Process for producing a thin fluorescent film for electroluminescence
Assignee: Futaba Corp
•
Filing: 1975-06-10
•
Granted: 1978-07-04
•
Expires: 1995-06-10
Abstract
Abstract A process for producing a thin fluorescent film for electroluminescence includes the steps of heating a raw material, composed of a base material and an activator, within an enclosed type crucible so as to generate a mixed vapor, injecting the mixed vapor into a vacuum zone through means of an injection nozzle, projecting an electron beam into the injected mixed vapor so as to ionize the mixed vapor, accelerating the ionized mixed vapor by means of an electric field, and permitting the accelerated ionized mixed vapor to collide with a base plate so as to form a vapor-deposited film upon the base plate.
Inventors
- 👤 Kiyoshi Morimoto
- 👤 Yukihiko Utamura
- 👤 Toshinori Takagi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 22:37
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/22; C23C14/221; H; H05; H05B; H05B33/00; H05B33/10; Y; Y10; Y10S; Y10S148/00; Y10S148/045; Y10S148/169
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
205 words
A process for producing a thin fluorescent film for electroluminescence coated upon a base plate, which comprises the steps of: (a) placing a base material and an activator within an enclosed-type crucible having at least one injection nozzle; (b) placing the thus charged crucible into a vacuum chamber; (c) heating said base material and activator so as to generate a mixed vapor within said crucible having a pressure greater than the vacuum outside the crucible; (d) injecting said mixed vapor into said vacuum zone through said injection nozzle provided upon said crucible to adiabatically expand said mixed vapor so as to attain a supercooled state and form a mixed vapor comprising atom groups or clusters; (e) projecting an electron beam into said injected mixed vapor comprising said atom groups or clusters so as to thereby ionize at least a portion of said atom groups or clusters; (f) accelerating said ionized atom groups or clusters by means of an electric field; and (g) permitting said mixed vapor comprising said ionized and accelerated atom groups or clusters and the non-ionized atom groups or clusters to collide with said base plate so as to thereby form a vapor-deposited film, acting as a fluorescent film, upon said base plate.
Claim 2
Dependent Claim
205 words
A process for producing a thin fluorescent film for electroluminescence coated upon a base plate, which comprises the steps of: (a) placing a base material and an activator within an enclosed-type crucible having at least one injection nozzle; (b) placing the thus charged crucible into a vacuum chamber; (c) heating said base material and activator so as to generate a mixed vapor within said crucible having a pressure greater than the vacuum outside the crucible; (d) injecting said mixed vapor into said vacuum zone through said injection nozzle provided upon said crucible to adiabatically expand said mixed vapor so as to attain a supercooled state and form a mixed vapor comprising atom groups or clusters; (e) projecting an electron beam into said injected mixed vapor comprising said atom groups or clusters so as to thereby ionize at least a portion of said atom groups or clusters; (f) accelerating said ionized atom groups or clusters by means of an electric field; and (g) permitting said mixed vapor comprising said ionized and accelerated atom groups or clusters and the non-ionized atom groups or clusters to collide with said base plate so as to thereby form a vapor-deposited film, acting as a fluorescent film, upon said base plate.
Claim 3
Dependent Claim
25 words
The process as set forth in claim 1, wherein: said base material is composed of at least one of the compounds ZnS, ZnSe, or CdS.
Claim 4
Dependent Claim
32 words
The process of claim 1 wherein said base material is selected from the group consisting of a mixture of elemental zinc and sulfur, elemental zinc and selenium and elemental cadmium and sulfur.
Claim 5
Dependent Claim
41 words
The process of claim 1, wherein said base material is selected from the group consisting of ZnS in admixture with elemental zinc and sulfur, ZnSe in admixture with elemental zinc and selenium and CdS in admixture with elemental cadmium and sulfur.
Claim 6
Dependent Claim
73 words
The process as set forth in claim 1, wherein: said enclosed type crucible has a plurality of heating chambers and at least a common injection nozzle, said base material and activator are separately placed within said plurality of heating chambers separately according to their components which are separately heated therein so as to generate respective vapors; and said respective vapors are mixed and injected from said common injection nozzle into said vacuum zone.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1981-07-03 | 1982-01-02 | 1982-07-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1985-07-03 | 1986-01-02 | 1986-07-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1989-07-03 | 1990-01-02 | 1990-07-04 | $7700.00 | Window Closed / Lapsed |