US4282117A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for producing electrically conductive zinc oxide
Assignee: Honjo Chemical Corp
•
Filing: 1979-05-30
•
Granted: 1981-08-04
•
Expires: 1999-05-30
Abstract
Abstract A method for producing electrically conductive zinc oxide comprising calcining zinc oxide under an ambient atmosphere in a vessel at a temperature from about 800 DEG to about 1100 DEG C. in a mixture thereof with aluminum oxide or a precursor thereof convertible into the oxide under the conditions of treatment in an amount of about 0.05 to about 5 moles based on aluminum atom therein in relation to 100 moles of zinc oxide in the presence of solid carbon. A further improvement in the method comprises mixing zinc oxide with aluminum oxide powder of not more than about 20 millimicrons in average particle size in the dry form to provide a feed mixture, and calcining the mixture, to provide a highly conductive form of zinc oxide.
Inventors
- 👤 Makoto Muramoto
- 👤 Nobuyuki Ishida
- 👤 Fujio Matsushita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 15:09
CPC Classifications
C; C01; C01G; C01G9/00; C01G9/02; H; H01; H01B; H01B1/00; H01B1/06; H01B1/08
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
149 words
A method for producing electrically conductive zinc oxide comprising: calcining zinc oxide under an ambient atmosphere in a vessel at a temperature of about 800° C. to about 1100° C. in a mixture thereof with aluminum oxide or a precursor thereof convertible into the oxide under the conditions of treatment, the precursor being selected from the group consisting of aluminum nitrate, aluminum sulfate, aluminum chloride, aluminum bromide, aluminum hydroxide, aluminum formate and aluminum acetate, in an amount of from 0.5 moles to about 5 moles, based on the aluminum therein, in relation to 100 moles of zinc oxide, in the presence of solid carbon, while allowing the gases generated by the reaction of the solid carbon with the ambient atmosphere to be discharged spontaneously from the vessel as the gases are generated; and cooling the thus calcined mixture to a temperature below about 200° C. under a non-oxidizing atmosphere.
Claim 2
Independent Claim
149 words
A method for producing electrically conductive zinc oxide comprising: calcining zinc oxide under an ambient atmosphere in a vessel at a temperature of about 800° C. to about 1100° C. in a mixture thereof with aluminum oxide or a precursor thereof convertible into the oxide under the conditions of treatment, the precursor being selected from the group consisting of aluminum nitrate, aluminum sulfate, aluminum chloride, aluminum bromide, aluminum hydroxide, aluminum formate and aluminum acetate, in an amount of from 0.5 moles to about 5 moles, based on the aluminum therein, in relation to 100 moles of zinc oxide, in the presence of solid carbon, while allowing the gases generated by the reaction of the solid carbon with the ambient atmosphere to be discharged spontaneously from the vessel as the gases are generated; and cooling the thus calcined mixture to a temperature below about 200° C. under a non-oxidizing atmosphere.
Claim 3
Dependent Claim
46 words
A method for producing electrically conductive zinc oxide as claimed in claim 1 further comprising: mixing zinc oxide with aluminum oxide or a precursor thereof in an aqueous solution or a suspension thereof; drying the resulting paste or slurry; pulverizing the mixture; and calcining the mixture.
Claim 4
Dependent Claim
42 words
A method for producing electrically conductive zinc oxide as claimed in claim 1 further comprising: mixing zinc oxide powder with aluminum oxide powder of not more than about 20 millimicrons in average particle size in the dry form; and calcining the mixture,
Claim 5
Dependent Claim
23 words
A method for producing electrically conductive zinc oxide as claimed in claim 1 wherein the solid carbon is uniformly dispersed in the mixture.
Claim 6
Dependent Claim
34 words
A method for producing electrically conductive zinc oxide as claimed in claim 1 wherein the solid carbon is placed in a layer in the vessel and the mixture is thereupon placed in a layer.
Claim 7
Dependent Claim
26 words
A method for producing electrically conductive zinc oxide as claimed in claim 1 wherein the solid carbon is portionwise placed in a layer of the mixture.
Claim 8
Dependent Claim
30 words
A method for producing electrically conductive zinc oxide as claimed in claim 1 wherein the solid carbon wrapped in a porous container is placed in a layer of the mixture.
Claim 9
Dependent Claim
29 words
A method for producing electrically conductive zinc oxide as claimed in claim 1 wherein the solid carbon is charcoal or coal in the form of powder, granule or lump.
References Cited (Backward Citations)
US3515686A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-08-03 | 1985-02-02 | 1985-08-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-08-03 | 1989-02-02 | 1989-08-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-08-03 | 1993-02-02 | 1993-08-04 | $7700.00 | Window Closed / Lapsed |