Method and apparatus for the heat treatment of fine-grained material
Assignee: Kloeckner Humboldt Deutz AG
•
Filing: 1979-10-15
•
Granted: 1981-09-08
•
Expires: 1999-10-15
Abstract
Abstract Method and apparatus for the heat treatment of fine-grained material, particularly raw material for the manufacture of cement wherein the material is pre-heated, calcined, sintered, and then cooled, the sintering of the substantially calcined material according to the present invention being carried out in the form of an airborne suspension.
Inventors
- 👤 Horst Herchenbach
- 👤 Hubert Ramesohl
- 👤 Joachim Fleischer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 03:59
CPC Classifications
C; C04; C04B; C04B7/00; C04B7/36; C04B7/43; C04B7/44
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
73 words
In a method for heat treating a fine-grained material in which said material is sequentially passed through a pre-heating zone, a calcining zone, a sintering zone, and a cooling zone, the improvement which comprises separately heat treating the calcined material from said calcining zone to volatilize lower melting components, suspending the substantially calcined and heat treated material as an airborne suspension in said sintering zone and sintering the suspension in said sintering zone.
Claim 2
Dependent Claim
73 words
In a method for heat treating a fine-grained material in which said material is sequentially passed through a pre-heating zone, a calcining zone, a sintering zone, and a cooling zone, the improvement which comprises separately heat treating the calcined material from said calcining zone to volatilize lower melting components, suspending the substantially calcined and heat treated material as an airborne suspension in said sintering zone and sintering the suspension in said sintering zone.
Claim 3
Dependent Claim
35 words
A method according to claim 1 which includes the step of separating the material from hot gases produced in said sintering zone in a separate separation zone between the sintering zone and the cooling zone.
Claim 4
Dependent Claim
26 words
A method according to claim 1 which comprises cooling the material leaving the sintering zone in the cooling zone in the form of an airborne suspension.
Claim 5
Dependent Claim
48 words
A method according to claim 1 which includes the step of dividing the fuel required for the heat treatment of the material between the calcining and sintering zones, introducing relatively low caloric fuel into the calcining zone and introducing relatively high caloric content fuel into the sintering zone.
Claim 6
Dependent Claim
39 words
A method according to claim 1 which includes the step of introducing hot air from the cooling zone selectively into the calcining zone or the sintering zone depending upon the nature of the fuel being burned in said zones.
Claim 7
Dependent Claim
34 words
A method according to claim 5 which includes the step of throttling the hot air being fed to said calcining zone to thereby distribute the same between said calcining zone and said sintering zone.
Claim 8
Dependent Claim
35 words
A method according to claim 5 which includes the steps of supplying the hot air withdrawn from the cooling zone to the sintering zone in relation to the gas velocity required in said sintering zone.
Claim 9
Dependent Claim
35 words
A method according to claim 5 which includes the step of supplying the hot exhaust gas from the cooling zone to the sintering zone at a location where the clinker mineral formation is substantially terminated.
Claim 10
Dependent Claim
22 words
A method according to claim 1 which includes the step of supplying exhaust gases from the sintering zone to the calcining zone.
Claim 11
Dependent Claim
26 words
A method according to claim 2 which includes the step of reintroducing a part of the material separated in the separation zone into the sintering zone.
Claim 12
Dependent Claim
36 words
A method according to claim 2 which includes the step of withdrawing a portion of the gas separated in the separation zone from the system in the area between the separation zone and the calcining zone.
Claim 13
Dependent Claim
29 words
A method according to claim 11 which includes the step of cooling the gases withdrawn from the system immediately after being withdrawn and subsequently removing dust from said gases.
Claim 14
Dependent Claim
24 words
A method according to claim 1 in which the lower melting components constitute less than 25% of the material delivered into the sintering zone.
Claim 15
Dependent Claim
25 words
A method according to claim 1 in which the lower melting components constitute from 10% to 20% of the material introduced into the sintering zone.
Claim 16
Dependent Claim
29 words
A method according to claim 1 which includes the step of introducing a flux material to the separate heat treatment to improve the volatility of the lower melting components.
References Cited (Backward Citations)
US2670193A
Cited
US2874950A
Cited
US2981531A
Cited
US3498594A
Cited
US3932117A
Cited
US4118177A
Cited
US4174946A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-09-07 | 1985-03-09 | 1985-09-08 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-09-07 | 1989-03-09 | 1989-09-08 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-09-07 | 1993-03-09 | 1993-09-08 | $7700.00 | Window Closed / Lapsed |