Assignee: Lockheed Martin Tactical Systems Inc
•
Filing: 1975-02-27
•
Granted: 1976-05-11
•
Expires: 1995-02-27
Abstract
Abstract The invention resides in a carbonaceous aircraft brake disk having a reuseable lightweight carbon composite center core to which can be bonded lightweight composite wearing materials to each side. The wearing surface is particularly designed for wear loading applications, and is relatively thin thereby simplifying manufacturing and quality assurance steps. The center core is designed for long life and strength at relatively low cost. A carbon felt layer saturated with an adhesive is located between the center core and the lightweight side wear materials to form an integral disk upon pyrolizing of the adhesive.
Inventors
- 👤 James J. Kovac
- 👤 Mial T. Hillhouse
- 👤 David M. Seikel
- 👤 Richard L. Ramsey
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 14:28
CPC Classifications
B; B32; B32B; B32B9/00; B32B9/005; B32B9/007; C; C04; C04B; C04B35/00; C04B35/71; C04B35/78; C04B35/80; C04B35/83; F; F16; F16D; F16D65/00; F16D65/02; F16D65/12; F16D65/125; F16D65/126; F16D65/127; F16D69/00; F16D69/02; F16D69/023; B32B2305/00; B32B2305/70; B32B2307/00; B32B2307/50; B32B2307/554; B32B2309/00; B32B2309/02; B32B2605/00; B32B2605/18; F16D2069/002; F16D2069/005; F16D69/04; F16D2069/0425; F16D2069/045; F16D2069/0466; Y; Y10; Y10S; Y10S428/00; Y10S428/902; Y10T; Y10T156/00; Y10T156/10; Y10T428/00; Y10T428/21; Y10T428/213; Y10T428/24; Y10T428/24942; Y10T428/2495; Y10T428/24967; Y10T428/30; Y10T442/00; Y10T442/50; Y10T442/56
Claims Analysis
Total Claims: 18
Claim 1
Independent Claim
115 words
An integral duo carbon composite brake, disk comprising, a reusable carbon composite core, said composite core containing a laminate of a carbon cloth fiber and a high coking value material pyrolized to yield essentially a carbon material, at least one carbon composite low wear layer, said low wear layer containing a laminate of a carbon cloth fiber and a high coking value material pyrolized to yield essentially a carbon material, at least one carbon felt layer bonded by a high carbon bearing cement to said core and said low wear layer to form the brake disk, and, said carbon cement pyrolized to form a carbon material so that an integral duo brake disk is formed.
Claim 2
Dependent Claim
115 words
An integral duo carbon composite brake, disk comprising, a reusable carbon composite core, said composite core containing a laminate of a carbon cloth fiber and a high coking value material pyrolized to yield essentially a carbon material, at least one carbon composite low wear layer, said low wear layer containing a laminate of a carbon cloth fiber and a high coking value material pyrolized to yield essentially a carbon material, at least one carbon felt layer bonded by a high carbon bearing cement to said core and said low wear layer to form the brake disk, and, said carbon cement pyrolized to form a carbon material so that an integral duo brake disk is formed.
Claim 3
Dependent Claim
36 words
An integral duo carbon composite brake disk according to claim 1, wherein said pyrolized material of said carbon composite core is selected from the class consisting of coal tar pitch, furan resin, polyacrylonitrile, and mixtures thereof.
Claim 4
Dependent Claim
36 words
An integral duo carbon composite brake disk according to claim 12, wherein said pyrolized material of said low wear layer is selected from the calss consisting of coal tar pitch, furan resin, polyacrylonitrile, and mixtures thereof.
Claim 5
Dependent Claim
59 words
An integral duo carbon composite brake disk according to claim 3, wherein said carbon felt layer is made from pyrolized material selected from the class consisting of rayon, polyacrylonitrile, furan resins, coal tar pitch precursors, and mixtures thereof, said high carbon bearing cement selected from the class consisting of furan resins, petroleum pitch, coal tar pitch, and mixtures thereof.
Claim 6
Dependent Claim
20 words
An integral brake disk according to claim 3, wherein one low wear layer exists on each side of said core.
Claim 7
Dependent Claim
38 words
An integral carbon brake disk according to claim 5, wherein said core has a thickness of from about 0.350 to about 0.385 inches and said wear plate has a thickness of from about 0.100 to about 0.150 inches.
Claim 8
Dependent Claim
16 words
An integral carbon brake disk according to claim 3, containing from one to three felt layers.
Claim 9
Dependent Claim
24 words
An integral duo carbon composite brake disk, according to claim 7, wherein said low wear layer has a high density or a low porosity.
Claim 10
Dependent Claim
24 words
An integral carbon brake disk according to claim 3, wherein one said carbon felt layer exists between said core and each low wear layer.
Claim 11
Dependent Claim
84 words
An integral carbon brake disk according to claim 7, wherein said core has a bulk density of at least 1.4 grams per cc, wherein said core has a bulk density of at least 1.4 grams per cc, a flex strength perpendicular to the lamina of at least 9,000 psi, and interlaminar shear strength of at least 1,000 psi, a compressive strength perpendicular to the lamina of at least 8,000 psi and an impact strength perpendicular to the laminar of at least 10 inch lbs./in.
Claim 12
Dependent Claim
29 words
An integral carbon brake disk, according to claim 7, wherein said wear material has a maximum wear rate of 0.0004 inches per face per 100 percent energy braking stop.
Claim 13
Dependent Claim
22 words
An integral carbon disk brake according to claim 7, wherein said cement layer is baked at high temperatures to pyrolize said cement.
Claim 14
Dependent Claim
21 words
An integral carbon disk brake according to claim 12, wherein said high baked temperature ranges from about 2000° to about 3000°F.
Claim 15
Dependent Claim
184 words
A process for producing integral duo carbon composite brake disk, comprising the steps of, fabricating a reusable carbon composite core, said carbon composite core containing a laminate of a carbon cloth fiber and a pyrolized material selected from the class consisting of coal tar pitch, furan resin, polyacrylonitrile, and mixtures thereof, fabricating a carbon composite low wear layer, said low wear layer containing a laminate of a carbon cloth and a pyrolized material selected from the class consisting of coal tar pitch, furan resin, polyacrylonitrile, and mixtures thereof, fabricating a carbon felt layer, said carbon felt layer made from pyrolized materials selected from the class consisting of rayon, polyacrylonitrile, furan resins, coal tar pitch precursors, and mixtures thereof, saturating said felt layer with a high carbon bearing cement bonding said core to said wear layer through said saturated felt layer to form the brake disk, said high carbon bearing cement selected from the class consisting of furan, petroleum pitch, coal tar pitch, and mixtures thereof, and baking said brake disk at a high temperature to pyrolize said cement to form an integral brake disk.
Claim 16
Dependent Claim
184 words
A process for producing integral duo carbon composite brake disk, comprising the steps of, fabricating a reusable carbon composite core, said carbon composite core containing a laminate of a carbon cloth fiber and a pyrolized material selected from the class consisting of coal tar pitch, furan resin, polyacrylonitrile, and mixtures thereof, fabricating a carbon composite low wear layer, said low wear layer containing a laminate of a carbon cloth and a pyrolized material selected from the class consisting of coal tar pitch, furan resin, polyacrylonitrile, and mixtures thereof, fabricating a carbon felt layer, said carbon felt layer made from pyrolized materials selected from the class consisting of rayon, polyacrylonitrile, furan resins, coal tar pitch precursors, and mixtures thereof, saturating said felt layer with a high carbon bearing cement bonding said core to said wear layer through said saturated felt layer to form the brake disk, said high carbon bearing cement selected from the class consisting of furan, petroleum pitch, coal tar pitch, and mixtures thereof, and baking said brake disk at a high temperature to pyrolize said cement to form an integral brake disk.
Claim 17
Dependent Claim
23 words
A method according to claim 14, including the baking of said brake disk at a temperature of from about 2000° to about 3000°F.
Claim 18
Dependent Claim
21 words
A method according to claim 15, wherein said brake disk is baked under a compression of from 200 to 2,000 psi.
References Cited (Backward Citations)
US2520192A
Cited
US2717427A
Cited
US3055789A
Cited
US3187502A
Cited
US3334040A
Cited
US3261440A
Cited
US3672936A
Cited
US3650357A
Cited
US3650357B1
Cited
US3576700A
Cited
US3712427A
Cited
US3730320A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1979-05-11 | 1979-11-10 | 1980-05-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1983-05-11 | 1983-11-10 | 1984-05-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1987-05-11 | 1987-11-10 | 1988-05-11 | $7700.00 | Window Closed / Lapsed |