US4280944A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Thermosetting polyurethane resin and coating agent thereof prepared from at least two polyoxyalkylene polyols, blocking agent, chain-elongating agent, cross-linking agent and a mixture of diisocyanates
Assignee: Mitsui Toatsu Chemicals Inc
•
Filing: 1980-05-16
•
Granted: 1981-07-28
•
Expires: 2000-05-16
Abstract
Abstract A thermosetting polyurethane resin which when used as a one-pack surface-protective coating agent for glass bottles, inorganic vessels, and the like exhibits excellent mechanical strength, appearance, and water resistance at sterilization temperatures of about 90 DEG C. is obtained by interacting: (a) 10 to 40% by weight of at least two polyoxyalkylene polyols based on the weight of the nonvolatile matter of the thermosetting polyurethane resin, said at least two polyoxyalkylene polyols including 1 to 8% by weight relative to the nonvolatile matter of the thermosetting polyurethane resin of a nonionic surface active agent selected from the group consisting of a polyoxyethylene glycol or a polyoxyethylene-polyoxypropylene glycol, and mixtures thereof, (b) a monofunctional isocyanate-blocking agent, (c) a chain-elongating agent, (d) a cross-linking agent, and (e) a mixture of methylene-bis (4-cyclohexylisocyanate) and iso-phorone diisocyanate at a molar ratio in the range of from 1:0.3 to 1:1.5.
Inventors
- 👤 Takashi Saito
- 👤 Kiyotsugu Asai
- 👤 Toshihiko Kawabata
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 15:51
CPC Classifications
C; C08; C08G; C08G18/00; C08G18/06; C08G18/70; C08G18/72; C08G18/74; C08G18/75; C03; C03C; C03C17/00; C03C17/28; C03C17/32; C03C17/322; C08G18/08; C08G18/10; C08G18/28; C08G18/40; C08G18/48; C08G18/4833; C08G18/4837
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
158 words
A thermosetting polyurethane resin obtained by interacting: (a) a prepolymer having terminal NCO groups which is obtained by reacting at least one polyoxyalkylene polyol with methylene bis(4-cyclohexylisocyanate) and isophorone diisocyanate and then with a chain-elongating agent, (b) a monofunctional isocyanate-blocking agent, (c) a non-ionic surface active agent selected from the group consisting of a polyoxyethylene glycol or a polyoxyethylene-polyoxypropylene glycol, and mixtures thereof, and (d) a cross-linking agent wherein said prepolymer is reacted with said monofunctional isocyanate-blocking agent, the total weight percentage of said at least one polyoxyalkylene polyol and said non-ionic surface active agent is 10 to 40% based upon the weight of the nonvolatile matter of the thermosetting polyurethane resin, the weight percentage of said non-ionic surface active agent is 1 to 8% relative to the weight of the non-volatile matter of the thermosetting polyurethane resin, and the molar ratio of the methylene bis(4-cyclohexylisocyanate) and iso-phorone diisocyanate is in the range of from 1:0.3 to 1:1.5.
Claim 2
Dependent Claim
158 words
A thermosetting polyurethane resin obtained by interacting: (a) a prepolymer having terminal NCO groups which is obtained by reacting at least one polyoxyalkylene polyol with methylene bis(4-cyclohexylisocyanate) and isophorone diisocyanate and then with a chain-elongating agent, (b) a monofunctional isocyanate-blocking agent, (c) a non-ionic surface active agent selected from the group consisting of a polyoxyethylene glycol or a polyoxyethylene-polyoxypropylene glycol, and mixtures thereof, and (d) a cross-linking agent wherein said prepolymer is reacted with said monofunctional isocyanate-blocking agent, the total weight percentage of said at least one polyoxyalkylene polyol and said non-ionic surface active agent is 10 to 40% based upon the weight of the nonvolatile matter of the thermosetting polyurethane resin, the weight percentage of said non-ionic surface active agent is 1 to 8% relative to the weight of the non-volatile matter of the thermosetting polyurethane resin, and the molar ratio of the methylene bis(4-cyclohexylisocyanate) and iso-phorone diisocyanate is in the range of from 1:0.3 to 1:1.5.
Claim 3
Dependent Claim
105 words
A thermosetting polyurethane resin as claimed in claim 1 wherein said non-ionic surface active agent is a polyoxyethylene glycol with terminal hydroxyl groups having a molecular weight in the range of from 400 to 20,000 or propylene oxide and ethylene oxide copolymers having a molecular weight in the range of from 1,000 to 20,000 or mixtures thereof, and said at least one polyoxyalkylene polyol is selected from the group consisting of polyoxypropylene glycol, polyoxytetramethylene glycol, polyoxypropylene-polyoxytetramethylene glycol, terpolymerized glycols of propylene oxide and tetrahydrofuran, and trifunctional polyoxyalkylene polyols obtained by adding at least one alkylene oxide to glycerine, trimethylol propane, trimethylol ethane, or 1,2,6-hexane triol.
Claim 4
Dependent Claim
44 words
A thermosetting polyurethane resin as claimed in claim 1 wherein said monofunctional isocyanate-blocking agent is selected from the group consisting of phenol, o-cresol, xylenol, nonylphenol, γ-butyrolactam, ε-caprolactam, acetoxime, methylethyl-ketoxime, methylisobutyl-ketoxime, cyclohexanoneoxime, benzophenone-ketoxime, succinic imide, phthalic imide malonic esters, acetoacetic esters, butanol, isopropanol, and t-butanol.
Claim 5
Dependent Claim
71 words
A thermosetting polyurethane resin as claimed in claim 1 wherein said cross-linking agent is selected from the group consisting of trimethylol propane, pentaerythritol, glycerin, an adduct of trimethylol propane with propylene oxide having an OH-value above 450, an adduct of glycerin with propylene oxide having an OH-value above 450, diethanolamine, triethanolamine, triisopropanolamine, diisopropanolamine, an adduct of 1 mole of ethylene-diamine and 4 moles or less of propylene oxide, diethylene-triamine, and triethylene-tetramine.
Claim 6
Dependent Claim
49 words
A thermosetting polyurethane resin as claimed in claim 1 wherein said chain-elongating agent is selected from the group consisting of ethylene glycol, 1,2-propylene glycol, 1,3-propylene glycol, 1,3-butylene glycol, 1,-4-butylene glycol, 1,6-hexanediol, diethylene glycol, dipropylene glycol, monoethanolamine, monoisopropanolamine, ethylene diamine, butylene diamine, isophorone diamine, 4,4'-diamino-diphenyl methane, 3,3'-dichloro-4,4'-diamino-diphenyl methane, and N-β-(aminoethyl)-γ-aminopropyl-trimethoxysilane.
Claim 7
Dependent Claim
14 words
A thermosetting polyurethane resin as claimed in claim 1 which is in powdered form.
Claim 8
Dependent Claim
18 words
An aqueous dispersed thermosetting polyurethane resin prepared by dispersing the thermosetting polyurethane resin of claim 1 in water.
Claim 9
Dependent Claim
18 words
The aqueous dispersed thermosetting polyurethane resin of claim 7 wherein the water dispersion is substantially free of solvent.
Claim 10
Dependent Claim
30 words
A thermosetting polyurethane resin as claimed in claim 1 wherein said non-ionic surface active agent is added with said at least one polyoxyalkylene polyol in the production of said prepolymer.
Claim 11
Dependent Claim
25 words
A thermosetting polyurethane resin as claimed in claim 1 wherein said non-ionic surface active agent is added after reacting said blocking agent with said prepolymer.
Claim 12
Dependent Claim
20 words
A thermosetting polyurethane resin as claimed in claim 1 wherein the prepolymer is formed in the presence of a catalyst.
Claim 13
Dependent Claim
28 words
A thermosetting polyurethane resin as claimed in claim 1 wherein the methylene bis(4-cyclohexylisocyanate) and the isophorone diisocyanate are added as a mixture in the production of said prepolymer.
Claim 14
Dependent Claim
20 words
A coating agent for glass bottles, and vessels made of inorganic materials comprising a thermosetting polyurethane resin of claim 1.
Claim 15
Dependent Claim
24 words
A coating agent for glass bottles and vessels made of inorganic materials comprising an aqueous dispersion of a thermosetting polyurethane resin of claim 1.
References Cited (Backward Citations)
US3992316A
Cited
US4098933A
Cited
US4130542A
Cited
US4163814A
Cited
US3997592A
Cited
US4190566A
Cited
US4119602A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-07-27 | 1985-01-26 | 1985-07-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-07-27 | 1989-01-26 | 1989-07-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-07-27 | 1993-01-26 | 1993-07-28 | $7700.00 | Window Closed / Lapsed |