US4279848A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for extruding an open-cell foamed polyolefin filter
Assignee: Solutia Inc
•
Filing: 1980-02-11
•
Granted: 1981-07-21
•
Expires: 2000-02-11
Abstract
Abstract A polyolefin filter for tobacco products and the like was prepared. The extruded element is an open-cell foamed polyethylene or polypropylene having a TPM filtration efficiency greater than 20%. The filter rod can be made by extruding polyethylene containing less than 0.2 moles of a volatile blowing agent per 100 grams of resin at a melt temperature between 130 DEG C. and 150 DEG C., the temperature of the die being between 120 DEG C. and 136 DEG C. Higher melt temperature and die temperature are required for polypropylenes.
Inventors
- 👤 Samuel Baxter
- 👤 Pushpkumar D. Changani
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 02:08
CPC Classifications
C; C08; C08J; C08J9/00; C08J9/04; C08J9/12; A; A24; A24D; A24D3/00; A24D3/06; A24D3/08; B; B29; B29C; B29C44/00; B29C44/34; B29C44/36; B29C44/46; B29C44/50; B29K; B29K2023/00; B29K2023/04; B29K2023/06; B29K2105/00; B29K2105/04; B29K2105/045; B29L; B29L2031/00; B29L2031/14; B29L2031/7414; B29L2031/7416; C08J2323/00; C08J2323/02; Y; Y10; Y10S; Y10S264/00; Y10S264/13
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
108 words
In a process for the extrusion through a metal die of a high density polyethylene resin having a melt temperature between 130° C. and 150° C. or a polypropylene resin having a melt temperature of between 160° C. and 180° C., wherein each resin contains a volatile blowing agent in an amount less than 0.2 moles per 100 grams of the final extruded resin, the improvement which comprises maintaining the temperature of the die within 5 millimeters of the metal-resin interface at a temperature of between 120° C. and 136° C. where the resin is polyethylene and between 155° C. and 165° C. where the resin is polypropylene.
Claim 2
Dependent Claim
108 words
In a process for the extrusion through a metal die of a high density polyethylene resin having a melt temperature between 130° C. and 150° C. or a polypropylene resin having a melt temperature of between 160° C. and 180° C., wherein each resin contains a volatile blowing agent in an amount less than 0.2 moles per 100 grams of the final extruded resin, the improvement which comprises maintaining the temperature of the die within 5 millimeters of the metal-resin interface at a temperature of between 120° C. and 136° C. where the resin is polyethylene and between 155° C. and 165° C. where the resin is polypropylene.
Claim 3
Dependent Claim
12 words
The process of claim 1 wherein the resin is high density polyethylene.
Claim 4
Dependent Claim
10 words
The process of claim 1 wherein the resin is polypropylene.
Claim 5
Dependent Claim
12 words
The process of claim 1 wherein the resin contains a nucleating agent.
Claim 6
Dependent Claim
16 words
The process of claim 1 wherein the said volatile blowing agent is a lower aliphatic hydrocarbon.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-07-20 | 1985-01-19 | 1985-07-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-07-20 | 1989-01-19 | 1989-07-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-07-20 | 1993-01-19 | 1993-07-21 | $7700.00 | Window Closed / Lapsed |