Method of making an ion conductive gas sensor body with a cermet electrode thereon
Assignee: Robert Bosch GmbH
•
Filing: 1979-11-29
•
Granted: 1981-08-11
•
Expires: 1999-11-29
Abstract
Abstract To increase the response speed and sensitivity, while providing higher output voltages and permitting higher loading of the electrodes of gas sensors, particularly exhaust gas sensors to determine the transition of exhaust gases from internal combustion engines between reducing and oxidizing state, the sintering activity of the electrode which, typically, a cermet electrode, is selected to be less than that of the solid electrolyte body so that the resulting pore structure will be more open than that of the solid electrolyte body. The electrodes, essentially, consist of finely divided ceramic material, such as zirconium oxide, and finely divided electron conductive material such as platinum. On the pre-sintered solid electrolyte body, a mixture of the ceramic and the electron conductive material is applied in which the ceramic of the lattice support structure for the cermet electrode is less sinter-active than the ceramic of the solid electrolyte body, resulting in the improved pore structure of the cermet electrode layer.
Inventors
- 👤 Wolf-Dieter Haecker
- 👤 Karl-Hermann Friese
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 02:40
CPC Classifications
G; G01; G01N; G01N27/00; G01N27/26; G01N27/403; G01N27/406; G01N27/407; G01N27/4075; C; C04; C04B; C04B35/00; C04B35/01; C04B35/48; C04B35/486; H; H01; H01M; H01M8/00; H01M8/10; H01M8/12; Y; Y02; Y02E; Y02E60/00; Y02E60/30; Y02E60/50; Y02P; Y02P70/00; Y02P70/50
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
100 words
In a method of making a cermet electrode for gas sensors having an ion conductive solid electrolyte body, in which the electrode essentially comprises a mixture of a finely divided ceramic to form a support lattice and a finely divided electron conductive material, and including the steps of applying the mixture of ceramic-electron conductive material to said body and sintering the body and mixture thereon to form a cermet electrode on the body, the improvement wherein the finely divided ceramic for the lattice comprises a material having a lesser sintering activity than the sintering activity of the solid electrolyte body.
Claim 2
Dependent Claim
100 words
In a method of making a cermet electrode for gas sensors having an ion conductive solid electrolyte body, in which the electrode essentially comprises a mixture of a finely divided ceramic to form a support lattice and a finely divided electron conductive material, and including the steps of applying the mixture of ceramic-electron conductive material to said body and sintering the body and mixture thereon to form a cermet electrode on the body, the improvement wherein the finely divided ceramic for the lattice comprises a material having a lesser sintering activity than the sintering activity of the solid electrolyte body.
Claim 3
Dependent Claim
42 words
Method according to claim 1, wherein the ion conductive solid electrolyte body and the ceramic material forming the lattice for the electron conductive material comprises essentially a material selected from the group consisting of: zirconium dioxide, thorium oxide, hafnium oxide, cerium oxide.
Claim 4
Dependent Claim
61 words
Method according to claim 2, wherein the material of said group which forms the lattice structure has a higher content of stabilizing additive than the material of the group forming the solid electrolyte body; and wherein the stabilizing additive comprises at least one of the materials of the group of: CaO, Y 2 O 3 or Yb 2 O 3 .
Claim 5
Dependent Claim
30 words
Method according to claim 3, wherein the material of the solid electrolyte body comprises partially stabilized zirconium oxide, and the material for the lattice structure comprises fully stabilized zirconium oxide.
Claim 6
Dependent Claim
37 words
Method according to claim 4, wherein the zirconium oxide of the solid electrolyte body includes 5 mol-% Y 2 O 3 and the zirconium oxide of the lattice structure includes 7.5 mol-% Y 2 O 3 .
Claim 7
Dependent Claim
39 words
Method according to claim 2, wherein flux additives are added to the material of said group; and the material of the lattice support structure has a lesser content of flux additives than the material of the solid electrolyte body.
Claim 8
Dependent Claim
46 words
Method according to claim 6, wherein the flux additive comprises at least one of the materials of the group consisting of: silicate flux; sintering enhancing raw material contaminants selected from the group consisting of: titanium dioxide, Al 2 O 3 , phosphates, sulfates, or rare-earth oxides.
Claim 9
Dependent Claim
27 words
Method according to claim 1, wherein the materials of said group forming the lattice support structure are coarser than the raw materials for the solid electrolyte body.
Claim 10
Dependent Claim
53 words
Method according to claim 1, including the step of grinding the material of said group for pulverization thereof; and where the grinding step of the material for the lattice structure is carried out to grind the material for the lattice structure to a lesser extent than the material for the solid electrolyte body.
Claim 11
Dependent Claim
41 words
Method according to claim 1, wherein said material for the lattice structure comprises pre-calcined, stabilized powder of a material selected from the group consisting of at least one of: ZrO 2 , ThO 2 , HfO 2 , CeO 2 .
Claim 12
Dependent Claim
20 words
Method according to claim 2, wherein the material for the lattice support structure comprises pure zirconium oxide without stabilization additive.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-08-10 | 1985-02-09 | 1985-08-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-08-10 | 1989-02-09 | 1989-08-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-08-10 | 1993-02-09 | 1993-08-11 | $7700.00 | Window Closed / Lapsed |