Abstract
Abstract A process for making electroluminescent films and devices by sputtering. Zinc sulfide, manganese, and copper sputtering targets are arranged in a circular configuration. RF voltages, applied to the targets, cause sputtering of the target materials. A transparent substrate with a transparent electrode formed thereon is rotated beneath the sputtering targets. An electroluminescent film including the target materials is formed on the upper surface of the transparent electrode. Concentration of the target materials in the electroluminescent film can be controlled by controlling the rf voltages applied to the sputtering targets. An electroluminescent device is completed by depositing a second electrode on the upper surface of the electroluminescent film and applying a forming voltage between the electrodes.
Inventors
- 👤 Donald H. Baird
- 👤 Martin S. McDonough
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 00:21
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/22; C23C14/34; C23C14/3464; H; H05; H05B; H05B33/00
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
157 words
A method for making a low voltage dc electroluminescent film comprising the steps of: placing a plurality of discrete sputtering targets, including a zinc sulfide target, a manganese target, and a copper target, and a substrate in vacuum-tight vessel containing a gas at a pressure suitable for sputtering, said targets being placed in a circular arrangement; applying to said targets voltages which cause sputtering of said target materials; rotating said substrate sequentially into proximity to each of said sputtering targets such that said substrate is sequentially exposed to said targets, said target materials are sequentially sputtered onto said substrate and an electroluminescent film, including material from each of said targets, is formed on said substrate; and controlling the rate of sputtering of said copper target so as to provide a copper concentration in said electroluminescent film in the range between one weight percent and two weight percent, whereby said electroluminescent film is operable at low dc voltages.
Claim 2
Independent Claim
157 words
A method for making a low voltage dc electroluminescent film comprising the steps of: placing a plurality of discrete sputtering targets, including a zinc sulfide target, a manganese target, and a copper target, and a substrate in vacuum-tight vessel containing a gas at a pressure suitable for sputtering, said targets being placed in a circular arrangement; applying to said targets voltages which cause sputtering of said target materials; rotating said substrate sequentially into proximity to each of said sputtering targets such that said substrate is sequentially exposed to said targets, said target materials are sequentially sputtered onto said substrate and an electroluminescent film, including material from each of said targets, is formed on said substrate; and controlling the rate of sputtering of said copper target so as to provide a copper concentration in said electroluminescent film in the range between one weight percent and two weight percent, whereby said electroluminescent film is operable at low dc voltages.
Claim 3
Dependent Claim
40 words
The method as defined in claim 1 wherein said substrate is rotated at a rate of about 5 r.p.m. and is heated during rotation so as to cause leveling by diffusion of local non-uniformities of composition of said electroluminescent film.
Claim 4
Dependent Claim
22 words
The method as defined in claim 1 wherein said electroluminescent film has a thickness in the range between 1.0 and 1.5 microns.
Claim 5
Independent Claim
191 words
A method for making a low voltage dc electroluminescent device comprising the steps of: placing a plurality of discrete sputtering targets, including a zinc sulfide target, a manganese target, and a copper target, and a substrate having a transparent electrode formed thereon in a vacuum-tight vessel containing a gas at a pressure suitable for sputtering, said targets being placed in a circular arrangement; applying to said targets voltages which cause sputtering of said target materials; rotating said substrate sequentially into proximity to each of said sputtering targets such that said substrate is sequentially exposed to said targets, said target materials are sequentially sputtered onto said substrate and an electroluminescent film, including material from each of said targets, is formed on said substrate; controlling the rate of sputtering of said copper target so as to provide a copper concentration in said electroluminescent film in the range between one weight percent and two weight percent; forming a second electrode on said electroluminescent film; and applying between said electrodes a voltage of sufficient magnitude to create an insulating layer in said electroluminescent film, whereby an electroluminescent device operable at low dc voltages is provided.
Claim 6
Independent Claim
191 words
A method for making a low voltage dc electroluminescent device comprising the steps of: placing a plurality of discrete sputtering targets, including a zinc sulfide target, a manganese target, and a copper target, and a substrate having a transparent electrode formed thereon in a vacuum-tight vessel containing a gas at a pressure suitable for sputtering, said targets being placed in a circular arrangement; applying to said targets voltages which cause sputtering of said target materials; rotating said substrate sequentially into proximity to each of said sputtering targets such that said substrate is sequentially exposed to said targets, said target materials are sequentially sputtered onto said substrate and an electroluminescent film, including material from each of said targets, is formed on said substrate; controlling the rate of sputtering of said copper target so as to provide a copper concentration in said electroluminescent film in the range between one weight percent and two weight percent; forming a second electrode on said electroluminescent film; and applying between said electrodes a voltage of sufficient magnitude to create an insulating layer in said electroluminescent film, whereby an electroluminescent device operable at low dc voltages is provided.
Claim 7
Dependent Claim
40 words
The method as defined in claim 4 wherein said substrate is rotated at a rate of about 5 r.p.m. and is heated during rotation so as to cause leveling by diffusion of local non-uniformities of composition of said electroluminescent film.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1984-07-20 | 1985-01-19 | 1985-07-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1988-07-20 | 1989-01-19 | 1989-07-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1992-07-20 | 1993-01-19 | 1993-07-21 | $7700.00 | Window Closed / Lapsed |