim 9
Dependent Claim
20 words
The improved process as recited in claim 7 wherein the high pressure high temperature process takes place at 2000°-2100° C.
Claim 10
Dependent Claim
27 words
The improvd process as recited in claim 8 wherein the conditions of the pretreatment process are: (i) temperature of 1580°-1615° C.; and (ii) time of 60-90 minutes.
Claim 11
Dependent Claim
23 words
Cubic boron nitride grit which comprises polycrystalline cubic boron nitride particles made from pyrolytic boron nitride obtained by the process of claim 8.
Claim 12
Dependent Claim
23 words
Cubic boron nitride grit which comprises polycrystalline cubic boron nitride particles made from pyrolytic boron nitride obtained by the process of claim 9.
Claim 13
Dependent Claim
16 words
A resin-bonded grinding wheel containing the cubic boron nitride abrasive particles of claims 10 or 11.
Claim 14
Dependent Claim
17 words
The resin-bonded grinding wheel of claim 12 wherein the cubic boron nitride abrasive particles are nickel coated.
Claim 15
Dependent Claim
18 words
The method of grinding high speed tool steel which comprises grinding with the grinding wheel of claim 13.
Claim 16
Dependent Claim
21 words
The product of the process recited in claim 2 or claim 6 wherein the hexagonal boron nitride is graphitic boron nitride.
Claim 17
Dependent Claim
81 words
The improved process as recited in claim 2 or claim 6 which further comprises mixing the vacuum-fired hexagonal boron nitride powder from the pretreatment process with a quantity of single-crystal cubic boron nitride particles having a maximum dimension ranging from 5 to 150 microns in a concentration of 5-30 volume percent single crystal cubic boron nitride crystals, which process yields aggregate cubic boron nitride masses comprised of single-crystal cubic boron nitride particles embedded in a boron-rich, polycrystalline cubic boron nitride matrix.
Claim 18
Dependent Claim
18 words
The improved process as recited in claim 16 wherein the hexagonal boron nitride has the graphitic crystal structure.
Claim 19
Dependent Claim
13 words
The aggregated cubic boron nitride masses made by the process of claim 17.
Claim 20
Dependent Claim
15 words
The grinding grit comprised of aggregated cubic boron nitride masses as recited in claim 18.
Claim 21
Dependent Claim
11 words
A resin-bonded grinding wheel containing the grinding grit of claim 19.
Claim 22
Dependent Claim
14 words
The resin-bonded grinding wheel of claim 20 wherein the grinding grit is nickel coated.
Claim 23
Dependent Claim
18 words
The method of grinding high speed tool steel which comprises grinding with the grinding wheel of claim 21.
Claim 24
Dependent Claim
66 words
The improved process as recited in claims 2 or 6 which further comprises mixing the vacuum-fired hexagonal boron nitride powder from Step A with a quantity of a powdered material which does not interfere with the conversion of the hexagonal boron nitride or the sintering of the cubic boron nitride, which process yields aggregate cubic boron nitride masses comprised of polycrystalline cubic boron nitride with inclusions.
Claim 25
Dependent Claim
19 words
The improved process of claim 23 wherein the powdered material mixed with the vacuum-fired HBN is a refractory metal.
Claim 26
Dependent Claim
20 words
The improved process as recited in claim 24 which further comprises leaching out the refractory metal inclusions from the product.
Claim 27
Dependent Claim
13 words
The polycrystalline cubic boron nitride masses made by the process of claim 25.
Claim 28
Dependent Claim
15 words
The grinding grit comprised of aggregated cubic boron nitride masses as recited in claim 26.
Claim 29
Dependent Claim
11 words
A resin-bonded grinding wheel containing the grinding grit of claim 27.
Claim 30
Dependent Claim
14 words
The resin-bonded grinding wheel of claim 28 wherein the grinding grit is nickel coated.
Claim 31
Dependent Claim
18 words
The method of grinding high speed tool steel which comprises grinding with the grinding wheel of claim 29.
Claim 32
Dependent Claim
18 words
The improved process as recited in claim 24 wherein the hexagonal boron nitride has the graphitic crystal structure.
Claim 33
Dependent Claim
13 words
The aggregated cubic boron nitride masses made by the process of claim 31.
Claim 34
Dependent Claim
15 words
The grinding grit comprised of aggregated cubic boron nitride masses as recited in claim 32.
Claim 35
Dependent Claim
11 words
A resin-bonded grinding wheel containing the grinding grit of claim 33.
Claim 36
Dependent Claim
14 words
The resin-bonded grinding wheel of claim 34 wherein the grinding grit is nickel coated.
Claim 37
Dependent Claim
18 words
The method of grinding high speed tool steel which comprises grinding with the grinding wheel of claim 35.
Claim 38
Dependent Claim
31 words
An aggregated cubic boron nitride abrasive particle consisting essentially of single-crystal, catalyst-grown cubic boron nitride embedded in a matrix of boron-rich, polycrystalline cubic boron nitride made from graphitic hexagonal boron nitride.
Claim 39
Dependent Claim
31 words
An aggregated cubic boron nitride abrasive particle consisting essentially of single-crystal, catalyst-grown cubic boron nitride embedded in a matrix of boron-rich, polycrystalline cubic boron nitride made from graphitic hexagonal boron nitride.
Claim 40
Dependent Claim
30 words
An aggregated cubic boron nitride abrasive particle consisting essentially of refractory metal powder particles embedded in a matrix of boron-rich, polycrystalline cubic boron nitride made from graphitic hexagonal boron nitride.
Claim 41
Dependent Claim
30 words
An aggregated cubic boron nitride abrasive particle consisting essentially of refractory metal powder particles embedded in a matrix of boron-rich, polycrystalline cubic boron nitride made from graphitic hexagonal boron nitride.
Claim 42
Dependent Claim
20 words
A boron-rich polycrystalline cubic boron nitride particle made from graphitic hexagonal boron nitride which particle has surface voids and indentations.
Claim 43
Dependent Claim
20 words
A boron-rich polycrystalline cubic boron nitride particle made from graphitic hexagonal boron nitride which particle has surface voids and indentations.
References Cited (Backward Citations)
US3212852A
Cited
GB1313533A
Cited
US3645706A
Cited
GB1303925A
Cited
GB1317716A
Cited
US3926571A
Cited
US3918931A
Cited
US4008055A
Cited
US4089931A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-09-14 | 1985-03-16 | 1985-09-15 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-09-14 | 1989-03-16 | 1989-09-15 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-09-14 | 1993-03-16 | 1993-09-15 | $7700.00 | Window Closed / Lapsed |