Method for producing printed circuits
Assignee: Bayer Pharma AG
•
Filing: 1980-05-15
•
Granted: 1981-08-25
•
Expires: 2000-05-15
Abstract
Abstract A method for producing printed circuits. An epoxy resin reinforced with glass fiber is used as basis material, coated with copper, drilled and activated. In one embodiment, the circuit diagram is applied after covering the non-desired regions with a resistance, by screen or photo printing. A nickel, cobalt, or nickel-cobalt layer is deposited onto the circuit, the circuit is covered with a solder prevention lacquer, then the eyes and bore holes are covered with copper. Alternatively, after pre-treatment and activation, all areas except the soldering eyes and bore holes are covered with resist, a nickel, cobalt or nickel-cobalt layer is applied, the circuit diagram is printed using a resist, and the eyes and bore hole are treated as above.
Inventors
- 👤 Klaus Gedrat
- 👤 Hans-Jurgen Ehrich
- 👤 Hartmut Mahlkow
- 👤 Joachim Wolff
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 12:24
CPC Classifications
H; H05; H05K; H05K3/00; H05K3/22; H05K3/24; H05K3/244; H05K3/02; H05K3/06; H05K3/061; H05K3/062; H05K3/40; H05K3/42; H05K3/422; H05K3/425; H05K3/427; H05K2201/00; H05K2201/03; H05K2201/0332; H05K2201/0335; H05K2201/0341; H05K2201/0344; H05K2201/09; H05K2201/09209; H05K2201/09654; H05K2201/09736; H05K2203/00; H05K2203/05; H05K2203/0562; H05K2203/0571; H05K2203/14; H05K2203/1407; H05K3/243; H05K3/28; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49002; Y10T29/49117; Y10T29/49124; Y10T29/49155; Y10T29/49165
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
139 words
A method of producing printed circuits of the type wherein basis material is coated with copper which material is drilled, purified, activated, reduced and after-treated, wherein the circuit image is applied by printing the copper with a resist after covering of all areas not belonging to the circuit intended to be produced, wherein the improvement comprises covering the exposed copper of the so-pretreated basis material with a layer of metal selected from the group consisting of nickel, cobalt and nickel-cobalt through treatment with a chemical bath of said metal; removing the resist; etching the copper exposed by removal of the resist; covering the circuit image negatively with a solder prevention lacquer but leaving the soldering eyes and bore holes exposed; and providing the exposed eyes and bore holes with a copper layer though treatment with a chemical copper bath.
Claim 2
Independent Claim
139 words
A method of producing printed circuits of the type wherein basis material is coated with copper which material is drilled, purified, activated, reduced and after-treated, wherein the circuit image is applied by printing the copper with a resist after covering of all areas not belonging to the circuit intended to be produced, wherein the improvement comprises covering the exposed copper of the so-pretreated basis material with a layer of metal selected from the group consisting of nickel, cobalt and nickel-cobalt through treatment with a chemical bath of said metal; removing the resist; etching the copper exposed by removal of the resist; covering the circuit image negatively with a solder prevention lacquer but leaving the soldering eyes and bore holes exposed; and providing the exposed eyes and bore holes with a copper layer though treatment with a chemical copper bath.
Claim 3
Dependent Claim
20 words
Method according to claim 1, wherein as basis material, an epoxy resin is used which is reinforced with glass fibers.
Claim 4
Dependent Claim
24 words
Method according to claim 1, wherein a chemical nickel bath is used containing as essential components a nickel salt, a citrate and an alkalihypophosphite.
Claim 5
Dependent Claim
32 words
Method according to claim 1, wherein a chemical nickel bath is used containing as essential components a nickel salt, an alkalidiphosphate, an alkali hydrogen phosphate and hydrazine or one of its derivates.
Claim 6
Dependent Claim
24 words
Method according to claim 1, wherein a chemical cobalt bath is used containing as essential components a cobalt salt, a citrate and an alkali-hypophosphite.
Claim 7
Dependent Claim
32 words
Method according to claim 1, wherein a chemical cobalt bath is used containing as essential components a cobalt salt, an alkalidiphosphate, an alkali hydrogen phosphate and hydrazine or one of its derivates.
Claim 8
Dependent Claim
27 words
Method according to claim 1, wherein a chemical nickel-cobalt bath is used containing as essential components a nickel salt, a cobalt salt, a citrate and an alkalihypophosphite.
Claim 9
Dependent Claim
23 words
Method according to claim 1, wherein the nickel, cobalt or nickel-cobalt layer is applied having a thickness of about 0.1 to 0.5 μm.
Claim 10
Dependent Claim
23 words
Method according to claim 1, wherein the nickel, cobalt or nickel-cobalt layer is applied having a thickness of about 0.3 to 0.8 μm.
Claim 11
Dependent Claim
13 words
Method according to claim 1, wherein a stabilized chemical copper bath is used.
Claim 12
Dependent Claim
37 words
Method according to claim 10, wherein a chemical copper bath is used containing as essential components a copper salt, a complex forming substance, formaldehyde as well as an alkalicyanide and if necessary a selenium compound as stabilizors.
Claim 13
Dependent Claim
19 words
Method according to claim 1, further comprising applying a lead-tin alloy onto the so-coppered soldering eyes and bore holes.
Claim 14
Dependent Claim
32 words
Method according to claim 1, further comprising coppering with a copper bath selected from the group consisting of chemical and galvanic copper baths after said covering with a layer of selected metal.
Claim 15
Independent Claim
131 words
A method of producing printed circuits of the type wherein basis material is coated with copper which material is drilled, purified, activated, reduced and after-treated wherein the improvement comprises covering a portion of copper on the so-pretreated basis material with a layer of metal selected from the group consisting of nickel, cobalt and nickel-cobalt through treatment with a chemical bath of said metal; applying the circuit image positively by means of a resist onto the remaining exposed copper; etching the copper where it remains uncovered by said layer and the resist; removing the resist; covering the circuit image by means of a solder prevention lacquer while leaving the soldering eyes and bore holes uncovered; and providing the exposed eyes and bore holes with a copper layer in a chemical copper bath.
Claim 16
Independent Claim
131 words
A method of producing printed circuits of the type wherein basis material is coated with copper which material is drilled, purified, activated, reduced and after-treated wherein the improvement comprises covering a portion of copper on the so-pretreated basis material with a layer of metal selected from the group consisting of nickel, cobalt and nickel-cobalt through treatment with a chemical bath of said metal; applying the circuit image positively by means of a resist onto the remaining exposed copper; etching the copper where it remains uncovered by said layer and the resist; removing the resist; covering the circuit image by means of a solder prevention lacquer while leaving the soldering eyes and bore holes uncovered; and providing the exposed eyes and bore holes with a copper layer in a chemical copper bath.
Claim 17
Dependent Claim
42 words
Method according to claim 14, further comprising covering all areas with resist except the soldering eyes and bore holes prior to said covering with a layer of selected metal and removing the resist after said covering with a layer of selected metal.
Claim 18
Dependent Claim
19 words
Method according to claim 14 further comprising applying a lead-tin alloy onto the so-coppered soldering eyes and bore holes.
Claim 19
Dependent Claim
32 words
Method according to claim 14, further comprising coppering with a copper bath selected from the group consisting of chemical and galvanic copper baths after said covering with a layer of selected metal.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-08-24 | 1985-02-23 | 1985-08-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-08-24 | 1989-02-23 | 1989-08-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-08-24 | 1993-02-23 | 1993-08-25 | $7700.00 | Window Closed / Lapsed |