Abstract
Abstract Ion exchange resins having improved physical stability and perfect bead count are prepared by a free-radical catalyzed polymerization of a monomer mixture utilizing certain peroxyester and peroxydicarbonate catalysts, followed by functionalizing the so prepared polymer.
Inventors
- 👤 Thomas J. Howell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-07 07:10
CPC Classifications
B; B01; B01J; B01J41/00; B01J41/08; B01J41/12; B01J41/14; B01J39/00; B01J39/08; B01J39/16; B01J39/18; B01J39/20; C; C08; C08F; C08F212/00
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
184 words
In the process of preparing hard, crosslinked discrete ion exchange copolymer beads by the thermally induced free-radical polymerization in an aqueous dispersion of a monomer mixture comprised of a major proportion of a monovinyl aromatic monomer and a minor proportion of a crosslinking monomer having at least two active vinyl groups, the improvement which comprises conducting the polymerization reaction in the presence of a peroxy catalyst of the formula: ##STR5## wherein R 1 is a branched alkyl of 3 to 12 carbon atoms and having a secondary or tertiary carbon linked to the carbonyl group and X is a positive integer having a value of either 1 or 2 and when X is 1, R 2 is a branched alkyl radical containing a tertiary carbon attached to the oxygen, and when X is 2, R 2 is an alkylene or aralkylene, in either case terminating in tertiary carbons attached to the oxygen, or of the formula: ##STR6## wherein Y and Z are independently selected from lower alkyl, cycloalkyl, alkyl-substituted cycloalkyl and aralkyl, and thereafter functionalizing the copolymer bead to form ion exchange sites therein.
Claim 2
Dependent Claim
184 words
In the process of preparing hard, crosslinked discrete ion exchange copolymer beads by the thermally induced free-radical polymerization in an aqueous dispersion of a monomer mixture comprised of a major proportion of a monovinyl aromatic monomer and a minor proportion of a crosslinking monomer having at least two active vinyl groups, the improvement which comprises conducting the polymerization reaction in the presence of a peroxy catalyst of the formula: ##STR5## wherein R 1 is a branched alkyl of 3 to 12 carbon atoms and having a secondary or tertiary carbon linked to the carbonyl group and X is a positive integer having a value of either 1 or 2 and when X is 1, R 2 is a branched alkyl radical containing a tertiary carbon attached to the oxygen, and when X is 2, R 2 is an alkylene or aralkylene, in either case terminating in tertiary carbons attached to the oxygen, or of the formula: ##STR6## wherein Y and Z are independently selected from lower alkyl, cycloalkyl, alkyl-substituted cycloalkyl and aralkyl, and thereafter functionalizing the copolymer bead to form ion exchange sites therein.
Claim 3
Dependent Claim
12 words
The process of claim 1 wherein the peroxy catalyst is t-butyl peroctoate.
Claim 4
Dependent Claim
12 words
The process of claim 1 wherein the peroxy catalyst is t-butyl peroxyneodecanoate.
Claim 5
Dependent Claim
11 words
The process of claim 1 wherein the peroxy catalyst is 2,5-dimethyl-2,5-bis(2-ethylhexanoylperoxy)-hexane.
Claim 6
Dependent Claim
11 words
The process of claim 1 wherein the peroxy catalyst is di-(4-t-butylcyclohexyl)peroxydicarbonate.
Claim 7
Dependent Claim
12 words
The process of claim 1 wherein the peroxy catalyst is dicyclohexyl peroxydicarbonate.
Claim 8
Dependent Claim
40 words
The process of claim 1 wherein the polymerization with the peroxy catalyst is conducted with oxygen in contact with the monomer mixture so that oxygen is absorbed by said monomer mixture at least until the polymerization reaches the gel point.
Claim 9
Dependent Claim
49 words
The process of claim 1 wherein the polymerization with the peroxy catalyst is conducted with a modifier in admixture with the monomer mixture in a concentration of from about 0.01 to about 20 millimoles per mole of monomer, said modifier being an organic compound containing acetylenic or allylic unsaturation.
Claim 10
Dependent Claim
28 words
The process of claim 1 wherein the polymerization with the peroxy catalyst is conducted with the oxygen addition of claim 7 and the modifier addition of claim 8.
Claim 11
Dependent Claim
93 words
Hard, crosslinked discrete ion exchange beads having improved physical properties formed by the thermally induced free-radical polymerization in an aqueous dispersion of a monovinyl aromatic monomer and a polyvinyl monomer according to claim 1 followed by functionalization of the resulting copolymer to form ion exchange sites therein, which beads have a perfect bead count of at least 90%, a Chatillion value of at least 500 grams per bead and are capable of withstanding 50 cycles of alternating acid and base treatment without loss of more than 15% of the original perfect bead content.
Claim 12
Dependent Claim
16 words
Improved ion exchange beads derived from the ion exchange copolymer beads produced according to claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-08-10 | 1985-02-09 | 1985-08-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-08-10 | 1989-02-09 | 1989-08-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-08-10 | 1993-02-09 | 1993-08-11 | $7700.00 | Window Closed / Lapsed |