Multilayer insulating material and process for production thereof
Assignee: Kureha Corp
•
Filing: 1978-11-27
•
Granted: 1981-07-21
•
Expires: 1998-11-27
Abstract
Abstract By bonding a graphite sheet possessing tightness to at least one surface of carbon fiber felt sheet possessing gas permeability by means of a carbonaceous binder, a multilayer thermally insulating material suitable for use in a heating furnace employing a nonoxidizing atmosphere is obtained. This insulating material has mechanical strength which does not decrease with a long period of use and gives rise to little contamination of articles being heated in the furnace.
Inventors
- 👤 Fumio Kodama
- 👤 Noboru Ohyama
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 18:45
CPC Classifications
B; B32; B32B; B32B9/00; B32B9/04; B32B9/047; B32B1/00; B32B1/08; B32B18/00; B32B19/00; B32B19/06; B32B7/00; B32B7/04; B32B7/12; B32B9/005; B32B9/007; C; C04; C04B; C04B35/00; C04B35/622; C04B35/626; C04B35/63; C04B35/632; C04B35/634; C04B35/63448; C04B35/63472; C04B35/63476; C04B35/64; C04B35/645; C04B35/71; C04B35/78; C04B35/80; C04B35/83; C04B37/00; C04B37/003; C04B37/005; C04B37/008; F; F16; F16L; F16L59/00; F16L59/02; F16L59/029; F27; F27D; F27D1/00; F27D1/0003; F27D1/0006; F27D1/04; F27D1/06; B32B2262/00; B32B2262/10; B32B2262/106; B32B2307/00; B32B2307/30; B32B2307/304; B32B2307/306; B32B2307/70; B32B2307/724; B32B2313/00; B32B2313/04; B32B2597/00; C04B2235/00; C04B2235/02; C04B2235/30; C04B2235/48; C04B2237/00; C04B2237/02; C04B2237/04; C04B2237/08; C04B2237/086; C04B2237/30; C04B2237/32; C04B2237/36; C04B2237/363; C04B2237/38; C04B2237/385; C04B2237/50; C04B2237/70; C04B2237/704; C04B2237/76; C04B2237/765; C04B2237/84; Y; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/1362; Y10T428/24; Y10T428/24942; Y10T428/24992; Y10T428/30; Y10T442/00; Y10T442/50; Y10T442/57
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
87 words
A multilayer heat insulating material suitable for use in heating furnaces in which a non-oxidizing atmosphere is used, which insulating material comprises a sheet of carbon fiber felt having gas permeability, and a sheet of graphite having a thickness less than 1 mm. and a density of 0.6 to 1.6 grams/cm 3 , bonded to at least one surface of the sheet of carbon fiber felt by means of a carbonaceous binder, the density of said graphite sheet being substantially greater than that of said felt sheet.
Claim 2
Dependent Claim
87 words
A multilayer heat insulating material suitable for use in heating furnaces in which a non-oxidizing atmosphere is used, which insulating material comprises a sheet of carbon fiber felt having gas permeability, and a sheet of graphite having a thickness less than 1 mm. and a density of 0.6 to 1.6 grams/cm 3 , bonded to at least one surface of the sheet of carbon fiber felt by means of a carbonaceous binder, the density of said graphite sheet being substantially greater than that of said felt sheet.
Claim 3
Dependent Claim
25 words
The multilayer sheet of claim 1 wherein the density of said graphite sheet is from 6 to 10 times that of said carbon fiber felt.
Claim 4
Dependent Claim
73 words
A multilayer heat insulating material as set forth in claim 1 in which: at least two superimposed sheets of the carbon fiber felt is used; a sheet of graphite is interposed between and bonded to each pair of adjacent sheets of the carbon fiber felt; and another sheet of graphite is bonded to at least on outer surface of the felt sheets constituting the outermost felt layers of the entire resulting laminated structure.
Claim 5
Dependent Claim
24 words
A multilayer heat insulating material as set forth in claim 1 in which the carbonaceous binder is a carbonization product of a carbonizable resin.
Claim 6
Dependent Claim
31 words
A multilayer heat insulating material as set forth in claim 1 in which the bulk density of the bonded carbon fiber felt sheet is from 0.13 to 0.20 gram/cm. 3 .
Claim 7
Dependent Claim
18 words
A multilayer heat insulating material as set forth in claim 1 the entire shape of which is cylindrical.
Claim 8
Dependent Claim
23 words
A multilayer heat insulating material as set forth in claim 1 the entire shape of which is the shape of a flat plate.
Claim 9
Dependent Claim
37 words
A multilayer heat insulating material as set forth in claim 1 in which the graphite sheet has a density of from 0.6 to 1.6 grams/cm. 3 and is a flexible sheet comprising graphite particles in bonded state.
Claim 10
Dependent Claim
142 words
A process for producing a heat insulating material which comprises steps of: (1) forming a multi-layer structure comprising: (a) a sheet of gas permeable carbon felt having a bulk density of from 0.06 to 0.10 grams/cm 3 and a compressibility such that the force required to compress the felt sheet to twice said bulk density is from 100 to 200 g/cm 2 and (b) a sheet of graphite adjacent at least one surface of said carbon fiber felt, and (c) interposed between said sheet of graphite and said sheet of carbon fiber felt, a carbonizable resin, (2) hardening the carbonizable resin while applying a pressure of from 50 to 300 grams/cm 3 at the interface between said graphite sheet and said carbon fiber felt and (3) carbonizing said carbonizable resin to form said heat insulating material, material having a bonded multi-layer structure.
Claim 11
Dependent Claim
142 words
A process for producing a heat insulating material which comprises steps of: (1) forming a multi-layer structure comprising: (a) a sheet of gas permeable carbon felt having a bulk density of from 0.06 to 0.10 grams/cm 3 and a compressibility such that the force required to compress the felt sheet to twice said bulk density is from 100 to 200 g/cm 2 and (b) a sheet of graphite adjacent at least one surface of said carbon fiber felt, and (c) interposed between said sheet of graphite and said sheet of carbon fiber felt, a carbonizable resin, (2) hardening the carbonizable resin while applying a pressure of from 50 to 300 grams/cm 3 at the interface between said graphite sheet and said carbon fiber felt and (3) carbonizing said carbonizable resin to form said heat insulating material, material having a bonded multi-layer structure.
Claim 12
Dependent Claim
65 words
A process for producing a heat insulating material as set forth in claim 9 in which the carbonizable resin is a member selected from the group consisting of resins whose carbonization yield is more than 30 percent by weight when the resins are heated and carbonizied at a temperature up to 1,000° C. in an inactive atmosphere and liquors comprising the resins diluted in solvents.
Claim 13
Dependent Claim
64 words
A process for producing a heat insulating material as set forth in claim 10 in which the carbonizable resin is a member selected from thermosetting phenolic resins, epoxy resins, furan resins, and the like, and liquors comprising the thermosetting resins diluted in solvents each in a ratio by weight of from 0.8 to 3 of the solvent to 1 (unity) of the thermosetting resin.
Claim 14
Dependent Claim
39 words
A process for producing a heat insulating material as set forth in claim 11 in which the carbonizable resin is a member selected from phenolic resins of resol type and liquors comprising the phenolic resins diluted in lower alcohols.
Claim 15
Dependent Claim
60 words
A process for producing a heat insulating material as set forth in claim 9 in which, in step (1), the quantity of the carbonizable resin, excluding any solvent which may be associated therewith, is of the order of from 400 to 800 grams per square meter of the bonding area between the graphite sheet and the carbon fiber felt sheet.
Claim 16
Dependent Claim
38 words
A process for producing a thermally insulating material as set forth in claim 9 which further comprises, prior to step (1), a step wherein the gas permeable carbon fiber felt sheet is impregnated beforehand with the carbonizable resin.
References Cited (Backward Citations)
US3404061A
Cited
US3579401A
Cited
US3607541A
Cited
US3844877A
Cited
US3991248A
Cited
US3956548A
Cited
US4029829A
Cited
US3980105A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-07-20 | 1985-01-19 | 1985-07-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-07-20 | 1989-01-19 | 1989-07-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-07-20 | 1993-01-19 | 1993-07-21 | $7700.00 | Window Closed / Lapsed |